The oxidation and its effect on room temperature flexural strength were examined in hot-pressed 3 vol.-% La2O3-doped HfB2-20 vol.-% SiC composite exposed to air at 1400°C and 1500°C, respectively, for up to 100 h. The major oxidation products consisted of SiO2 (α-cristobalite), La2Si2O7, HfO2 and HfSiO4 regardless of oxidation temperature. However, the morphology of the microstructure of the oxidised surfaces was shown to be dependent on oxidation temperature. In addition, it was found that the room temperature flexural strength of the composite degraded after oxidation and the degradation of strength depended on oxidation time at temperature and oxidation temperature. The strength retention displayed by composite after 100 h of oxidation at 1400°C and 1500°C was ∼83% and ∼74%, respectively.
FahrenholtzWG, HilmasGE, TalmyIG, Refractory diborides of zirconium and hafnium. J Am Ceram Soc. 2007;90:1347–1364. doi: 10.1111/j.1551-2916.2007.01583.x
2.
KalishD, CloughertyEV, KrederK.Strength, fracture mode, and thermal stress resistance of HfB2 and ZrB2. J Am Ceram Soc. 1969;52:30–36. doi: 10.1111/j.1151-2916.1969.tb12655.x
3.
UpadhyaK, YangJM, HoffmannWP.Materials for ultrahigh temperature structural applications. Am Ceram Soc Bull. 1997;76:51–56.
4.
SavinoR, FumoMDS, SilvestroniL, Arc-jet testing on HfB2 and HfC-based ultra-high temperature ceramic materials. J Eur Ceram Soc. 2008;28:1899–1907. doi: 10.1016/j.jeurceramsoc.2007.11.021
5.
Berkowitz-MattuckJB.High temperature oxidation. J Electrochem Soc. 1966;113:908–914. doi: 10.1149/1.2424154
6.
ParthasarathyTA, RappRA, OpekaM, A model for the oxidation of ZrB2, HfB2 and TiB2. Acta Mater. 2007;55:5999–6010. doi: 10.1016/j.actamat.2007.07.027
7.
TrippWC, DavisHH, GrahamHC.Effect of an SiC addition on the oxidation of ZrB2. Am Ceram Soc Bull. 1973;52:612–616.
8.
HinzeJW, TrippWC, GrahamHC.The high temperature oxidation behavior of a HfB2 + 20 v/o SiC composite. J Electrochem Soc. 1975;122:1249–1253. doi: 10.1149/1.2134436
9.
JayaseelanDD, Zapata-SolvasE, BrownP, In situ formation of oxidation resistant refractory coating on SiC-reinforced ZrB2 ultra high temperature ceramics. J Am Ceram Soc. 2012;95:1247–1254. doi: 10.1111/j.1551-2916.2011.05032.x
10.
FahrenholtzWG, HilmasGE.Oxidation of ultra-high temperature transition metal diboride ceramics. Int Mater Rev. 2012;57:61–72. doi: 10.1179/1743280411Y.0000000012
11.
GuoSQ, YangJM, TanakaH, Effect of thermal exposure on strength of ZrB2-based composites with nano-sized SiC particles. Compos Sci Technol. 2008;68:3033–3040. doi: 10.1016/j.compscitech.2008.06.021
ZhuS, FahrenholtzWG, HilmasGE.Influence of silicon carbide particle size on the microstructure and mechanical properties of zirconium diboride-silicon carbide ceramics. J Eur Ceram Soc. 2007;27:2077–2083. doi: 10.1016/j.jeurceramsoc.2006.07.003
14.
GuoSQ.High-temperature mechanical behavior of ZrB2-based composites with micrometer- and nano-sized SiC particles. J Am Ceram Soc. 2018;101:2707–2711. doi: 10.1111/jace.15446
15.
MonteverdeF, BellosiA.Microstructure and properties of an HfB2-SiC composite for ultra-high temperature applications. Adv Eng Mater. 2004;6:331–336. doi: 10.1002/adem.200400016
16.
GuoSQ, LiuTW, PingDH, Enhanced high-temperature strength of HfB2-SiC composite up to 1600°C. J Eur Ceram Soc. 2018;38:1152–1157. doi: 10.1016/j.jeurceramsoc.2017.12.040
17.
PaulA, JayaseelanDD, VenugopalS, UHTS composites for hypersonic applications. Am Ceram Soc Bull. 2012;91:22–29.
18.
WuchinaE, OpilaE, OpekaM, UHTCs: ultra-high temperature ceramic materials for extreme environment applications. Interface. 2007;16:30–36.
19.
SavinoR, FumoMD.Aerothermodynamic study of ultra-high temperature ceramic winglet for atmospheric reentry test. J Thermophys Heat Transf. 2008;22:669–676. doi: 10.2514/1.33296
20.
SquireTH, MarschallJ.Material property requirements for analysis and design of UHTC composites in hypersonic application. J Eur Ceram Soc. 2010;30:2239–2251. doi: 10.1016/j.jeurceramsoc.2010.01.026
21.
Zapata-SolvasE, JayaseelanDD, BrownPM, Effect of La2O3 addition on long-term oxidation kinetics of ZrB2-SiC and HfB2-SiC ultra-high temperature ceramics. J Eur Ceram Soc. 2014;34:3535–3548. doi: 10.1016/j.jeurceramsoc.2014.06.004
22.
GuoSQ, MizuguchiT, IkegamiM, Oxidation behavior of ZrB2-MoSi2-SiC composites in air at 1500°C. Ceram Int. 2011;37:585–591. doi: 10.1016/j.ceramint.2010.09.034
23.
LangeFF, DavisBI, GrahamHC.Compressive creep and oxidation resistance of an Si3N4 material fabricated in the system Si3N4-Si2N2O-Y2Si2O7. J Am Ceram Soc. 1983;66:C98–C99.
24.
MieskowskiDM, SandersWA.Oxidation of silicon nitride sintered with rare-earth oxide additions. J Am Ceram Soc. 1985;68:C160–C163.
25.
BabiniGN, BellosiA, VincenziniP.Factors influencing structural evolution in the oxide of hot-pressed Si3N4-Y2O3-SiO2 materials. J Mater Sci. 1984;19:3487–3497. doi: 10.1007/BF02396923
26.
ChenM, LiH, YaoX, High temperature oxidation resistance of La2O3-modified ZrB2-SiC coating for SiC-coated carbon/carbon composites. J Alloys Compd. 2018;765:37–45. doi: 10.1016/j.jallcom.2018.06.230
27.
GuoSQ.Strength retention in hot-pressed ZrB2-SiC composite after thermal cycling exposure in air at 1200°C and 1400°C. J Am Ceram Soc. 2019;102:3843–3848. doi: 10.1111/jace.16413
28.
ParkH, KimHW, KimHE.Oxidation and strength retention of monolithic Si3N4 and nanocomposite Si3N4-SiC with Yb2O3 as a sintering aid. J Am Ceram Soc. 1998;81:2130–2134. doi: 10.1111/j.1151-2916.1998.tb02596.x