Hubble Space Telescope Metallized Teflon ® FEP thermal Control Materials: On-Orbit Degradation and Post-Retrieval Analysis

Abstract

During the Hubble Space Telescope (HST) second servicing mission (SM2), degradation of unsupported Teflon^® FEP (fluorinated ethylene propylene), used as the outer layer of the multilayer insulation (MLI) blankets, was evident as large cracks on the telescope light shield. A sample of the degraded outer layer was retrieved during the mission and returned to Earth for ground testing and evaluation. The results of the Teflon^® FEP sample evaluation and additional testing of pristine Teflon^® FEP led the investigative team to theorize that the HST damage was caused by thermal cycling with deep-layer damage from electron and proton radiation which allowed the propagation of cracks along stress concentrations, and that the damage increased with the combined total dose of electrons, protons, ultraviolet and x-ray radiation along with thermal cycling. This paper discusses the testing and evaluation of the retrieved Teflon^® FEP.

Get full access to this article

View all access options for this article.

References

[1] Zuby T , de Groh K and Smith D 1995

Degradation of FEP thermal control materials returned from the Hubble Space Telescope

NASA Technical Memorandum 104627-104627

[2] Hansen P A , Townsend J A , Yoshikawa Y , Castro J D , Triolo J J and Peters W C 1998

Degradation of Hubble Space Telescope metallized Teflon® FEP thermal control materials

Sci. Adv. Mater. Process Eng. Ser. 43 570–581

[3] Wang L , Viens M and Townsend J 1998

Mechanical properties and fractography of MLI FEP from the HST second service mission

Sci. Adv. Mater. Process Eng. Ser. 43 594–606

[4] Dever J A , de Groh K K , Townsend J A and Wang L L 1998

Mechanical properties degradation of Teflon® FEP returned from the Hubble Space Telescope

NASA/TM-1998-206618

[5] He C and Townsend J A 1998

Solar absorptance of the Teflon® FEP samples returned from the HST servicing missions

Sci. Adv. Mater. Process Eng. Ser. 43 607–615

[6] Townsend J A , Hansen P A , Dever J A and Triolo J J 1998

Analysis of retrieved Hubble Space Telescope thermal control materials

Sci. Adv. Mater. Process Eng. Ser. 43 582–593

[7] Milintchouk A , Van Eesbeek M , Levadou F and Harper T 1997 J. Spacecraft Rockets 34 542–548

[8] Mark H F 1983

Degradation of polymers in hostile environments

The Effects of Hostile Environments on Coatings and Plastics (Am. Chem. Soc. Symp. Ser. 229) (Washington, DC: American Chemical Society) pp 11–15

[9] Townsend J A , Powers C E , Viens M J , Ayers-Treusdell M T and Munoz B F 1998 Degradation of Teflon® FEP following charged particle radiation and rapid thermal cycling 20th Space Simulations Conf. Proc. (NASA/CR-1998-208598 preprint) pp 201–209

10.

[10] Hermans P H and Weidinger A 1948 J. Appl. Phys. 19 491-491

11.

[11] Parkinson W W 1990

Radiation-resistant polymers

Encyclopedia of Polymer Science and Engineering vol 13, 2nd edn, pp 667–703