Abstract
The poor surface finish of as-printed (AP) laser powder bed fusion (L-PBF) 316L stainless steels has detrimental impacts on the resulting fatigue and corrosion performance. One postprocessing method, a self-terminating etching process (STEP), can improve the surface finish of parts up to 76%, but the resulting effects on fatigue life and corrosion reliability remain unknown. This work evaluates the effect of the STEP on the fatigue and corrosion performance of L-PBF 316L. In addition, to determine the influence of changing the microstructures from the as-built condition, specimens having undergone a pre-STEP stress relief (SR + STEP) heat treatment and a pre-STEP solution anneal (SA + STEP) were evaluated. The results showed that a pre-STEP SR resulted in the best Sa roughness, while a pre-STEP SA had the biggest improvement in Sv roughness. Despite Sv roughness being a major indicator of fatigue performance, the coarse grains and internal porosity in the SA specimens resulted in the poorest fatigue performance. The SR + STEP specimens' fatigue lives were 10 × higher than the AP samples under a load of 275 MPa and 2–3 × higher under a 350 MPa load. The SR + STEP specimen also had the best corrosion performance in a sodium chloride electrolyte due to the smoother surface and least remnant surface carbides.
Get full access to this article
View all access options for this article.
References
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.