Numerous cholesteric copoly(ester-imide)s were prepared from mixtures of isosorbide and tert.-buthylhydroquinone (or other diphenols), on the one hand, and mixtures of adipoylchloride and N-(4-chlorocarbonylphenyl) trimellitimide chloride on the other. When the molar ratio of isosorbide/diphenol was varied, Grandjean textures were only observed for low concentrations of isosorbide (5/95 or 10/90). In the case of adipoylchloride/imide dichloride molar ratios of 30/70–50/50 favoured the formation of Grandjean textures. Most copoly(esterimide)s were non-crystalline with glass transition temperatures (T _gs) between 90 and 190 °C. In several cases the Grandjean textures were frozen in by cooling below T _g. Such copoly(esterimide)s may be useful as pigments. All copoly(ester-imide)s containing methylhydroquinone were semicrystalline with melting temperatures in the range of 240–270 °C.

Get full access to this article

View all access options for this article.

References

[1] Kricheldorf H R 1994 Mol. Cryst. Liq. Cryst. 254 87-87

[2] Kricheldorf H R and Gurau M 1995 J.M.S.–Pure Appl. Chem. A 32 1831-1831

[3] Kricheldorf H R , Probst N and Wutz Ch 1995 Macromolecules 28 7990-7990

[4] Kricheldorf H R and Probst N 1995 Makromol. Rapid. Commun. 16 231-231

[5] Kricheldorf H R and Berghahn M 1995 J. Polym. Sci., Part A, Polym. Chem. 33 427-427

[6] Kricheldorf H R , Probst N , Gurau M and Berghahn M 1995 Macromolecules 28 6565-6565

[7] Schwarz G and Kricheldorf H R 1996 J. Polym. Sci., Part A, Polym. Chem. 34 603-603

[8] Stumpe J , Ziegler A , Berghahn M and Kricheldorf H R 1995 Macromolecules 28 5306-5306

[9] Probst N and Kricheldorf H R 1995 High Perform. Polym. 7 461-461

10.

[10] Kricheldorf H R and Probst N 1995 High Perform. Polym. 7 471-471

11.

[11] Bouligand Y 1973 J. Physique 34 603-603

12.

[12] de Jeu H W and Vertogen G 1977 Thermotropic Liquid Crystals (Berlin: Springer)

13.

[13] Etzbach K H, Delavier P, Siemensmeyer K, Wagenblast G, Laupichler L and Vill V 1995 DE.-OS. 4.343.280 to BASF AG

14.

[14] Kricheldorf H R and Sun S-J High Perform. Polym. at press

15.

[15] Kricheldorf H R , Sun S-J and Gerken A Macromol. Rapid. Commun. at press

16.

[16] Buning T J and Kreuzer F-H 1995 Trends Polym. Sci. 3 318-318

17.

[17] Vill V , Fischer F and Thiem J 1988 Z. Naturforsch. 43a 1119-1119

18.

[18] Kricheldorf H R , Domschke A and Schwarz G 1991 Macromolecules 24 1011-1011

19.

[19] de Abajo J , de la Campa J , Kricheldorf H R and Schwarz G 1992 Eur. Polym. J. 28 261-261

20.

[20] Kricheldorf H R , Schwarz G , Domschke A and Linzer V 1993 Macromolecules 26 5161-5161

21.

[21] Beston J , Dewinter W and Black W B 1972 J. Polym. Sci. Polym. Chem. Ed. 10 1377-1377

22.

[22] Kurita K and Matsuda S 1983 Makromol. Chem. 184 1223-1223

23.

[23] Kricheldorf H R 1978 Makromol. Chem. 179 2133-2133

24.

[24] Kricheldorf H R , Mang Th and Jonté J M 1985 Makromol. Chem. 186 955-955

LC Polyimides 29. Non-Crystalline Cholesteric Copoly(Ester-Imide)s Derived from Adipic Acid and Isosorbide

Abstract

Get full access to this article

References