Experimental investigations of mechanical properties and slurry erosion behaviour of high velocity oxy fuel and plasma sprayed Cr 2 O 3 –50%Al 2 O 3 coatings on CA6NM turbine steel under hydro accelerated conditions

Abstract

Slurry erosion behaviour of HVOF (High Velocity Oxy Fuel) and plasma sprayed coatings on CA6NM hydraulic turbine steel has been investigated at different levels of various parameters. The Cr₂O₃–50%Al₂O₃ composite powder was prepared and deposited on CA6NM steel samples to get the uniform thickness coatings. The surface roughness, porosity and microhardness of as-coated samples were measured. The as-coated samples were subjected to SEM/EDS analysis to evaluate the surface microstructure of the developed coatings. Erosion tests were performed on self made erosion test rig under hydro accelerated conditions. The study reveals that the velocity, impact angle and slurry concentration were the most significant parameters, influencing the erosion rate of these coatings. The average particle size had least affect on the erosion rate. HVOF-coated samples showed better corrosion resistance as compared to plasma-coated samples due to high hardness of HVOF-coated CA6NM samples.