Automated Tow Placed LARC™-PETI-5 Composites

Abstract

LARC™-PETI-5 is a PhenylEthynyl-Terminated Imide resin developed at NASA Langley Research Center (LARC) during the 1990s. It offers a combination of attractive composite and adhesive properties. IM7/LARC™-PETI-5 composites exhibit thermal and thermo-oxidative stability typical of polyimides, superior chemical resistance and processability, excellent mechanical properties, toughness and damage tolerance. It was selected for study in the High Speed Research program aimed at developing technologies for a future supersonic aircraft, the High Speed Civil Transport, with a projected life span of 60 000 h at a cruise speed up to March 2.4. Robust autoclave processing cycles for LARC™-PETI-5 composites have been thoroughly designed and demonstrated, which involved hand lay-up of solvent-ladened ‘wet’ prepregs. However, this type of processing is not only costly but also environmentally unfriendly. Volatile management and shrinkage could become serious problems in the fabrication of large complex airframe structural subcomponents. Robotic tow placement technology utilizing ‘dry’ material forms represents a new fabrication process which overcomes these deficiencies.

This work evaluates and compares mechanical properties of composites fabricated by heated head automated tow placement (dry process) with those obtained by hand lay-up/autoclave fabrication (wet process). Thermal and rheological properties of the robotically as-placed uncured composites were measured. A post-cure cycle was designed due to the requirement of the PETI-5 resin for a 370 °C/1 h hold to reach full cure, conditions which cannot be duplicated during heated head robotic placement. Mechanical properties such as 0° flexural strength and modulus, open hole tensile and compressive strength and moduli, reduced section compression dogbone compressive strength, and modified zippora-medium small (MZ-MS) tensile and compressive properties were obtained on the post-cured panels. These properties compared favourably with those obtained from the wet process.

Get full access to this article

View all access options for this article.

References

[1] Hergenrother P M 2000

Development of composites, adhesives and sealants for high-speed commercial airplanes

SAMPE J. 36 30-30

[2] Bryant R G , Jensen B J and Hergenrother P M 1993

Synthesis and properties of phenylethynyl-terminated polyimides

Polym. Prepr. 34 566-566

[3] Jensen B J , Bryant R G and Wilkinson S P 1994

Development of a unique copolyimide backbone for imide oligomers with terminal reactive groups

Polym. Prepr. 35 539-539

[4] Havens S J , Bryant R G , Jensen B J and Hergenrother P M 1994

Phenylethynyl terminated imide oligomers and polymers therefrom

Polym. Prepr. 35 553-553

[5] Smith J G Jr and Hergenrother P M 1994

Chemistry and properties of phenylethynyl phthalic anhydride imide oligomers

Polym. Prepr. 35 353-353

[6] Hergenrother P M , Bryant R G , Jensen B J , Smith J G Jr and Wilkinson S P 1994

Chemistry and properties of phenylethynyl terminated imide oligomers and their cured polymers

Soc. Adv. Mater. Proc. Eng. Series 39 961-961

[7] Rommel M L , Konopka L and Hergenrother P M 1996

Process development and mechanical properties of IM7/LaRC-PETI5 composites

Intl. SAMPE Tech. Conf. Series 28 1-1

[8] Hou T H , Jensen B J and Hergenrother P M 1996

Processing and properties of IM7/PETI composites

J. Comp. Mater. 30 109-109

[9] Smith J G Jr , Connell J W , Hergenrother P M and Criss J M 2000

High temperature transfer molding resins

Soc. Adv. Mater. Proc. Eng. Series 45 1584-1584

10.

[10] Lamontia M A 1999 Private communications, Lamontia Technical Services

11.

[11] Rommel M 1994 Private communication, Northrop Grumman Co

12.

[12] 1998 Boeing specification BSS-7320, Boeing Co, Seattle, WA

13.

[13] Coguill S L 2000 Private communication, Composite Materials Research Group, University of Wyoming, Laramie, WY