Glassy state of wood polymers in native and thermally modified wood: Effects on long-term material performance in service 1

Abstract

This research analyses the effect of a glassy state of wood polymers, as found in some dense naturally durable wood species and in thermally modified wood (TMW), on their equilibrium moisture content, mechanical and fungal resistance (durability) performance. In the EN350-class I durability range, moisture and fungal durability are argued to become controlled by the physical state of wood polymers rather than their chemical composition. Glassy polymers may assist the dimensional stability and fungal resistance of wood, as characterised by standardised accelerated laboratory tests. However, for long-term mechanical performance and fungal resistance in service, strong cross-links must prevent the natural (aging) relaxation of the glassy state. Physical aging is expected to occur in TMW, as opposed to naturally durable wood species. The current test methodology for dimensional and fungal stability does not take physical aging effects in wood polymers into account.

Keywords

Heat-treated wood Glassy polymers Fungal resistance Moisture sorption Long-term service performance Soil contact

Get full access to this article

View all access options for this article.

References

Ahajji

, Diouf

P. N.

, Aloui

, Elbakali

, Perrin

, Merlin

and George

2009. Influence of heat treatment on antioxidant properties and colour stability of beech and spruce wood and their extractives. Wood Science and Technology. 43(1–2): 69–83. doi: 10.1007/s00226-008-0208-3

Back

E. L.

and Salmén

N. L.

1982. Glass transitions of wood components hold implications for molding and processing. Tappi. 65(7): 107–110.

Bourgois

and Guyonnet

1988. Characterization and analysis of torrefied wood. Wood Science and Technology. 22(2): 143–155. doi: 10.1007/BF00355850

Buitink

, Hemminga

M. A.

and Hoekstra

F. A.

2000. Molecular mobility in the cytoplasm of lettuce radicles correlates with longevity. Seed Science Research. 10(3): 285–292. doi: 10.1017/S0960258500000325

Chaouch

, Dumarçay

, Pétrissans

and Gérardin

2013. Effect of heat treatment intensity on some conferred properties of different European softwood and hardwood species. Wood Science and Technology. 47(4): 663–673. doi: 10.1007/s00226-013-0533-z

Ergun

, Lietha

and Hartel

R. W.

2010. Moisture and shelf life in sugar confections. Critical Reviews in Food Science and Nutrition. 50(2): 162–192. doi: 10.1080/10408390802248833

Fengel

and Wegener

1983. Wood: Chemistry, Ultrastructure, Reactions. Berlin: Walter de Gruyter.

Flournoy

D. S.

, Kirk

T. K.

and Highley

T. L.

1991. Wood decay by brown-rot fungi: changes in pore structure and cell wall volume. Holzforschung. 45(5): 383–388. doi: 10.1515/hfsg.1991.45.5.383

González-Peña

M. M.

and Hale

M. D. C.

2007. The relationship between mechanical performance and chemical changes in thermally modified wood. in proceedings of the third European Conference on Wood Modification (ed. Hill, C.A.S. et al.), 169–172, Cardiff.

10.

Hakkou

, Pétrissans

, Gérardin

and Zoulalian

2006. Investigations of the reasons for fungal durability of heat-treated beech wood. Polymer Degradation and Stability. 91(2): 393–397. doi: 10.1016/j.polymdegradstab.2005.04.042

11.

Hill

C. A. S.

2006. Wood Modiﬁcation – Chemical, Thermal and Other Processes. Chichester: John Wiley & Sons.

12.

Hill

C. A. S.

, Keating

B. A.

, Jalaludin

and Mahrdt

2012. A rheological description of the water vapour sorption kinetics behaviour of wood invoking a model using a canonical assembly of Kelvin–Voigt elements and a possible link with sorption hysteresis. Holzforschung. 66(1): 35–47. doi: 10.1515/HF.2011.115

13.

Himmel

and Mai

2015. Water vapour sorption of wood modified by acetylation and formalisation – analysed by a sorption kinetics model and thermodynamic considerations. Holzforschung. doi:10.1515/hf-2015-0015

14.

Hoffmeyer

, Thygesen

L. G.

, and Engelund

E. T.

2011. Equilibrium moisture content (EMC) in Norway spruce during the first and second desorptions. Holzforschung. 65(6): 875–882. doi: 10.1515/HF.2011.112

15.

Hon

D. N. S.

and Shiraishi

1991. Wood and Cellulosic Chemistry. New York: Marcel Dekker.

16.

Hosseinpourpia

and Mai

2015a. Mode of action of brown rot decay resistance in phenol–formaldehyde-modified wood: resistance to Fenton's reagent. Holzforschung. doi:10.1515/hf-2015-0045

17.

Hosseinpourpia

and Mai

2015b. Mode of action of brown rot decay resistance of thermally modified wood: resistance to Fenton's reagent. Holzforschung. doi:10.1515/hf-2015-0141

18.

Hughes

, Hill

and Pfriem

2015. The toughness of hygrothermally modified wood. Holzforschung. 69(7): 851–862. doi: 10.1515/hf-2014-0184

19.

Karlsson

, Torniainen

, Dagbro

, Granlund

and Morén

2012. Presence of water-soluble compounds in thermally modified wood: carbohydrates and furfurals. BioResources. 7(3): 3679–3689.

20.

Kirker

G. T.

, Blodgett

A. B.

, Arango

R. A.

, Lebow

P. K.

and Clausen

C. A.

2013. The role of extractives in naturally durable wood species. International Biodeterioration & Biodegradation. 82: 53–58. doi: 10.1016/j.ibiod.2013.03.007

21.

LaRowe

D. E.

and van Cappellen

2011. Degradation of natural organic matter: a thermodynamic analysis. Geochimica et Cosmochimica Acta. 75(8): 2030–2042. doi: 10.1016/j.gca.2011.01.020

22.

Mayes

and Oksanen

2002. ThermoWood Handbook. Helsinki: International Thermowood Association.

23.

Militz

and Altgen

2014. Processes and properties of thermally modified wood manufactured in Europe. In: Schultz, T. P. et al. (eds). Deterioration and Protection of Sustainable Biomaterials. ACS Symposium Series 1158, Ch. 16, 269–285.

24.

Mitsui

, Inagaki

and Tsuchikawa

2008. Monitoring of hydroxyl groups in wood during heat treatment using NIR spectroscopy. Biomacromolecules. 9(1): 286–288. doi: 10.1021/bm7008069

25.

Obataya

, Higashihara

and Tomita

2002. Hygroscopicity of heat-treated wood III. Effects of steaming on the hygroscopicity of wood. Mokuzai Gakkaishi. 48(5): 348–355.

26.

Phuong

L. X.

, Takayama

, Shida

, Matsumoto

and Aoyagi

2007. Determination of the accessible hydroxyl groups in heat-treated Styrax tonkinensis (Pierre) Craib ex Hartwich wood by hydrogen–deuterium exchange and ²H NMR spectroscopy. Holzforschung. 61(5): 488–491. doi: 10.1515/HF.2007.086

27.

Ringman

, Pilgård

and Richter

2014. Effect of wood modification on gene expression during incipient Postia placenta decay. International Biodeterioration & Biodegradation. 86: 86–91. doi: 10.1016/j.ibiod.2013.09.002

28.

Sablík

, Giagli

, Parˇil

, Baar

and Rademacher

2016. Impact of extractive chemical compounds from durable wood species on fungal decay after impregnation of nondurable wood species. European Journal of Wood and Wood Products. doi:10.1007/s00107-015-0984-z

29.

Salmén

, Possler

, Stevanic

J. S.

and Stanzl-Tschegg

S. E.

2008. Analysis of thermally treated wood samples using dynamic FT-IR-spectroscopy. Holzforschung. 62(6): 676–678. doi: 10.1515/HF.2008.113

30.

Scheiding

and Direske

2014. Comparison of reaction to water and moisture of sapwood and heartwood of Pinus sylvestris L., thermally modified with two treatment intensities, in proceedings of the seventh European Conference on Wood Modification (ed. Nunes, L. et al.), Lisbon.

31.

Schultz

T. P.

and Nicholas

D. D.

2000. Naturally durable heartwood: evidence for a proposed dual defensive function of the extractives. Phytochemistry. 54(1): 47–52. doi: 10.1016/S0031-9422(99)00622-6

32.

Seborg

R. M.

, Tarkow

and Stamm

A. J.

1953. Effect of heat upon dimensional stabilization of wood. Journal of the Forest Products Research Society. 3: 59–67.

33.

Skaar

1988. Wood–Water Relations. Berlin: Springer Verlag.

34.

Suchy

, Virtanen

, Kontturi

and Vuorinen

2010. Impact of drying on wood ultrastructure observed by deuterium exchange and photoacoustic FT-IR spectroscopy. Biomacromolecules. 11(2): 515–520. doi: 10.1021/bm901268j

35.

Tausch

2011. Pilzresistenz von Thermoholz − gravimetrische und mikroskopische Untersuchungen. PhD Thesis, Albert-Ludwigs University, Freiburg am Breisgau, Germany.

36.

Tjeerdsma

B. F.

, Boonstra

, Pizzi

, Tekely

and Militz

1998. Characterisation of thermally modified wood: molecular reasons for wood performance improvement. Holz als Roh- und Werkstoff. 56(3): 149–153. doi: 10.1007/s001070050287

37.

Willems

2009. A novel economic large-scale production technology for high-quality thermally modified wood, in proceedings of the fourth European Conference on Wood Modification (ed. Englund, F. et al.), 31–35, Stockholm.

38.

Willems

2014. The water vapor sorption mechanism and its hysteresis in wood: the water/void mixture postulate. Wood Science and Technology. 48(3): 499–518. doi: 10.1007/s00226-014-0617-4

39.

Willems

, Mai

and Militz

2013a. Thermal wood modification chemistry analysed using van Krevelen's representation. International Wood Products Journal. 4(3): 166–171. doi: 10.1179/2042645313Y.0000000033

40.

Willems

, Gérardin

and Militz

2013b. The average carbon oxidation state of thermally modified wood as a marker for its decay resistance against Basidiomycetes. Polymer Degradation and Stability. 98(11): 2140–2145. doi: 10.1016/j.polymdegradstab.2013.09.003

41.

Willems

, Tausch

and Militz

2010. Direct estimation of the durability of high-pressure steam modified wood by ESR-spectroscopy. Doc. 10-40508. Stockholm, Sweden: International Research Group on Wood Protection.

42.

Zelinka

S. L.

, Gleber

S. C.

, Vogt

, Rodríguez López

G. M.

and Jakes

J. E.

2015. Threshold for ion movements in wood cell walls below fiber saturation observed by X-ray fluorescence microscopy (XFM). Holzforschung. 69(4): 441–448. doi: 10.1515/hf-2014-0138