This paper discussed the influence of duration and modes of heating on structural and physicochemical properties of silver-doped hydroxyapatite (Ag-HAP) nanopowders (NPs). Conventional electric furnace and microwave (MW) heating modes were employed during the synthesis. MW mode of synthesis was relatively an efficient method as it prepared monolithic HAP NP in just one minute of heating. With the increase in duration of heating in both modes of heating; lattice parameters, crystal size, lattice strain, Ca/P ratio, and degree of crystallinity of HAP phase increased. The morphology of particles was rod-shaped having aspect ratio between 2 and 3. EDX confirmed the presence of Ag and corroborated the formation of apatite. The hydrodynamic diameter of Ag-HAP NPs was significantly bigger than the particle sizes calculated using XRD, FESEM, and TEM. Thus, an overall examination concluded MW as an efficient mode of synthesis, able to produce Ag-HAP NPs in a possible minimum time.
SinghRP, SinghM, VermaG, . Structural analysis of silver doped hydroxyapatite nanopowders by Rietveld refinement. Trans Indian Inst Met. 2016;70(8):1973–1980. doi: 10.1007/s12666-016-1019-0
2.
ParkEJ, LeeSW, BangIC., Optimal synthesis and characterization of Ag nanofluids by electrical explosion of wires in liquids. Nanoscale Res Lett. 2011;6(1):223–233. doi: 10.1186/1556-276X-6-223
3.
MirandaM, FernandezA, DiazM., Silver-hydroxyapatite nanocomposites as bactericidal and fungicidal materials. Int J Mater Res. 2010;101(1):122–127. doi: 10.3139/146.110256
4.
CiobanuCS, MassuyeauF, ConstantinLV., Structural and physical properties of antibacterial Ag-doped nano-hydroxyapatite synthesized at 100°C. Nanoscale Res Lett. 2011;6(1):613–620. doi: 10.1186/1556-276X-6-613
5.
MoA, LiaoJ, XuW., Preparation and antibacterial effect of silver-hydroxyapatite/titania nanocomposite thin film on titanium. Appl Surf Sci. 2008;255(2):435–438. doi: 10.1016/j.apsusc.2008.06.083
6.
MelaiyeA, YoungsWJ.Silver and its application as an antimicrobial agent. Expert Opin Ther Pat. 2005;15(2):125–130. doi: 10.1517/13543776.15.2.125
CostescuA, CiobanuCS, IconaruSL., Fabrication, characterization, and antimicrobial activity, evaluation of low silver concentrations in silver-doped hydroxyapatite nanoparticles. J Nanomater. 2013;5:1–9. doi: 10.1155/2013/194854
9.
PopaCL, CiobanuCS, VoicuG., Influence of thermal treatment on the antimicrobial activity of silver-doped biological apatite. Nanoscale Res Lett. 2015;10(1):502–512. doi: 10.1186/s11671-015-1211-x
10.
ChungRJ, HsiehMF, HuangKC., Anti-microbial hydroxyapatite particles synthesized by a sol-gel route. J Sol-Gel Sci Technol. 2005;33(2):229–239. doi: 10.1007/s10971-005-5618-1
11.
SinghB, DubeyAK, KumarS., In vitro biocompatibility and antimicrobial activity of wet chemically prepared Ca10-xAgx(PO4)6(OH)2 (0.0≤x≤0.5) hydroxyapatites. Mater Sci Eng, C. 2011;31(7):1320–1329. doi: 10.1016/j.msec.2011.04.015
12.
IqbalN, KadirMRA, MalekNANN., Rapid microwave assisted synthesis and characterization of nanosized silver-doped hydroxyapatite with antibacterial properties. Mater Lett. 2012;89:118–122. doi: 10.1016/j.matlet.2012.08.057
13.
IqbalN, KadirMRA, MalekNANN., Characterization and antibacterial properties of stable silver substituted hydroxyapatite nanoparticles synthesized through surfactant assisted microwave process. Mater Res Bull. 2013;48(9):3172–3177. doi: 10.1016/j.materresbull.2013.04.068
14.
IqbalN, KadirMRA, MahmoodNH., Characterization, antibacterial and in vitro compatibility of zinc-silver doped hydroxyapatite nanoparticles prepared through microwave synthesis. Ceram Int. 2014;40(3):4507–4513. doi: 10.1016/j.ceramint.2013.08.125
15.
RameshbabuN, Sampath KumarTS, PrabhakarTG., Antibacterial nanosized silver substituted hydroxyapatite: synthesis and characterization. J Biomed Mater Res. 2007;80A(3):581–591. doi: 10.1002/jbm.a.30958
16.
PangYX, BaoX.Influence of temperature, ripening time and calcination on the morphology and crystallinity of hydroxyapatite nanoparticles. J Eur Ceram Soc. 2003;23(10):1697–1704. doi: 10.1016/S0955-2219(02)00413-2
17.
KothapalliCR, WeiM, LegerosRZ., Influence of temperature and aging time on HA synthesized by the hydrothermal method. J Mater Sci-Mater Med. 2005;16(5):441–446. doi: 10.1007/s10856-005-6984-5
18.
CiobanuCS, IconaruSL, ChiriucC., Synthesis and antimicrobial activity of silver-doped hydroxyapatite nanopowders. BioMed Res Int. 2013;10.
19.
LimPN, ChangL, ThianES.Development of nanosized silver-substituted apatite for biomedical applications: a review. Nanomed Nanotechnol. 2005;11:1331–1344. doi: 10.1016/j.nano.2015.03.016
20.
MaMG, ZhuYJ, ChangJ.Monetite formed in mixed solvents of water and ethylene glycol and its transformation to hydroxyapatite. J Phys Chem B. 2006;110(29):14226–14230. doi: 10.1021/jp061738r
21.
Da SilvaMP, LimaJHC, SoaresGA., Transformation of monetite to hydroxyapatite in bioactive coatings on titanium. Surf Coat Technol. 2001;137(2):270–276. doi: 10.1016/S0257-8972(00)01125-7
22.
WuE, KisiEH, GrayEMA.Modelling dislocation-induced anisotropic line broadening in Rietveld refinements using a Voigt function. II. Application to neutron powder diffraction data. J Appl Crystallogr. 1998;31(3):363–368. doi: 10.1107/S0021889897012181