Fatigue Response and Modelling of Variable Stress Amplitude and Frequency in AS-4/PEEK Composite Laminates,Part 1: Experiments

Abstract

This paper aims to investigate the tension-tension (T-T) fatigue behavior at variable fatigue loadings in AS-4/PEEK composite laminates. Three lay-ups of specimens, such as cross-ply [0/90]_4s, quasi-isotropic [0/45/90/-45]_2s and angle-ply [±45]_4s, were tested at room temperature and moisture. The parameters involved were maximum stress (low and high), frequency (5 Hz and 25 Hz), and stress ratio (R = 0 and 0.2). We received the fatigue life and found that the maximum stress and stress ratio are the two controlling factors on lives, whilst frequency affects significantly in [±⁴⁵]_4s laminates. Next, stiffness and strength degradation were defined to describe the laminate damage process due to cyclic loadings and these experimental data were correlated with suitable models proposed in power function form. From the damage curves we observe that three stages of damage growth can be clearly divided and different failure mechanisms exist among three lay-ups. All these valuable data will be used to predict fatigue life under multi-block cyclic loadings in association with Cumulative Damage Theory in Part 2: Analysis and Formulation.

Get full access to this article

View all access options for this article.

References

1. Blundeu, D. J. and Osborn, B. N. , "Crystalline Morphology of the Matrix of PEEK-Carbon Fiber APC-2 Crystallization Behavior," SAMPE Quarter, Vol. 17, No. 1, Oct. 1985, p. 420.

2. Lee, Y. and Porter, R. S. , "Crystallization of PEEK in Carbon Fiber Composites," Polymer Engineering Science, Vol. 26, 1986, p. 633.

3. Cebe, P. , Hong, S.-D. , Chung, S. and Gupta, A. , "Mechanical Properties and Morphology of Poly(etheretherketone)," Toughened Composites, ASTM STP 937, N. J. Johnston , Ed. American Society for Testing and Materials, Philadelphia, 1987, p. 342.

4. Beehag, A. and Ye, L. , "Role of Cooling Pressure on Interlaminar Fracture Properties of Commingled CF/PEEK Composites" Composites, Vol 27A, 1996, p. 175.

5. Mall, S. , Yun, K. T. and Kochhar, N. K. , "Characterization of Matrix Toughness Effect on Cyclic Delamination Growth in Graphite Fiber Composites," Composite Materials: Fatigue and Fracture, Second Volume, ASTM STP 1012, P. A. Lagace Ed., 1989, p. 296.

6. Simonds, R. A. , Stinchcomb, W. W. , "Response of Notched AS4/PEEK Laminates due to Tension/Compression Loadings," ASTM STP 1044, 1989, p. 133.

7. Dillon, G. and Buggy, M. , "Damage Development during Flexural Fatigue of Carbon Fiber-Reinforced PEEK," Composites, Vol. 26, 1995, p. 355.

8. Spearing, S. M. , Beaumont, P. W. R. and Kortschat, M. T. , "The Fatigue Damage Mechanics of Notched Carbon Fiber/PEEK Laminates," Composites, Vol. 23, 1992, p. 305.

9. Carlile, D. R. , Leach, D. C. , "Mechanical Properties of the Carbon Fiber/PEEK Composite APC-2/AS-4 for Structural Applications," ASTM STP 1044, 1989, p. 199.

10.

10. O'Conner, J. E. , Lou, A. Y. and Beever, W. H. , "A Thermoplastic Polymer Matrix for High Performance Composites," Phillips Petroleum Company, Phillips Research Center, Bartlesville, OK 74004.

11.

11. Curtis, D. C. , et al , "Fatigue Testing of Multi-Angle Laminates of CF/PEEK," Composites, Vol. 19, 1988, p. 446.

12.

12. Tai, N. H. , Ma, C. C. M. and Wu, S. H. , "Fatigue Behavior of Carbon Fiber/PEEK Laminate Composites," Composites, Vol. 26, 1995, p. 551.

13.

13. Adams, D. F. , Zimmerman, R. S. and Odom, E. M. , "Frequency and Load Ratio Effects on Critical Strain Energy Release Rate Thresholds of Graphite/Epoxy Composites," ASTM STP 937, 1987, p. 242.

14.

14. Chan, W. S. and Wang, A. S. D. , "Free Edge Delamination Characteristics in S2/CE 9000 Glass Epoxy Laminates Under Static and Fatigue Loads," ASTM STP 1012, 1989, p. 270.

15.

15. Mandel, J. F. and Meier, U. , " Effects of Stress Ratio, Frequency and Loading Time in the Tensile Fatigue of Glass-Reinforced Epoxy," ASTM STP 873, 1983, p. 55.

16.

16. Scrivner, G. C. and Chan, W. S. , "Effect of Stress Ratio on Edge Delamination Characteristics in Laminated Composites," ASTM STP 1156, 1993, p. 538.

17.

17. Maier, G. and Ott, H. et al , "Damage Development in Carbon Fiber-Reinforced Polyimides in Fatigue Loading as a Function of Stress Ratio," Composites, Vol. 17, 1986, p. 111.

18.

18. Yasushi, M. et al. , "Influence of Stress Ratio on Fatigue Behavior in the Transverse Direction of Unidirectional CFRPS," J. of Composite Materials, Vol. 29, 1995, p. 1808.

19.

19. Saff, C. R. , "Effect of Load Frequency and Lay-up on Fatigue Life of Composites," ASTM STP 813, 1983, p. 78.

20.

20. Reifsnider, K. L. , et al. , "Frequency Effects on a Stiffness-Based Fatigue Failure Criterion in Flawed Composite Specimens," ASTM STP 636, 1977, p. 71.

21.

21. Stinchcomb, W. W. and Reifsnider, K. L. et al. , "Effect of Frequency on the Mechanical Response of Two Composite Materials to Fatigue Loads," ASTM STP 569, 1975, p. 115.

22.

22. Kujawski, D. and Ellyin, F. , "Rate/Frequency-Dependent of Fiber Glass-Epoxy Laminates in Tensile and Cyclic Loading," Composites, Vol. 26, 1995, p. 719.

23.

23. Lin, S. H. and Ma, C. C. M. et al. , "Effect of Frequency on the Fatigue Behavior of [+45]4s Laminates of Carbon Fiber Reinforced PEEK Composites under Tension-Tension Loading," J. of Polymer Research, Vol. 2, No. 3, 1995, p. 171.

24.

24. Shuler, S. F. et al. , "Influence of Loading Frequency on the Room-Temperature Fatigue of a Carbon-Fiber/SiC-Matrix Composite," . of American Ceramic Society, Vol. 76, No. 9, 1993, p. 2327.