Transverse Stitched T-Joints in Bending with PR520 Resin: Initial Results

Abstract

An experimental investigation was undertaken to evaluate the bending strength of transversely stitched T-joints using fiber insertion as the primary load transfer mechanism and using resin transfer molding with PR520 toughened epoxy resin. Tests were conducted to determine the ultimate bending strength of two joint configurations and fractographic examination was performed to determine joint failure mechanisms. This study shows that increasing the web thickness and the subsequent number of rows of stitching has the effect of increasing the initial and maximum bending strength of the T-joint design. As indicated by the fractographic examination, initial joint failure occurs by matrix cracking initiating at the resin rich corner fillet and propagates inward toward the transverse stitching; and ultimate joint failure occurs by fiber breakage and/or fiber pullout.

Keywords

composite T-joint transverse stitching fiber insertion flexural strength resin transfer molding PR520 resin

Get full access to this article

View all access options for this article.

References

1. Baker, A. “Joining and Repair of Aircraft Composite Structures” in Composite Materials Handbook, Edited by P.K. Mallick , Marcel Decker, NY, 1997.

2. J. A. Soden , G. Weissenbach , and B.J. Hill , “The Design and Fabrication of 3D Multi-layer Woven T-Section Reinforcements,” Composite Part A: Applied Science and Manufacturing, Vol. 30 (1999) pp. 213–220.

3. L. K. Jain and Y-W Mai , “Recent Work on Stitching of Laminated Composites—Theoretical Analysis and Experiments,” Proceedings of ICCM-1 1, (1997) pp. 25–51.

4. E. E. Theotokoglou and T. Moan , “Experimental and Numerical Study of Composite T-Joint,” Journal of Composite Materials, Vol. 30, No. 2, (1996) pp. 190–209.

5. E. E. Theotokoglou , “Study of Numerical Fracture Mechanics Analysis of Composite T-Joints,” Journal of Reinforced Plastics and Composites, Vol. 18, No. 3, (1999) pp. 215–223.

6. E. E. Theotokoglou , “Strength of Composite T-Joints Under Pull-Out Loads,” Journal of Reinforced Plastics and Composites, Vol. 16, No. 6, (1997) pp. 503–518.

7. W. B. Young and M. T. Chuang , “Fabrication of T-shaped Composite Through Resin Transfer Molding,” Journal of Composite Materials, Vol. 29, No. 16, (1996) pp. 2192–2214.

8. A. R. Rispler , G. P. Stevens , and L. Tong , “Failure Analysis of Composite T-Joints Including Inserts,” Journal of Reinforced Plastics and Composites, Vol. 16, No. 18, (1997) pp. 1642–1658.

9. Y. Tada and T. Ishikawa , “Experimental Evaluation of the Effects of Stitching on CFRP Laminate Specimens with Various Shapes and Loadings,” Key Engineering Materials, Vol. 37, (1989) pp. 305–316.

10.

10. G. Freitas , T. Fusco , T. Campbell , J. Harris and S. Rosenberg , “Z-Fiber Technology and Products for Enhancing Composite Design,” AGARD Conference Proceedings 590, Bolted/Bonded Joints in Polymeric Composites, (1997) pp. 17-1–17-8.

11.

11. P.B. Stickler , M. Ramulu , and P.S. Johnson , “Experimental and Numerical Analysis of Transverse Stitched T-Joints in Bending,” Composite Structures, Vol. 50(1), (2000) pp. 17–27.

12.

12. B.J. Sullivan , R. Miller , K. Ouellette and B. Coffenberry , “Short Beam Shear Test Design and Results for 3-D Woven Reinforced Composites,” 43rd International SAMPE Symposium, (1998) pp. 1205–1213.

13.

13. D. Jarmon , C.A. Weeks , R.A. Naik , C.L. Kogstrom , C.P. Logan and P.F. Braun , “Mechanical Property Comparison of 3-D and 2-D Graphite Reinforced Epoxy Composites Fabricated by Resin Transfer Molding,” 43rd International SAMPE Symposium, (1998) pp. 2043–2056.

14.

14. C.A. Weeks , R.A. Naik , and C.L. Kogstrom , “Analysis of Damage in Through Thickness Reinforced Composites Induced by Soft Body Impact,” 43rd International SAMPE Symposium, (1998) pp. 2070–2081.

15.

15. C.A. Weeks , S.R. Morris , C.L. Kogstrom , R.A. Naik , and C.P. Logan , “Manufacture and Assessment of 3D Woven Turbofan Compressor Fan Blades,” 43rd International SAMPE Symposium, (1998) pp. 2082–2094.