Thermal properties of La 2 Zr 2 O 7 double-layer thermal barrier coatings

Abstract

La₂Zr₂O₇ is a promising thermal barrier coating (TBC) material. In this work, La₂Zr₂O₇ and 8YSZ-layered TBC systems were fabricated. Thermal properties such as thermal conductivity and coefficient of thermal expansion were investigated. Furnace heat treatment and jet engine thermal shock (JETS) tests were also conducted. The thermal conductivities of porous La₂Zr₂O₇ single-layer coatings are 0.50–0.66 W m⁻¹ °C⁻¹ at the temperature range from 100 to 900°C, which are 30–40% lower than the 8YSZ coatings. The coefficients of thermal expansion of La₂Zr₂O₇ coatings are about 9–10 × 10⁻⁶ °C⁻¹ at the temperature range from 200 to 1200°C, which are close to those of 8YSZ at low temperature range and about 10% lower than 8YSZ at high temperature range. Double-layer porous 8YSZ plus La₂Zr₂O₇ coatings show a better performance in thermal cycling experiments. It is likely because porous 8YSZ serves as a buffer layer to release stress.