Effect of Thermal Cycling on Microcracking and Strength Degradation of High-Temperature Polymer Composite Materials for Use in Next-Generation SST Structures

Abstract

The objective of this study was to investigate the effect of thermal cycles encountered by an SST in service on the cumulative frequency of microcracks and degradation of open-hole-compressive (OHC) strength in high-temperature polymer-matrix composite materials. One cycle of thermal cycling was designated as the sequence from room temperature (RT) to 54C, up to +177C, and back to RT. Thermal-cycling tests were conducted up to 10,000 cycles on two kinds of carbonfiber/thermoplastic polyimide composite material: IM7/PIXA, IM7/K3B, and up to 1000 cycles on G40-800/5260 carbon fiber/bismaleimide composite material. At scheduled thermal cycles, transverse microcracks initiated on the sectional surface of the laminates were observed and counted using an optical microscope. Static mechanical tests at RT provided OHC strength before and after thermal cycles. In addition, a simple and approximate finite element model (FEM) analysis using basic lamina data of the T800H/PMR-15 carbon fiber/polyimide composite was conducted to estimate the thermal stresses generated in the laminate.

Major results obtained by the tests and FEM analysis are as follows: A fairly large number of microcracks were initiated, though the number as a function of thermal cycles varied according to the material; OHC strength before and after thermal cycles did not change during the course of this study; thermal cycles and transverse microcracks did not affect OHC strength; the calculated thermal-stress level in layers generated by one thermal-cycle of 231C temperature difference was under the limit for crack initiation of the T800H/PMR-15.

Keywords

CFRP high-temperature polymer supersonic transport thermal cycling microcrack initiation OHC strength degradation FEM analysis

Get full access to this article

View all access options for this article.

References

1. National Research Council (1997). U.S. Supersonic Commercial Aircraft–Assessing NASA’s High Speed Research Program. Washington DC: National Academy Press. p. 72-72.

2. Hergenrother, P.M. (Feb. 2000). Composites, adhesives and sealants for high speed commercial airplanes. Chemical Innovations. pp. 34–44.

3. Mazzio, V.F. and Mehan, R.L. (1977). Effects of thermal cycling on the properties of graphiteepoxy composites. ASTM STP 617, 466–480.

4. Henaff-Gardin, C. , Lafarie-Frenot, M.C. and Ganby, D. (1996). Doubly periodic matrix cracking in composite laminates–Part 2: Thermal biaxial loading. Composite Structures, 36: 131–140.

5. Terada, K. , Kobayashi, S. and Takeda, N. (August 2000). Microscopic damage progress in high temperature CFRP cross-ply laminates under thermal cycling. Proceedings of the Second Asian-Australasian Conference on Composite Materials. Kyongju. pp. 981–986.

6. Fahmy, A.A. and Cunningham, T.G. (July 1976). Investigation of thermal fatigue in fiber composite materials. NASA-CR-2641.

7. Shimokawa, T. , Hamaguchi, Y. , Kakuta, Y. , Katoh, H. , Sanda, T. , Mizuno, H. and Toi, Y. (1999). Effect of isothermal aging on ultimate strength of high temperature composite materials for SST structures. Journal of Composite Materials, 33(12): 1104–1118.

8. Shimokawa, T. , Hamaguchi, Y. and Katoh, H. (1999). Effect of moisture absorption on hot/wet compressive strength of T800H/PMR-15 carbon/polyimide. Journal of Composite Materials, 33:(18), 1685–1698.