Foaming behavior of poly(lactic acid) with different D-isomer content based on supercritical CO 2 -induced crystallization

Abstract

Using supercritical carbon dioxide (sc-CO₂) as a physical foaming agent, the effect of sc-CO₂ on the formation of crystalline domains and subsequently on the foaming behaviors of the two grades of PLA with different D-isomer content were investigated in a wide foaming temperature range. The PLA’s final crystallinity is significantly increased with decreasing annealing temperature and by reducing the D-isomer content. Cellular structure results show that not only the crystallinity but also the crystalline morphology play an important role in cellular structure. A novel spherulite morphology including ringless and ring-banded morphology in the same spherulite was formed at lower foaming temperature, as a result, some entities were nonuniformly distributed in the PLA foams. Uniform and closed cellular structure were obtained when only the ring-banded spherulites were formed. An opened and interconnected cellular structure is tended to be formed because of the synergistic effect of high temperature and plasticization of CO₂. Based on the crystallinity and morphology, a suitable foaming window as a function of temperature is proposed. It is found that PLA with 4.1% D-isomer content had much broader suitable foaming window range to produce homogeneous cellular structure.