Anti-oxidation coatings of MoSi2-SiC-Si-ZrB2 were prepared on the graphite surface by laser cladding. The XRD, scratching bonding force, SEM and isothermal oxidation tests were used to investigate the microstructure and properties of the coatings. The coating with 40 wt% ZrB2 added (MoSi2:SiC:Si:ZrB2 = 16:4:5:16.6) has the lowest degree of oxidation, the best oxidation resistance and the highest bonding strength between coating and matrix. The scratching bonding force still maintained at about 9.9 N after laser ablation, and there were no obvious destructive defects but some pores and cracks on the coating. After a Si-enriched amorphous layer was formed, the relative oxygen permeability was significantly decreased and the oxidation of the coating was passivated, which prevented the matrix from further oxidation.
RenXR, WangWH, ShangTQ, Dynamic oxidation protective ultrahigh temperature ceramic TaB2-20%wt SiC composite coating for carbon material. Compos B Eng. 2019;161:220–227.
2.
WangL, FuQG, ZhaoFL, Constructing self-healing ZrSi2-MoSi2 coating for C/C composites with enhanced oxidation protective ability. Surf Coat Technol. 2018;347:257–269.
3.
ZhenQ, LiZ, HuPF, A glass-ceramic coating with self-healing capability and high infrared emissivity for carbon/carbon composites. Corros Sci. 2018;141:81–87.
4.
YangLW, XiaoXR, LiuLP, Dynamic oxidation mechanism of carbon fiber reinforced SiC matrix composite in high-enthalpy and high-speed plasmas. J Adv Ceram. 2022;11(2):365–377.
5.
ZhouLM, YouQB, XiongJ, Dry wear behaviors of graphite/cermet self-lubricating composite under different sliding conditions and simulation of temperature field. Int J Refract Met Hard Mater. 2018;73:85–90.
HuangJF, LiHJ, XiongXB.Research progress of high temperature anti-oxidation coatings for carbon/carbon composites. New Carbon Mater. 2005;20(4):373–379.
8.
JiangY, LiuTY, RuHQ, Ultra-high-temperature ceramic TaB2-SiC-Si coating by impregnation and in-situ reaction method to prevent graphite materials from oxidation and ablation. Ceram Int. 2019;54:6541–6551.
9.
ZouX, FuQG, LiuL, ZrB2-SiC coating to protect carbon/carbon composites against ablation. Surf Coat Technol. 2013;226:17–21.
10.
YanZQ, XiongX, XiaoP, Oxidation behavior of oxidation protective coatings for C/C-SiC composites at 1500°C. Trans Nonferrous Met Soc China. 2009;19:61–64.
11.
LyuY, DuBH, ChenGQ, Microstructural regulation, oxidation resistance, and mechanical properties of Cf/SiC/SiHfBOC composites prepared by chemical vapor infiltration with precursor infiltration pyrolysis. J Adv Ceram. 2021;11(1):120–135.
12.
FuQ, LiH, WangY, B2o3 modified SiC–MoSi2 oxidation resistant coating for carbon/carbon composites by a two-step pack cementation. Corros Sci. 2009;51(10):2450–2454.
13.
ChuY, FuG Q, CaoC, Microstructure and oxidation resistant property of C/C composites modified by SiC–MoSi2–CrSi2 coating. Surf Eng. 2011;27(5):355–361.
14.
HuangM, LiK, LiH, A Cr–Al–Si oxidation resistant coating for carbon/carbon composites by slurry dipping. Carbon. 2007;45(5):1124–1126.
15.
XiangZD, RoseSR, DattaPK, Codeposition of Al and Si to form oxidation-resistant coatings on γ-TiAl by the pack cementation process. Mater Chem Phys. 2003;80(2):482–489.
16.
NeumanEW, HilmasGE.Mechanical properties of zirconium-diboride based UHTCs. Hoboken: John Wiley & Sons; 2014.
17.
LiuXZ, DengCM, DengCG, Mullite-modified ZrB2-MoSi2 coating for carbon/carbon composites to withstand long term ablation. Ceram Int. 2018;44:4330–4337.
18.
WangDN, ZengY, XiongX, Preparation and ablation properties of ZrB2-SiC protective laminae for carbon/carbon composites. Ceram Int. 2014;40:14215–14222.
19.
YangX, LiW, WangS, Oxidation behavior of oxidation protective coatings for PIP–C/SiC composites at 1500°C. Ceram Int. 2012;38:9–13.
20.
GuoSQ.Oxidation and strength retention of HfB2-SiC composite with La2O3 additives. Adv Appl Ceram. 2020;119(4):218–223.
21.
AstapovAN, PogozhevYS, ProkofievV M, Kinetics and mechanism of high-temperature oxidation of the heterophase ZrSi2-MoSi2-ZrB2 ceramics. Ceram Int. 2019;45(5):6392–6404.
22.
YangGY, PengSW, LiZM, Factors affecting SiC-ZrO2-MoSi2/Ni antioxidation coating made by composite plating on carbon fibres. Adv Appl Ceram. 2019;118(7):387–394.
23.
RenXR, LvJS, LiW, Influence of MoSi2 on oxidation protective ability of TaB2-SiC coating in oxygen-containing environments within a broad temperature range. J Adv Ceram. 2020;9:703–715.