Influence of nucleating agent type on the morphology of extruded polyetherimide foam for printed circuit boards*

Abstract

This work focuses on the development of foamed high temperature thermoplastic substrates for printed circuit boards. For this application it is necessary to achieve mean cell diameters smaller than 30 µm in order to be able to realize vias and high packaging densities (miniaturization). Different additives as nucleating agents, namely macro- and micro-crystalline talc, silica, calcium carbonate, and wollastonite, were melt-compounded with polyetherimide using a twin-screw extruder. Foamed samples are prepared by foam extrusion using a slit die and CO₂ as physical blowing agent. The aim of this study is to analyze the influence of the mean particle size and the particle surface tension on the mean cell diameters. Therefore, the shape of the additives, the foam morphology, and the elongational viscosity were considered. The additives with a suitable particle size and surface tension exhibit a positive influence on the foam morphology, resulting in smaller cell diameters (<30 µm), a narrower cell size distribution and a foam density lower than 900 kg/m³. If the mean particle diameter of the nucleating agents is lower than 0.6 µm in this study, no nucleation effect could be observed. This is related to the fact that no heterogeneous nucleation occurs, if the particle diameter is too small. If the mean particle diameter of the used additives is larger than 1.5 µm, which could be demonstrated in this study in case of polyetherimide, then the additive acts as nucleating agent and heterogeneous nucleation occurs. Furthermore, it was observed that the mean cell diameter was affected by the different surface tensions of the studied nucleating agents.