Environmental Exposure Conditions for Teflon® Fluorinated Ethylene Propylene on the Hubble Space Telescope

Abstract

The outer layer of Teflon® fluorinated ethylene propylene (FEP) multi-layer insulation (MLI) on the Hubble Space Telescope (HST) was observed to be significantly cracked at the time of the Second HST Servicing Mission (SM2), 6.8 years after HST was launched into low Earth orbit (LEO). Comparatively minor embrittlement and cracking were also observed in the FEP materials retrieved from solar-facing surfaces on the HST at the time of the First Servicing Mission (3.6 years exposure). After SM2, a failure review board was convened to address the problem of degradation of MLI on the HST. In order for this board to determine possible degradation mechanisms, it was necessary to consider all environmental constituents to which the FEP MLI surfaces were exposed. Based on measurements and various models, the environmental exposure conditions for the FEP surfaces on the HST were estimated, including: the number and temperature ranges of thermal cycles; equivalent sun hours; fluence and absorbed radiation dose of x-rays, trapped protons and electrons and plasma electrons and protons; and atomic oxygen (AO) fluence. This paper presents the environmental exposure conditions for FEP on the HST, briefly describing the possible roles of the environmental factors in the observed FEP embrittlement and providing references to the published works which describe in detail testing and analysis related to FEP degradation on the HST.

Get full access to this article

View all access options for this article.

References

[1] Zuby T M , de Groh K K and Smith D C 1995

Degradation of FEP thermal control materials returned from the Hubble Space Telescope

NASA Technical Memorandum 104627-104627

[2] Hansen P A , Townsend J A , Yoshikawa Y , Castro J D , Triolo J J and Peters W C 1998 Sci. Advanced Mater. Process Eng. Series 43 570-570

[3] Townsend J A , Hansen P A , Dever J A , de Groh K K , Banks B A , Wang L and He C 1999 High Perform. Polym. 11 81–100

[4] Dever J A , de Groh K K , Townsend J A and Wang L L 1998 Mechanical properties degradation of Teflon FEP returned from the Hubble Space Telescope AIAA Paper No 98-0895, NASA Technical Memorandum 1998-206618

[5] Reed R P , Schramm R E and Clark A F 1973 Cryogenics 13 67–82

[6] Dever J A 1991

Low Earth orbital atomic oxygen and ultraviolet radiation effects on polymers

NASA Technical Memorandum 103-103 711-711

[7] Tribble A C 1995 The Space Environment: Implications for Spacecraft Design (Princeton, NJ: Princeton University Press) p 155-155

[8] Van Eesbeek M , Levadou F and Milintchouk A 1995 Proc. Hubble Space Telescope Solar-Array Workshop ESA WPP-77 p 405-405

[9] Dever J A , de Groh K K , Banks B A and Townsend J A 1999 High Perform. Polym. 11 123–140

10.

[10] Townsend J , Powers C , Viens M , Ayres-Treusdell M and Munoz B 1998 Proc. 20th Space Simulation Conf. NASA Conference Report 1998-208598

11.

[11] Drolshagen G 1995 Proc. Hubble Space Telescope Solar-Array Workshop ESA WPP-77 pp 53–65

12.

13.

14.

[14] Dever J A , Townsend J A , Gaier J R and Jalics A I 1998 Sci. Advanced Mater. Process Eng. Ser. 43 616–628

15.

[15] Banks B A , de Groh K K , Stueber T J , Sechkar E A and Hall R L 1988

Ground laboratory soft x-ray durability evaluation of aluminized Teflon® FEP thermal control insulation

NASA Technical Memorandum 1998-297964/REV1

16.

[16] Sawyer D M and Vette J I 1976 AP-8 trapped proton environment for solar maximum and solar minimum NSSDC/WDC-A-R&S, 76-06, NASA/Goddard Space Flight Center, Greenbelt, MD, USA

17.

[17] Vette J I 1991 The AE-8 trapped electron model environment, NSSDC/WDC-A-R&S 91-24, NASA/Goddard Space Flight Center, Greenbelt, MD, USA

18.

[18] Jordan T M 1991

Space system analysis using the NOVICE code system

Trans. of RADECS 91 (Montpellier, France, September 9–12, 1991)

19.

[19] Bilitza D , Rawer K , Bossy L and Gulyaeva T 1993

International reference ionosphere—past, present, future

Adv, Space Res. 13 2–23

20.

[20] De Groh K and Smith D 1997

Investigation of Teflon FEP embrittlement on spacecraft in low Earth orbit

NASA Technical Memorandum 113153-113153

21.

[21] Hedin A E 1987

MSIS-86 thermospheric model

J. Geophys. Res. 92 4649–4662

22.

[22] Johnson Space Center 1991 Flight Requirements Document NSTS 17462-17462-82

23.

[23] 1998 National Geophysical Data Center, Solar–Terrestrial Physics Division (E/GC2), 325 Broadway, Boulder, CO 80303-80303 USA

24.

[24] Schatten et al 1978 Geophys. Res. Lett. 5 411-411

25.

[25] Townsend J , Hansen P and Dever J 1998 Proc. 20th Space Simulation Conf. NASA Conference Report 1998-208598

26.

Townsend J Corporation 1990 Rocketdyne Division, Specification RC 1800 Review C p 18-18

27.

[27] Banks B A , Dever J A , Gebauer L and Hill C 1991 Atomic oxygen interactions with FEP Teflon and silicones on LDEF LDEF—69 Months in Space NASA Conference Publication 3134, part 2, pp 801–815

28.

[28] Sampair T R A

generalized approach to the thermal analysis of the Long Duration Exposure Facility’s flight experiments

LDEF—69 Months in Space NASA Conference Publication 3194, part 1, p 36-36