Low-Velocity Impact and Damage Process of Composite Laminates

Abstract

Several important issues regarding damage simulation of composite laminates due to low velocity impact were investigated including contact law, damage initiation and the corresponding change of stiffness, and damping. Continuum damage mechanics was applied to account for the change of mechanical properties of damaged materials. The Hertzian contact law was modified in order to accommodate the serious damage in the plate. A semi-empirical delamination damage criterion was introduced. A finite element program was written in FORTRAN using twenty-noded solid elements with layered structure to analyze the transient dynamic response of composite laminates. In the simulation computations, variable material damping coefficients were applied to the elements according to damage in order to stabilize the computation. Damage in the forms of matrix cracking, delamination, and fiber breakage were included and analyzed. Results including the force history and delamination areas were found to correlate well with the experiments.

Keywords

low-velocity impact damage mechanics residual strength composite laminate impact simulation

Get full access to this article

View all access options for this article.

References

1. Yang, S.H. and Sun, C.T. (1982). Indentation Law for Composite Laminates. Composite Materials: Testing and Design (6th conference), ASTM STP-787, pp. 425–449.

2. Belingardi, G. , Gugliotta, A. and Vadori, R. (1998). Numerical simulation of fragmentation of composite material plates due to impact. International Journal of Impact Engineering, 21: 335–347.

3. Luo, R.K. , Green, E.R. and Morrison, C.J. (1999). Impact damage analysis of composite plates. International Journal of Engineering, 22: 435–447.

4. Jones, R.R. , Callinan, R. , Hen, K.K. and Brown, K.C. (1984). Analysis of multi-layer laminates using three-dimensional super-elements. International Journal for Numerical Methods in Engineering, 20: 583–587.

5. Lagace, P.A. , Ryan, K.F. and Graves, M.J. (1994). Effect of damage on the impact response of composite laminates. AIAA Journal, 32: 1328–1330.

6. Shahid, I. , Chang, F.K. and Shah, B.M. (1996). Impact damage resistance and damage tolerance of composite with progressive damage. AIAA-96-1403-CP.

7. Guan, Z.D. (1994). Transient dynamic analysis of impact and damage processes of laminated composite panels and stiffened panels due to low velocity impact. PhD Dissertation, Department of Flying Vehicle Design and Applied Mechanics, Beijing University of Aeronautics and Astronautics.

8. Choi, H.Y. and Chang, F.K. (1992). A model for prediction damage in graphite/epoxy laminated composites resulting from low-velocity point impact. Journal of Composite Materials, 26: 2134–2169.

9. Shen, W. , Peng, L.H. , Yang, F. and Shen, Z. (1987). Generalized elastic damage theory and its application to composite plate.Engineering Fracture Mechanics, 28: 403–412.

10.

10. Shen,W. and Wu, C.S. (1992). Computer simulation for damage-failure process of composite plate under high-speed impact. Engineering Fracture Mechanics, 42: 159–168.

11.

11. The science and technology of aeronautics and astronautics institute (PRC) (1990). Manual of Composite Structure Design, p. 114-114.

12.

12. Liu, Dahsin , Raju, B.B. and Dang, X.L. (1998). Size effects on impact response of composite laminates. International Journal of Impact Engineering, 21: 837–854.

13.

13. Lee, Shaw Ming and Zahuta, P. (1991). Instrumented impact and static indentation of composites. Journal of Composite Materials, 25: 204–222.