Identification of the Most Significant Processing Parameters on the Development of Fiber Waviness in Thin Laminates

Abstract

This paper identifies the material and processing parameters which most significantly influence the development of in-plane waviness in laminates. Thin laminates of unidirectional, T300 carbon-fiber/polysulfone matrix prepreg were processed in an autoclave and a custom-made water-cooled chamber, which allowed fast cooling rates. Multivariate regression analysis of process-induced waviness was performed for combinations of the select process variables and their interactions to identify those factors responsible for waviness development. Of the eight parameters investigated – hold temperature, hold time, pressure, length, width, thickness, cooling rate, and tool plate material – only three affected the development of fiber waviness: length, cooling rate, and tool plate material. Length affects not only the number of wrinkles and wrinkle distribution, but also the average amplitude of the waviness. Cooling rate affects the wavelength and amplitude of the waviness, as well as the number of wrinkles. Tool plate material primarily affects the number of wrinkles, without showing a significant effect on the average wave geometry. There is also an interaction between tool plate material and cooling rate in producing fiber waviness. For the three relevant parameters, the possible waviness-inducing mechanisms are tool plate/part coefficient of thermal expansion (CTE) mismatch, temporal temperature gradients (or cooling rates), and spatial temperature gradients. The tool plate/part CTE mismatch proved to be the most important mechanism driving fiber waviness in plates, although changes in cooling rates also dramatically affected the quantity of waviness which developed. Spatial temperature gradients were negligible for this study. The tool plate/part CTE mismatch-driven axial buckling loads on the fibers were substantial in the outermost laminate plies, or skin, but negligible in the laminate core. Waviness was limited to the surface or skin plies, even in identically-processed thick laminates. This study confirmed that if the fibers experience axial loads – albeit a small fraction of their Young’s modulus – while the matrix is unable to provide some level of transverse fiber support, the fibers will microbuckle resulting in waviness (in-plane or out-of-plane depending upon the laminate constraint).

Keywords

composite laminates process-induced fiber waviness effects of process parameters hold temperature cooling rate tool plate material

Get full access to this article

View all access options for this article.

References

1. Chaudhuri, R.A. (1991). Prediction of the compressive strength of thick-section advanced composite laminates. Journal of Composite Materials, 25: 1244–1276.

2. Joyce, P.J. , Kugler, D. and Moon, T.J. (1997). A technique for characterizing process-induced fiber waviness in unidirectional composite laminates – using optical microscopy. Journal of Composite Materials, 31(17): 1694–1727.

3. Joyce, P.J. and Moon, T.J. (1998). Compression strength reduction in composites with in-plane fiber waviness. Accepted for Publication in ASTM STP 1330, Seventh Symposium on Composites: Fatigue and Fracture. pp. 76–96.

4. Nairn, J.A. (1985). Thermoelastic analysis of residual stresses in unidirectional, high- performance composites. Polymer Composites, 6: 123–130.

5. Bhalerao, M.S. (1996). On process-induced fiber waviness in composites: theory and experiments. PhD Thesis, University of Texas at Austin.

6. Hjellming, L.N. and Walker, J.S. (1989). Thermal curing cycles for composite cylinders with thick walls and thermoset resin. Journal of Composite Materials, 23: 1048–1064.

7. Twardowski, T.E., Lin, S.E. and Geil, P.H. (1991). Curing in composite laminates: thick sections and simulations. ONR-URI Composites Program, Report No. UIUC-NCCMR 91-08.

8. Zoller, P. (1978). Specific volume of polysulfone as a function of temperature and pressure. Journal of Polymer Science: Polymer Physics Edition, 16: 1261–1275.

9. Nairn, J.A. and Zoller, P. (1987). The development of residual thermal stresses in amorphous and semicrystalline thermoplastic matrix composites. In: Toughened Composites: Symposium on Toughened Composites, ASTM STP 937. American Society for Testing and Materials, Philadelphia. pp. 328–341.

10.

10. D’Amore, A. , Pompo, A. and Nicolais, L. (1991). Viscoelastic effects in PEEK and PEEK-based composites. Composites Science and Technology, 41: 303–325.

11.

11. Andersen, T. and Lystrup, A. (1993). Room temperature filament winding of thermoplastic composites. Plastics, Rubber and Composites Processing and Applications, 19(3): 143–149.

12.

12. Olson, B. , Lamontia, M. , Gillespie, J. and Bogetti, T. (1995). The effects and non-destructive evaluation of defects in thermoplastic compression-loaded composite cylinders. Journal of Thermoplastic Composite Materials, 8: 109–136.

13.

13. Hahn, H.T. (1984). Effects of residual stresses in polymer matrix composite. The Journal of Astronautical Sciences, 32(3): 253–267.

14.

14. Jansson, S. and Leckie, F. (1992). Reduction of thermal stresses in continuous fiber reinforced metal matrix composite with interface layers. Journal of Composite Materials, 26(10): 1474–1486.

15.

15. Chan, W.S. and Wang, J.S. (1994). Influence of fiber waviness on the structural response of composite laminates. Journal of Thermoplastic Composite Materials, 7: 243–260.

16.

16. Cohen, A. , Calhoun, D. , Adams, M.E. and Campbell, G.A. (1993). Experimental investigation of fiber buckling during fabrication of thermoplastic matrix composites. Heat and Mass Transfer in Materials Processing and Manufacturing, HTD-Vol. 261. pp. 127–132.

17.

17. Weitsman, Y. (1979). Residual thermal stresses due to cool down of epoxy-resin composites. Journal of Applied Mechanics, 46: 563–567.

18.

18. Manson, J.A. and Seferis, J.C. (1987). Internal stress determination by process simulated laminates. SPE 45th Annual Technical Conference and Exhibit, ANTEC ’87. pp. 1446–1449.

19.

19. Chapman, T.J. , Gillespie, J.W. , Pipes, R.B. , Manson, J.A.E. and Seferis, J.C. (1990). Prediction of process-induced residual stresses in thermoplastic composites. Journal of Composite Materials, 24: 616–642.

20.

20. Choi, H.J. and Thangjitham, S. (1992). Thermally induced local effects in laminated composites. Journal of Thermal Stresses, 15: 311–327.

21.

21. Highsmith, A.L. , Davis, J.J. and Helms, K.L.E. (1992). The influence of fiber waviness on the compressive behaviour of unidirectional continuous fiber composites. Composite Materials: Testing and Design, ASTM STP 1120. American Society for Testing and Materials, Philadelphia. pp. 20–36.

22.

22. White, S. and Zhang, S. (1993). The effect of mandrel material on the processing-induced residual stresses in thick filament wound composite cylinders. Journal of Reinforced Plastics and Composites, 12: 698–711.

23.

23. Loos, A. and Tzeng, J. (1994). Filament winding. Flow and Rheology in Polymer Composites Manufacturing. New York: Elsevier Science. pp. 571–591.

24.

24. Bhattacharyya, D. , Burt, C.R. and Martin, T.A. (1993). Forming of fibre reinforced thermoplastic sheets. International Conference on Advanced Composite Materials. pp. 875–882.

25.

25. Olson, S.H. (1990). Manufacturing with commingled yarns, fabrics and powder prepreg thermoplastic composite materials. Advanced Materials, the Challenge for the Next Decade, Part 2, 35th International SAMPE Symposium and Exhibition. pp. 1306–1320.

26.

26. Iaconis, J.M. (1987). Process variables evaluation of PEEK APC-2 thermoplastic matrix composite. In: 32nd International SAMPE Symposium. pp. 104–115.

27.

27. Brayshaw, J. and Pindera, M.-J (1990). The effect of temperature and time-dependent matrix properties on residual thermal stresses in MMC. Thermal Effects on Structures, AMD – Vol. 110. pp. 35–41.

28.

28. Mrse, A. and Piggott, M.R. (1990). Relation between fibre divagation and compressive properties of fibre composites. 35th International SAMPE Symposium. pp. 2236–2244.

29.

29. Piggott, M.R. (1992). Mesostructures: an overview. 37th International SAMPE Symposium, SAMPE. pp. 738–746.

30.

30. Tan, S.C. (1989). A simple approach for the buckling of unidirectional composites with circular and non-circular fibers. 34th International SAMPE Symposium. pp. 539–544.

31.

31. Claus, W. (1972). Filament misalignment and composite strength. Composite Materials: Testing and Design, ASTM STP 497. pp. 564–574.

32.

32. Gutowski, T. (1985). A resin flow/fiber deformation model for composites. Advancing Technology in Materials and Processes. pp. 925–934.

33.

33. Gutowski, T. , Cai, Z. , Bauer, S. , Boucher, D. , Kingery, J. and Wineman, S. (1987). Consolidation experiments for laminate composites. Journal of Composite Materials, 21: 650–667.

34.

34. Kyriakides, S. , Arseculeratne, R. , Perry, E.J. and Liechti, K.M. (1993). On the compressive failure of fiber reinforced composites. EMRL Report No. 93/11. Department of Aerospace Engineering and Engineering Mechanics, The University of Texas at Austin.

35.

35. Cai, Z. , Gutowski, T. and Allen, S. (1992). Winding and consolidation analysis for cylindrical composite structures. Journal of Composite Materials, 26(9): 1374–1399.

36.

36. Kugler, D. , Joyce, P.J. and Moon, T.J. (1997). Investigation of the effect of part length on process-induced fiber-wrinkled regions in composite laminates. Journal of Composite Materials, 31(17): 1728–1757.

37.

37. Amoco . (1993). T-300 fiber properties. Phone & Fax Conversation with the Technical Representatives. Amoco Performance Products, Inc., Marietta, GA.

38.

38. Amoco . (1993). UDEL polysulfone: design engineering data. Private Communications with the Technical Representatives. Amoco Performance Products, Inc., Marietta, GA.

39.

39. Adams, D.O. and Hyer, M.W. (1990). Fabrication and compression testing of layer waviness in thermoplastic composite laminates. Technical Report, Virginia Polytechnic Institute and State University, Blacksburg, VA.

40.

40. Naley, M. (1994). Fabrication and testing of unidirectional thermoplastic composite plates with varying degrees of fiber waviness. Master’s Thesis, The University of Texas at Austin, Austin, TX.

41.

41. Kugler, D. (1998). Experimental investigation of the effect of changes in processing history on composite laminates and cylinders. PhD Thesis, The University of Texas at Austin, Austin, TX.

42.

42. Hashin, Z. (1972). Theory of Fiber-Reinforced Materials. NASA, NASA-8818, Nov. 1970.

43.

43. Nairn, J.A. and Zoller, P. (1985). Matrix solidification and the resulting residual thermal stresses in composites. Journal of Materials Science, 20: 355–367.

44.

44. Piggott, M.R. (1981). A theoretical framework for the compressive properties of aligned fibre composites. Journal of Materials Science, 16: 2837–3845.

45.

45. Jeronimidis, G. and Parkyn, A.T. (1988). Residual stresses in carbon fiber – thermoplastic matrix laminates. Journal of Composite Materials, 22: 401–415.

46.

46. Weitsman, Y. (1980). Optimal cool-down in linear viscoelasticity. Journal of Applied Mechanics, 47: 35–39.

47.

47. Chapman, T.J. , Gillespie, J.W. , Manson, J.A.E. , Pipes, R.B. and Seferis, J.C. (1988). Thermal skin/core residual stresses induced during cooling of thermoplastic matrix composites. Proceedings of the American Society for Composites, Third Technical Conference. pp. 449–458.

48.

48. Neter, J. , Wasserman, W. and Kutner, M. (1990). Applied Linear Statistical Models: Regression, Analysis of Variance, and Experimental Design. Homewood, Illinois: Irwin.

49.

49. Barnes, J. (1994). Statistical Analysis for Engineers and Scientists. New York: McGraw-Hill, Inc.