In this study, the microabrasive wear of a plasma nitrided Inconel 625 superalloy was studied. Nitrogen supersaturation in the expanded FCC layer promoted hardening due to the higher compressive residual stresses. The results showed the formation of a nitrided layer consisting of nitrogen expanded FCC phase (γN) and CrN nitride, respectively. Friction coefficient, mechanical failure mode and critical loads for damaging the nitrided case, using the linear scratch test, were carried out at a linearly increased normal force. The scratch test results showed that the nitrided layer strongly decreased the apparent friction coefficient in comparison with the non-nitrided alloy. Tensile cracking was the prevalent mechanical failure mode of the nitrided layer. Microabrasion results showed that the nitriding layer improving the wear resistance. For the nitrided samples, wear coefficients were determined for the nitrided layer and the substrate, indicating a change in the wear volume loss rate with the test distance.
TschiptschinAP, NishikawaAS, VarelaLB, . Thermal stability of expanded austenite formed on a DC plasma nitrided 316L austenitic stainless steel. Thin Solid Films. 2017;644:156–165. doi:10.1016/j.tsf.2017.06.065.
4.
PinedoCE, TschiptschinAP.Low temperature nitriding, nitrocarburising and carburising of AISI 316L austenitic stainless steel. Int Heat Treat Surf Eng. 2011;5:73–77. doi:10.1179/174951411X13051201040703.
5.
MakishiT, NakataK.Surface hardening of nickel alloys by means of plasma nitriding. Metall Mater Trans A Phys Metall Mater Sci. 2004;35 A:227–238. doi:10.1007/s11661-004-0123-7.
6.
KahramanF, KaradenizS.Characterization and wear behavior of plasma nitrided nickel based dental alloy. Plasma Chem Plasma Process. 2011;31:595–604. doi:10.1007/s11090-011-9301-8.
7.
KovacíH, GhahramanzadehH, AlbayrakÇ, . Effect of plasma nitriding parameters on the wear resistance of alloy Inconel 718. Met Sci Heat Treat. 2016;58:470–474. doi:10.1007/s11041-016-0037-1.
8.
EspallargasN, MischlerS.Dry wear and tribocorrosion mechanisms of pulsed plasma nitrided Ni-Cr alloy. Wear. 2011;270:464–471. doi:10.1016/j.wear.2010.12.008.
9.
CzerwiecT, HeH, SakerA, . Reactive magnetron sputtering as a way to improve the knowledge of metastable f.c.c. nitrogen solid solutions formed during plasma assisted nitriding of Inconel 690. Surf Coatings Technol. 2003;174–175:131–138. doi:10.1016/S0257-8972(03)00529-2.
10.
HeH, CzerwiecT, DongC, . Effect of grain orientation on the nitriding rate of a nickel base alloy studied by electron backscatter diffraction. Surf Coatings Technol. 2003;163–164:331–338. doi:10.1016/S0257-8972(02)00611-4.
11.
FonovićM, LeineweberA, RobachO, . The nature and origin of ‘double expanded austenite’ in Ni-based Ni-Ti alloys developing upon low temperature gaseous nitriding. Metall Mater Trans A Phys Metall Mater Sci. 2015;46:4115–4131. doi:10.1007/s11661-015-2999-9.
12.
AwPK, BatchelorAW, LohNL.Failure mechanisms of plasma nitrided Inconel 718 film. Wear. 1997;208:226–236. doi:10.1016/S0043-1648(96)07298-5.
13.
BorowskiT, BrojanowskaA, KostM, . Modifying the properties of the Inconel 625 nickel alloy by glow discharge assisted nitriding. Vacuum. 2009;83:1489–1493. doi:10.1016/j.vacuum.2009.06.056.
14.
ToroA, TschiptschinAP.Chemical characterization of a high nitrogen stainless steel by optimized electron probe microanalysis. Scr Mater. 2010;63:803–806. doi:10.1016/j.scriptamat.2010.06.021.
15.
AltuhafiF, O'SullivanC, CavarrettaI.Analysis of an image-based method to quantify the size and shape of sand particles. J Geotech Geoenvironmental Eng. 2013;139:1290–1307. doi:10.1061/(ASCE)GT.1943-5606.0000855.
16.
Câmara CozzaR, RodriguesLC, Geraldo SchönC.Analysis of the micro-abrasive wear behavior of an iron aluminide alloy under ambient and high-temperature conditions. Wear. 2015;330–331:250–260. doi:10.1016/J.WEAR.2015.02.021.
17.
UmemuraMT, VarelaLB, PinedoCE, . Assessment of tribological properties of plasma nitrided 410S ferritic-martensitic stainless steels. Wear. 2019;426–427:49–58. doi:10.1016/j.wear.2018.12.092.
18.
Parreiras MarquesF, César BozziA, ScandianC, . Microabrasion of three experimental cobalt-chromium alloys: wear rates and wear mechanisms. Wear. 2017;390–391:176–183. doi:10.1016/j.wear.2017.07.023.
19.
ASTM, ASTM C1624 - 05. Standard test method for adhesion strength and mechanical failure modes of ceramic coatings by quantitative single point scratch testing, 2015. doi:10.1520/C1624-05R15.
20.
S. ASTM G171-03. Standard test method for scratch hardness of materials using a diamond stylus, 2017. doi:10.1520/G0171-03R17.
21.
HutchingsIM. Tribology: friction and wear of engineering materials. London: Arnold; 1992. ISBN 0-340-56184-x. 273 pages.
MindivanF, MindivanH.Comparisons of wear performance of hardened Inconel 600 by different nitriding processes. Procedia Eng.2013: 730–735. Elsevier Ltd. doi:10.1016/j.proeng.2013.12.246.
24.
TrezonaRI, AllsoppDN, HutchingsIM.Transition between two-body and three-body abrasive wear: influence of test conditions in the microscale abrasive wear test. Wear. 1999;225–229:205–214.
25.
AdachiK, HutchingsIM.Wear-mode mapping for the micro-scale abrasion test. Wear. 2003;255:23–29. doi:10.1016/S0043-1648(03)00073-5.
26.
AdachiK, HutchingsIM.Sensitivity of wear rates in the micro-scale abrasion test to test conditions and material hardness. Wear. 2005: 318–321. Elsevier. doi:10.1016/j.wear.2004.02.016.
27.
CozzaRC, SchonCG.Evidence of superposition between grooving abrasion and rolling abrasion. Tribol Trans. 2015;58:875–881. doi:10.1080/10402004.2015.1024907.
28.
OrdoñezMFC, AmorimCLG, KrindgesI, . Microstructure and micro-abrasive wear of sintered yttria-containing 316L stainless steel treated by plasma nitriding. Surf Coatings Technol. 2019;374:700–712. doi:10.1016/j.surfcoat.2019.06.002.
29.
StachowiakGW.Particle angularity and its relationship to abrasive and erosive wear. Wear. 2000;241:214–219. doi:10.1016/S0043-1648(00)00378-1.
30.
BingleyMS, SchneeS.A study of the mechanisms of abrasive wear for ductile metals under wet and dry three-body conditions. Wear. 2005;258:50–61. doi:10.1016/j.wear.2004.01.022.
31.
EspitiaLA, DongH, LiXY, . Scratch test of active screen low temperature plasma nitrided AISI 410 martensitic stainless steel. Wear. 2017;376–377:30–36. doi:10.1016/j.wear.2017.01.091.
32.
EspitiaL, VarelaL, TieppoG, . Microstructure and linear scratch test of low temperature plasma nitrided stainless steels, in: 5th World Tribol Congr. WTC 2013, 2014.