Expanded polylactic acid - an eco-friendly alternative to polystyrene foam

Abstract

A commercially viable process to manufacture low-density expanded polylactic acid (E-PLA) products with environmental-friendly blowing agents such as carbon dioxide has been developed. The resulting material is a sustainable alternative to expanded polystyrene (EPS). The E-PLA has thermal conductivity and mechanical properties comparable to EPS and can be used in many similar applications. The process involves impregnation of PLA beads with carbon dioxide and fusing with heat, including steam heating. Gel permeation chromatography indicated that the PLA polymer molecular weight was not degraded by the foaming or steam heating process. Visual characterization showed that under some circumstances, PLA precursor beads exhibited voids, which disappeared during CO₂ impregnation indicating some form of rearrangement or realignment of the polymer morphology or structure. Due to the effect of CO₂ on the glass transition temperature of the PLA, a linear reduction of 5.5°C per wt% of absorbed CO₂ was observed.

Keywords

polylactic acid CO2 foaming expanded polystyrene mechanical properties

Get full access to this article

View all access options for this article.

References

www.eumeps.org (accessed on June 2009).

Bandyopadhyay A. and Basak GC Studies on photocatalytic degradation of polystyrene . Mater Sci Technol 2007; 23(3): 307-317.

http://lightweightconcreteco.com/products/foamlite/recycl/ (accessed on June 2009).

Clydesdale P. 3rd Bioplastics Market Conference (2009).

Witt M. , Parker K. , Shah S. and Anderson R. BIOFOAMS 2007 Conference (2007).

Garlotta D. A literature review of poly(lactic acid). J Polym Environ 2001; 9(2): 63-84.

Di Landro L. , Sala G. and Olivieri D. Deformation mechanisms and energy absorption of polystyrene foams for protective helmets. Polym Test 2002; 21(2): 217-228.

Yu L. , Lui H. and Dean K. Thermal behavior of poly(lactic acid) in contact with compressed carbon dioxide . Polym Int 2009; 58(4): 368-372.