Abstract
The viscoelastic properties of Aeromonas (A) gum in water were investigated by using the Rheometric Scientific ARES controlled strain rheometer. An intrinsic viscosity of 8336 ml/g was obtained according to the Fuoss–Straus equation. The effect of salt concentration on intrinsic viscosity revealed that the A gum exists as semiflexible chain. Typical shear-thinning (pseudoplastic) behavior was observed at concentrations higher than 0.52%. The zero shear viscosity (η0) increased with increasing polysaccharide concentration (c) showing a gradient of approximately 1.0, 2.9 and 4.8 in different concentration domains. The critical concentrations c* and c**, at which the transitions from a dilute solution of independently moving chains to semidilute and then concentrated domains occurred, were determined roughly to be 1.2% and 3.5%. The results from dynamic experiments revealed that the A gum solution shows characteristics of polymer solutions without any evidence of gel-like character. All the results from steady and dynamic tests suggest that the A gum is a non-gelling polysaccharide. The temperature dependence of apparent viscosity was described by Arrhenius equation and the flow activation energy was estimated to be 45.2 kJ/mol, which is independent on polymer concentration.
Get full access to this article
View all access options for this article.