Fully dense WC-Al2O3 platelet composites with VC additive were fabricated by hot-press sintering. Their mechanical properties and microstructure were examined. The contents of Al2O3 platelet (Al2O3pl) and VC were optimised. The fracture toughness of WC-based composites would be obviously improved with Al2O3pl addition. The defined addition of VC was beneficial for the densification and improved mechanical properties of the WC-based composites. The microstructure of the composites was fine, compact and homogeneous compared with the composites without VC addition. The range of fracture toughness of WC-Al2O3pl composites was 9.3–13.5 MPa m1/2. The flexural strength of the composites varied a little and the maximum was 1289 MPa when the content of Al2O3pl was 5 vol.-%, the content of VC was 0.5wt-%.
DeorsolaFA, VallauriD, VillalbaGAO, Densification of ultrafine WC-12Co cermets by pressure assisted fast electric sintering[J]. Int J Refract Met H, 2010;28:254–259.
2.
KimHC, KimDK, WooKD, Consolidation of binderless WC-TiC by high frequency induction heating sintering. Int J Refract Met Hard Mater. 2008;26:48–54.
HuangSG, VanderBiestO, VleugelsJ.Pulsed electric current sintered Fe3Al bonded WC composites. Int J Refract Met Hard Mater. 2009;27:1019–1023.
5.
ZhangML, ZhuSG, MaJ, Preparation of WC/MgO composite nanopowders by high-energy reactive ball milling and their plasma-activated sintering. Powder Metall Met Ceram. 2008;47:525–530.
6.
QuaHX, ZhuSG, LiQ, Microstructure and mechanical properties of hot-pressing sintered WC–xvol.%Al2O3 composites. Mater Sci Eng A. 2012;543:96–103.
7.
QuaHX, ZhuSG, DiP, Microstructure and mechanical properties of WC-40vol%Al2O3 composites hot pressed with MgO and CeO2 additives. Ceram Int. 2013;39(2):1931–1942.
8.
KayaC, KayaF, MarsogluM.Processing, toughness improvement and microstructural analysis of SiC platelet-reinforced Al2O3/Y-TZP nano-ceramic matrix composites. Mater Sci Eng. 1998;247:75–80.
9.
KayaC, KayaF.On the toughening mechanisms of SiC platelet-reinforced Al2O3/Y-TZP nano-ceramic matrix composites. Ceram Int. 1999;25:359–366.
10.
ChoiBJ, KohYH, KimH-Ee.Mechanical properties of Si3N4–SiC three-layer composite materials. J Am Ceram Soc. 1998;81:2725–2728.
11.
YangYP, YangZF, YuanQM.Al2O3 platelet and tetragonal zirconia particle incorporation reinforced mullite matrix ceramics. J Mater Sci Lett. 1996;15:185–186.
12.
ZhouY, VleugelsJ, LaouiT, Toughening of X-Sialon with Al2O3 platelets. J Eur Ceram Soc. 1995;15:297–305.
13.
BernardoE, ScarinciG, HreglichS.Development and mechanical characterization of Al2O3 platelet-reinforced glass matrix composites obtained from glasses coming from dismantled cathode ray tubes. J Eur Ceram Soc. 2005;25:1541–1550.
14.
BoccacciniAR, WinklerV.Fracture surface roughness and toughness of Al2O3-platelet reinforced glass matrix composites. Composites Part A. 2002;33:125–131.
15.
AldoR.Pressureless sintering and characterization of Al2O3-platelet-reinforced barium-magnesium aluminosilicate glass-ceramic composites. Composites Part A. 1997;28:505–510.
16.
FengP, HeYH, XiaoYF, Effect of VC addition on sinterability and microstructure of ultrafine Ti(C, N)-based cermets in spark plasma sintering. J Alloys Compd. 2008;460:453–459.
17.
TaimatsuH, SugiyamaS, KomatsuM.Effects of Cr3C2 and V8C7 on themicrostructure and mechanical properties of WC–SiC whisker ceramics. Mater Trans JIM. 2009;50(10):2435–2440.
18.
MahmoodanM, AliakbarzadehH, GholamipourR.Sintering of WC–10%Co nano powders containing TaC and VC grain growth inhibitors. Trans Nonferrous Metals Soc. 2011;21(5):1080–1084.
19.
TrungTB, WatiHZ, ZainalAA, Grain growth, phase evolution and properties of NbC carbide-doped WC-10AISI304 hardmetals produced by pseudo hot isostatic pressing. J Alloys Compd. 2013;552:20–25.
20.
DongWW, ZhuSG, WangY, Influence of VC and Cr3C2 as grain growth inhibitors on WC-Al2O3 composites prepared by hot press sintering Int. Int J Refract Met Hard Mater. 2014;45:223–229.
21.
LepotN, Van BaelMK, Vanden RulH, Synthesis of platelet-shaped boehmite and g-alumina nanoparticles via an aqueous route. Ceram Int. 2008;34:1971–1974.
22.
ShettyDK, WrightIG, MincerPN, Indentation fracture of WC-Co cermets. J Mater Sci. 1985;20:1873–1882.
23.
ASTM B 312. Standard test method for green strength for compacted metal powder specimens, vol. 02.05. West Conshohocken: ASTM International; 1996.
24.
HuangS, VleugelsJ, LiL, Experimental investigation and thermodynamic assessment of the V–W–C system. Cheminform. 2005;395(1–2):68–74.
HuangSG, VanmeenselK, Vander BiestO, Binderless WC and WC–VC materials obtained by pulsed electric current sintering. Int J Refract Met Hard Mater. 2008;26:41–47.
27.
SunJ, ZhaoJ.Determination of microstructure and mechanical properties of VC/Cr3C2 reinforced functionally graded WC-TiC-Al2O3 micro-nano composite tool materials via two-step sintering. J Alloys Compd. 2017;709(30):197–205.
28.
WangH, WebbT, BitlerJW.Different effects of Cr3C2 and VC on the sintering behavior of WC–Co materials. Int J Refract Met Hard Mater. 2015;53:117–122.