The biodegradability and low cost of natural fibers make them attractive for composite applications. However, the density of natural fibers is higher than that of polymers, which increases the density of natural fiber composites. This drawback could be reduced by foaming. In this study, a polypropylene/rice husk natural fiber composite was extrusion foamed by a single-screw extruder using CO2 as the blowing agent. The effects of coupling agent, screw rotation speed, CO2 content, and die temperature on the cell structure were studied. Because moisture and volatile organic compounds from rice husks could be released during the extrusion process and deteriorate the cell structure, the thermal degradation behavior of rice husks was simulated using thermogravimetric analysis. The experiment results showed that the addition of a coupling agent improved the cell morphology and reduced the cell size of the composite. Before the coupling agent was added, there was a clear relation between the foam density and both the screw speed and the CO2 loading level. However, the relation disappeared after the coupling agent was added. The foam density decreased much more significantly with the decreasing die temperature. The lowest foam density achieved in this experiment was 0.6 g/cm3. Melt fracture phenomena were observed when the die temperature was below 160°C. In addition, a bouquet-like anisotropic cell structure was observed at a low die temperature of 147°C.
Ahmad FuadMYJamaludinMMohd IshakZAet al.
Rice husk ash as fillers in polypropylene: a preliminary study. Int J Polym Mater1993;
19: 75–92.
6.
Ahmad FuadMYYaakobIMohd IshakZAet al.
Density measurement of rice husk ash filler particles in polypropylene composites. Polym Test1993;
12: 107–112.
7.
Ahmad FuadMYZainiMJMohd IshakZAet al.
Rice husk ash (RHA)-based silica as filler in polypropylene composite: effect of peroxide-containing silane on the rheological behavior. J Elastomer Plast1994;
26: 252–264.
8.
FuadAMYIshakMZAOmarMAK.Rice husk ash as filler in polypropylene: effect of wax and silane coupling agents. Plast Rubber Compos Process Appl1994;
21: 225–235.
9.
Ahmad FuadMYIsmailZMansorMSet al.
Mechanical properties of rice husk ash/polypropylene composites. Polym J1995;
27: 1002–1015.
10.
Ahmad FuadMYMustafahJMansorMSet al.
Thermal properties of polypropylene/rice husk ash composites. Polym Int1995;
38: 33–43.
11.
IsmailHChungFL.The effect of partial replacement of silica by white rice husk ash in natural rubber composites. Int J Polym Mater PO1999;
43: 301–312.
12.
YangHSWolcottMPKimHSet al.
Effect of different compatibilizing agents on the mechanical properties of lignocellulosic material filled polyethylene bio-composites. Compos Struct2007;
79: 369–375.
BledzkiAKMamunAABonniaNNet al.
Basic properties of grain by-products and their viability in polypropylene composites. Ind Crop Prod2012;
37: 427–434.
15.
AridiNAMSapuanSMZainudinESet al.
Investigating morphological and performance deterioration of injection-molded rice husk–polypropylene composites due to various liquid uptakes. Int J Polym Anal Charact2016;
21: 675–685.
16.
YehS-KHsiehC-CChangH-Cet al.
Synergistic effect of coupling agents and fiber treatments on mechanical properties and moisture absorption of polypropylene–rice husk composites and their foam. Compos Part A2015;
68: 313–322.
17.
JearanaisilawongPEahkanongSPhungsaraBet al.
Determination of in-plane elastic properties of rice husk composite. Mater Des2015;
76: 55–63.
18.
AgrawalASatapathyA.Mathematical model for evaluating effective thermal conductivity of polymer composites with hybrid fillers. Int J Therm Sci2015;
89: 203–209.
19.
YamRCMMakD.A cleaner production of rice husk-blended polypropylene eco-composite by gas-assisted injection moulding. J Cleaner Prod2014;
67: 277–284.
20.
BurgstallerC.A comparison of processing and performance for lignocellulosic reinforced polypropylene for injection moulding applications. Compos Part B2014;
67: 192–198.
21.
SharmaJChandN.Dynamic mechanical analysis and dielectric studies of agro-waste rice husk/polypropylene composites with cenosphere. J Compos Mater2012;
47: 1833–1842.
22.
AyrilmisNKwonJHHanTH.Improving bending and tensile properties of lignocellulosic filled polypropylene composite panels using aramid fabric. Fibers Polym2014;
15: 2410–2415.
23.
NourbakhshAAshoriAKazemi TabriziA.Characterization and biodegradability of polypropylene composites using agricultural residues and waste fish. Compos Part B2014;
56: 279–283.
24.
GuoGLeeYHRizviGMet al.
Influence of wood fiber size on extrusion foaming of wood fiber/HDPE composites. J Appl Polym Sci2008;
107: 3505–3511.
25.
ChtourouHRiedlBAit-KadiA.Reinforcement of recycled polyolefins with wood fibers. J Reinf Plast Compos1992;
11: 372–394.
26.
RajRGKoktaBVGroleauGet al.
Use of wood fiber as a filler in polyethylene. Studies on mechanical properties. Plastics Rubber Proc Appl1989;
11: 215–221.
27.
ParkBDBalatineczJJ.Effects of impact modification on the mechanical properties of wood-fiber thermoplastic composites with high impact polypropylene (HIPP). J Thermoplast Compos Mater1996;
9: 342–364.
28.
SadikTPillonCCarrotCet al.
Polypropylene structural foams: measurements of the core, skin, and overall mechanical properties with evaluation of predictive models. J Cell Plast2016;
53: 25–44.
29.
MatuanaLMParkCBBauvhneczJJ.Cell morphology and property relationships of microcellular foamed PVC/wood-fiber composites. Polym Eng Sci1998;
38: 1862–1872.
30.
KordB.Preparation and characterization of lignocellulosic material filled polyethylene composite foams. J Thermoplast Compos Mater2012;
25: 917–926.
31.
MatuanaLMParkCBBalatineczJJ.Processing and cell morphology relationships for microcellular foamed PVC/wood-fiber composites. Polym Eng Sci1997;
37: 1137–1147.
32.
RizviGMParkCBGuoG.Strategies for processing wood plastic composites with chemical blowing agents. J Cell Plast2008;
44: 125–137.
33.
ParkCBBehraveshAHVenterRD.Low density microcellular foam processing in extrusion using CO2. Polym Eng Sci1998;
38: 1812–1823.
34.
LeungSNWongAGuoQPet al.
Change in the critical nucleation radius and its impact on cell stability during polymeric foaming processes. Chem Eng Sci2009;
64: 4899–4907.
35.
LeungSNParkCBXuDLet al.
Computer simulation of bubble-growth phenomena in foaming. Ind Eng Chem Res2006;
45: 7823–7831.
CooperAI.Polymer synthesis and processing using supercritical carbon dioxide. J Mater Chem2000;
10: 207–234.
38.
TomaskoDLLiHLiuDet al.
A review of CO2 applications in the processing of polymers. Ind Eng Chem Res2003;
42: 6431–6456.
39.
OkolieochaCRapsDSubramaniamKet al.
Microcellular to nanocellular polymer foams: progress (2004-2015) and future directions – a review. Eur Polym J2015;
73: 500–519.
40.
RizviGMParkCBLinWSet al.
Expansion mechanisms of plastic/wood-flour composite foams with moisture, dissolved gaseous volatiles, and undissolved gas bubbles. Polym Eng Sci2003;
43: 1347–1360.
ZhangHRizviGMParkCB.Development of an extrusion system for producing fine-celled HDPE/wood-fiber composite foams using CO2 as a blowing agent. Adv Polym Technol2004;
23: 263–276.
43.
GuoG. Development of fine-celled bio-fiber composite foams using physical blowing agents and nano-particles. PhD Dissertation, University of Toronto, 2006, p. 239.
44.
HanXMKoellingKWTomaskoDLet al.
Continuous microcellular polystyrene foam extrusion with supercritical CO2. Polym Eng Sci2002;
42: 2094–2106.
45.
ParkCBCheungLK.A study of cell nucleation in the extrusion of polypropylene foams. Polym Eng Sci1997;
37: 1–10.
46.
KubokiT.Foaming behavior of cellulose fiber-reinforced polypropylene composites in extrusion. J Cell Plast2014;
50: 113–128.
47.
WangYChenF-BWuK-C.Effect of the molecular weight of maleated polypropylenes on the melt compounding of polypropylene/organoclay nanocomposites. J Appl Polym Sci2005;
97: 1667–1680.
48.
LiTQWolcottMP.Rheology of wood plastics melt. Part 1. Capillary rheometry of HDPE filled with maple. Polym Eng Sci2005;
45: 549–559.
49.
ZhangYParentJSKontopoulouMet al.
Foaming of reactively modified polypropylene: effects of rheology and coagent type.J Cell Plast2015;
51: 505–522.
50.
GuoGRizviGMParkCBet al.
Critical processing temperature in the manufacture of fine-celled plastic/wood-fiber composite foams. J Appl Polym Sci2004;
91: 621–629.
51.
ZhaiWKubokiTWangLet al.
Cell structure evolution and the crystallization behavior of polypropylene/clay nanocomposites foams blown in continuous extrusion. Ind Eng Chem Res2010;
49: 9834–9845.
52.
ZhaiWParkCBKontopoulouM.Nanosilica addition dramatically improves the cell morphology and expansion ratio of polypropylene heterophasic copolymer foams blown in continuous extrusion. Ind Eng Chem Res2011;
50: 7282–7289.