This work studied the sliding wear performance of TiAl-based nitride coatings synthesized on austempered ductile iron (ADI) by cathodic arc deposition (CAD) and plasma-based ion implantation and deposition (PBIID). Monolayer CAD TiAlN films and bilayer CAD and PBIID TiAl/TiAlN films deposited on an experimental device were analyzed and benchmarked against a commercial bilayer CAD film. Sliding wear was evaluated in a pin–on–disc tribometer. Two test conditions were employed, one intended to prevent damage (low load, short distance) and another intended to promote damage (higher load, longer distance). Regarding low load tests, all coated samples showed friction coefficients of 0.40–0.45 and negligible wear. Regarding high load tests, all coated variants exhibited lower or equal disc and pin wear rates with respect to uncoated ADI. In addition, coated samples displayed steady-state friction coefficients between 0.2 and 0.6 while uncoated ADI steady-state coefficients between 0.6 and 0.85.
DuY, GaoX, WangX, . Tribological behavior of austempered ductile iron (ADI) obtained at different austempering temperatures. Wear. 2020;456-457:203396. doi:10.1016/j.wear.2020.203396
4.
KrellaA.Resistance of PVD coatings to erosive and wear processes: a review. Coatings. 2020;10(10):921. doi:10.3390/coatings10100921
5.
StewartS, AhmedR.Rolling contact fatigue of surface coatings – a review. Wear. 2002;253(11–12):1132–1144. doi:10.1016/S0043-1648(02)00234-X
6.
AdesinaAY, GasemZM, MohammedAS.Comparative investigation and characterization of the scratch and wear resistance behavior of TiN, CrN, AlTiN and AlCrN cathodic Arc PVD coatings. Arab J Sci Eng. 2019;44(12):10355–10371. doi:10.1007/s13369-019-04038-8
7.
GilewiczA, ChmielewskaP, MurzynskiD, . Corrosion resistance of CrN and CrCN/CrN coatings deposited using cathodic arc evaporation in Ringer's and Hank's solutions. Surf Coat Technol. 2016;299:7–14. doi:10.1016/j.surfcoat.2016.04.069
8.
ShuklaK, RaneR, AlphonsaJ, . Structural, mechanical and corrosion resistance properties of Ti/TiN bilayers deposited by magnetron sputtering on AISI 316L. Surf Coat Technol. 2017;324:167–174. doi:10.1016/j.surfcoat.2017.05.075
9.
AndersA., 2009, Cathodic arcs: from fractal spots to energetic condensation. New York: Springer
10.
PelletierJ, AndersA.Plasma-based Ion implantation and deposition: a review of physics, technology, and applications. IEEE Trans Plasma Sci. 2005;33:1944–1959. doi:10.1109/TPS.2005.860079
11.
FengHP, LeeSC, HsuCH, . Study of high cycle fatigue of PVD surface–modified austempered ductile iron. Mater Chem Phys. 1999;59(2):154–161. doi:10.1016/S0254-0584(99)00035-8
12.
HsuCH, ChenKL, LuKC.Effects of low–temperature duplex coatings on the abrasive and erosive behavior of ADI. Thin Solid Films. 2011;519(15):4855–4859. doi:10.1016/j.tsf.2011.01.041
13.
HsuCH, ChenML, LaiKL.Corrosion resistance of TiN/TiAlN–coated ADI by cathodic arc deposition. Mater Sci Eng A. 2006;421(1-2):182–190. doi:10.1016/j.msea.2005.12.014
14.
HsuCH, LeeCY, ChenKL, . Effects of CrN/EN and Cr2O3/EN duplex coatings on corrosion resistance of ADI. Thin Solid Films. 2009;517(17):5248–5252. doi:10.1016/j.tsf.2009.03.117
15.
HsuCH, LuJK, TsaiRJ.Effects of low–temperature coating process on mechanical behaviors of ADI. Mater Sci Eng A. 2005;398(1-2):282–290. doi:10.1016/j.msea.2005.03.092
16.
HsuC-H, ChenK-L, LeeC-Y, . Effects of low-temperature duplex coatings on corrosion behavior of austempered ductile iron. Surf Coat Technol. 2009;204(6-7):997–1001. doi:10.1016/j.surfcoat.2009.04.002
17.
HsuC-H, ChenK-L, LuJ-H.Effects of electroless nickel interlayer on surface properties of CrN arc-coated austempered ductile iron. Surf Coat Technol. 2008;203(5-7):868–871. doi:10.1016/j.surfcoat.2008.05.031
18.
HsuC-H, HuangK-H, ChenY-T, . The effect of electroless Ni–P interlayer on corrosion behavior of TiN-coated austempered ductile iron. Thin Solid Films. 2013;529:34–38. doi:10.1016/j.tsf.2012.05.050
19.
HsuC-H, LuJ-K, LaiK-L, . Erosion and corrosion behaviors of ADI deposited TiN/TiAlN coatings by cathodic arc evaporation. Mater Trans. 2005;46(6):1417–1424. doi:10.2320/matertrans.46.1417
20.
HsuC-H, LuJ-K, TsaiR-J.Characteristics of duplex surface coatings on austempered ductile iron substrates. Surf Coat Technol. 2006;200(20-21):5725–5732. doi:10.1016/j.surfcoat.2005.08.122
21.
ColomboDA, EcheverríaMD, LainoS, . Sliding wear behavior of PVD CrN and TiN coated austempered ductile iron. ISIJ Int. 2014;54(12):2860–2867. doi:10.2355/isijinternational.54.2860
22.
DasS, GuhaS, GhadaiR, . Structural and mechanical properties of CVD deposited titanium aluminium nitride (TiAlN) thin films. Appl Phys A. 2017;123(6):412. doi:10.1007/s00339-017-1032-0
23.
ÇomaklıO.Improved structural, mechanical, corrosion and tribocorrosion properties of Ti45Nb alloys by TiN, TiAlN monolayers, and TiAlN/TiN multilayer ceramic films. Ceram Int. 2021;47(3):4149–4156. doi:10.1016/j.ceramint.2020.09.292
24.
VettivelSC, JeganR, VigneshJ, . Surface characteristics and wear depth profile of the TiN, TiAlN and AlCrN coated stainless steel in dry sliding wear condition. Surf Interfaces. 2017;6:1–10. doi:10.1016/j.surfin.2016.10.008
25.
SzalaM, WalczakM, PasierbiewiczK, . Cavitation erosion and sliding wear mechanisms of AlTiN and TiAlN films deposited on stainless steel substrate. Coatings. 2019;9(5):340. doi:10.3390/coatings9050340
26.
CaiF, ChenM, LiM, . Influence of negative bias voltage on microstructure and property of Al-Ti-N films deposited by multi-arc ion plating. Ceram Int. 2017;43(4):3774–3783. doi:10.1016/j.ceramint.2016.12.019
27.
KimuraA, KawateM, HasegawaH, . Anisotropic lattice expansion and shrinkage of hexagonal TiAlN and CrAlN films. Surf Coat Technol. 2003;169-170:367–370. doi:10.1016/S0257-8972(03)00040-9
28.
ChenL, PaulitschJ, DuY, . Thermal stability and oxidation resistance of Ti–Al–N coatings. Surf Coat Technol. 2012;206(11):2954–2960. doi:10.1016/j.surfcoat.2011.12.028
29.
PalDeyS, DeeviSC.Single layer and multilayer wear resistant coatings of (Ti,Al)N: a review. Mater Sci Eng A. 2003;342(1–2):58–79. doi:10.1016/S0921-5093(02)00259-9
30.
HenryP, PacMJ, RousselotC, . Wear mechanisms of titanium and aluminium nitride coatings: a microtribological approach. Surf Coat Technol. 2013;223:79–86. doi:10.1016/j.surfcoat.2013.02.033
31.
ColomboDA, MandriAD, EcheverríaMD, . Mechanical and tribological behavior of Ti/TiN and TiAl/TiAlN coated austempered ductile iron. Thin Solid Films. 2018;647:19–25. doi:10.1016/j.tsf.2017.12.014
32.
ColomboDA, MassoneJM, EcheverríaMD, . Rolling contact fatigue behavior of Ti/TiN coated ADI by cathodic arc deposition. Ceram Int. 2017;43(5):4263–4271. doi:10.1016/j.ceramint.2016.12.068
33.
QuintanaJP, MassoneJM, MárquezAB, . Rolling contact fatigue behavior of TiN based coatings deposited on ADI by cathodic arc deposition and plasma based ion implantation and deposition. Thin Solid Films. 2019;671:95–102. doi:10.1016/j.tsf.2018.12.014
34.
ASTM A247-17. Standard test method for evaluating the microstructure of graphite in iron castings. West Conshohocken (PA): ASTM International, 2017.
35.
ASTM A897 / A897M-16. Standard specification for austempered ductile iron castings. West Conshohocken (PA): ASTM International, 2016.
36.
ColomboDA, EcheverríaMD, MoncadaOJ, . PVD tin and CrN coated austempered ductile iron: analysis of processing parameters influence on coating characteristics and substrate microstructure. ISIJ Int. 2012;52(1):121–126. doi:10.2355/isijinternational.52.121
37.
VogliE, TillmannW, Selvadurai-LasslU, . Influence of Ti/TiAlN-multilayer designs on their residual stresses and mechanical properties. Appl Surf Sci. 2011;257(20):8550–8557. doi:10.1016/j.apsusc.2011.05.013
38.
VDI 3198, Coating (CVD, PVD) of cold forging tools. The Association of German Engineers, Düsseldorf, Germany, 1992.
39.
ASTM G99-17. Standard test method for wear testing with a pin-on-disk apparatus. West Conshohocken (PA): ASTM International, 2017.
40.
ArchardJF.Contact and rubbing of flat surfaces. J Appl Phys. 1953;24(8):981–988. doi:10.1063/1.1721448
ColomboDA, EcheverríaMD, LainoS, . Rolling contact fatigue resistance of PVD CrN and TiN coated austempered ductile iron. Wear. 2013;308(1–2):35–45. doi:10.1016/j.wear.2013.09.015
43.
ColomboDA, EcheverríaMD, DommarcoRC, . Influence of TiN coating thickness on the rolling contact fatigue resistance of austempered ductile iron. Wear. 2016;350-351:82–88. doi:10.1016/j.wear.2016.01.009
44.
ZieglerJF.SRIM-2003. Nucl Instrum Methods Phys Res Sect B. 2004;219-220:1027–1036. doi:10.1016/j.nimb.2004.01.208
45.
GrondonaD, KellyH, MinottiFO.Hydrodynamic model for a vacuum arc operated with background gas: theory and experimental validation. J Appl Phys. 2006;99(4):043304. doi:10.1063/1.2168239
46.
MukherjeeS, ProkertF, RichterE, . Comparison of TiN and Ti1−xAlxN coatings deposited on Al using plasma immersion ion implantation assisted deposition. Surf Coat Technol. 2005;200(7):2459–2464. doi:10.1016/j.surfcoat.2004.11.028
47.
HuangH, LiZX, WangMJ, . Microstructural and mechanical properties of TiAlN and Ti3AlN films deposited by reactive magnetron sputtering. Mater Sci Forum. 2015;816:283–288. doi:10.4028/www.scientific.net/MSF.816.283
48.
TsuiTY, PharrGM, OliverWC, . Nanoindentation and nanoscratching of hard carbon coatings for magnetic disks. MRS Proc. 1995;383:447. doi:10.1557/PROC-383-447
49.
OnoT, UemuraM, YatsuzukaM.Adhesion improvement of TiN film on tool steel by a hybrid process of unbalanced magnetron sputtering and plasma-based ion implantation. Nucl Instrum Methods Phys Res Sect B. 2007;257(1):786–789. doi:10.1016/j.nimb.2007.01.088
50.
GerstnerEG, McKenzieDR.Adherent carbon film deposition by cathodic arc with implantation. J Vac Sci Technol A. 1995;13(2):406–411. doi:10.1116/1.579372
51.
DurmazYM, YildizF.The wear performance of carbide tools coated with TiAlSiN, AlCrN and TiAlN ceramic films in intelligent machining process. Ceram Int. 2019;45(3):3839–3848. doi:10.1016/j.ceramint.2018.11.055
52.
ElmkhahH, MahboubiF, Abdollah-zadehA, . A new approach to improve the surface properties of H13 steel for metal forming applications by applying the TiAlN multi-layer coating. J Manuf Process. 2018;32:873–877. doi:10.1016/j.jmapro.2018.04.010
53.
KalinM, JerinaJ.The effect of temperature and sliding distance on coated (CrN, TiAlN) and uncoated nitrided hot-work tool steels against an aluminium alloy. Wear. 2015;330-331:371–379. doi:10.1016/j.wear.2015.01.007
54.
RamadossR, KumarN, PandianR, . Tribological properties and deformation mechanism of TiAlN coating sliding with various counterbodies. Tribol Int. 2013;66:143–149. doi:10.1016/j.triboint.2013.05.001
55.
ShugurovAR, KazachenokMS.Mechanical properties and tribological behavior of magnetron sputtered TiAlN/TiAl multilayer coatings. Surf Coat Technol. 2018;353:254–262. doi:10.1016/j.surfcoat.2018.09.001
56.
TkadletzM, MittererC, SartoryB, . The effect of droplets in arc evaporated TiAlTaN hard coatings on the wear behavior. Surf Coat Technol. 2014;257:95–101. doi:10.1016/j.surfcoat.2014.01.010
57.
MusilJ, JiroutM.Toughness of hard nanostructured ceramic thin films. Surf Coat Technol. 2007;201(9):5148–5152. doi:10.1016/j.surfcoat.2006.07.020
58.
HuangX, EtsionI, ShaoT.Effects of elastic modulus mismatch between coating and substrate on the friction and wear properties of TiN and TiAlN coating systems. Wear. 2015;338-339(Supplement C):54–61. doi:10.1016/j.wear.2015.05.016
59.
HarlinP, BexellU, OlssonM.Influence of surface topography of arc-deposited TiN and sputter-deposited WC/C coatings on the initial material transfer tendency and friction characteristics under dry sliding contact conditions. Surf Coat Technol. 2009;203(13):1748–1755. doi:10.1016/j.surfcoat.2008.12.011
60.
HarlinP, CarlssonP, BexellU, . Influence of surface roughness of PVD coatings on tribological performance in sliding contacts. Surf Coat Technol. 2006;201(7):4253–4259. doi:10.1016/j.surfcoat.2006.08.103
61.
SaketiS, OlssonM.Influence of CVD and PVD coating micro topography on the initial material transfer of 316L stainless steel in sliding contacts – a laboratory study. Wear. 2017;388-389:29–38. doi:10.1016/j.wear.2016.12.003
62.
YoonS-Y, LeeKO, KangSS, . Comparison for mechanical properties between TiN and TiAlN coating layers by AIP technique. J Mater Process Technol. 2002;130-131:260–265. doi:10.1016/S0924-0136(02)00746-X
63.
BowdenFP, TaborD.The friction and lubrication of solids. Oxford: Clarendon Press; 1950.