Abstract
An ideal biomaterial for urethral reconstruction has not been developed. To create a urethral graft biomaterial with optimal biodegradability and biocompatibility, a copoly(L-lactide/∊-caprolactone) [P(LA/CL)] fabric tube was combined with a type I collagen sponge. The P(LA/CL) fibers were knitted into a vascular stent style (Type 1) or weaved into a mesh style (Type 2) to prepare P(LA/CL) tubes. The tubes were dipped in aqueous collagen solution and lyophilyzed to prepare the P(LA/CL)–collagen sponge graft. The grafts were applied to a 1.5-cm rabbit urethral defect (n = 14 for each condition), and tissue repair was evaluated using urethrographical, urethroscopical, and histological examination 1, 3, and 6 months after surgery. Although epithelialization was observed after 1 month in all Type 1 grafts, stenoses, fistulae, or stone formation was seen in 7 of the rabbits. In some cases, P(LA/CL) fibers prolapsed into the urethral lumen, causing stone formation. Only 3 rabbits survived for 6 months, and 2 of these had stenoses. For the Type 2 graft, all urethras were patent, without fistulae or stenoses, over the entire observation period. Histologically, urethral structure was disorganized for the Type 1 graft, whereas the urethral tissue on the Type 2 graft was slightly fibrotic but completely epithelialized and supported by a regenerated smooth muscle layer at 6 months. These findings suggest that creation of a scaffold suitable for urethral tissue regeneration will depend not only on the biomaterial composition, but also on the fabrication technique.
Get full access to this article
View all access options for this article.