The enhancement of wear resistance by laser carburisation on TiZrN coatings was investigated in terms of bond state. Graphite paste was used to cover the TiZrN coatings and then pulsed laser ablation was used to solidify the carbon. Tribometer test showed that the friction coefficient was reduced from 0.64 to 0.17 after laser carburisation. The doped carbon was analysed as a mixture with sp2C and sp3C bonds using an X-ray photoelectron spectroscopy depth profile. The sp2/sp3 ratio was 2.29 at the surface and increased up to 2.91 in the depth direction. To verify the effect of the hybrid bonds on the atomic order, annealing was carried out to the carburised specimens. As the ratio increased to 3.28, graphitisation resulting in transition from sp3 to sp2 was confirmed, and variation in the lattice structure was demonstrated by a reduction in the lattice constant (4.45 Å to 4.40 Å) using Rietveld refinement.
BoelensS, VeltropH.Hard coatings of TiN, (TiHf) N and (TiNb) N deposited by random and steered arc evaporation. Surf Coat Tech. 1987;33:63–71. doi: 10.1016/0257-8972(87)90177-0
2.
HuangHH, HeJL, HonMH.Microstructure and mechanical properties of surface layer obtained by plasma nitriding and/or TiN coating on high speed steel. Surf Coat Tech. 1994;64(1):41–46. doi: 10.1016/S0257-8972(09)90084-6
3.
WangY, NorthwoodDO.An investigation into TiN-coated 316L stainless steel as a bipolar plate material for PEM fuel cells. J Power Sourc. 2007;165(1):293–298. doi: 10.1016/j.jpowsour.2006.12.034
4.
DonohueLA, SmithIJ, MünzWD, . Microstructure and oxidation-resistance of Ti1− x− y− zAlxCryYzN layers grown by combined steered-arc/unbalanced-magnetron-sputter deposition. Surf Coat Tech. 1997;94–95:226–231. doi: 10.1016/S0257-8972(97)00249-1
5.
TakaokaH, NakamuraE, OshikaT, . Relationship between an affinity of (Ti1−x, Alx)N layer toward iron and its cutting performance. Surf Coat Tech. 2004;177–178:306–311. doi: 10.1016/j.surfcoat.2003.09.009
KnotekO, LöfflerF, KrämerG.Performance behaviour of physical-vapour-deposition-coated cermets in interrupted-cut machining. Surf Coat Tech. 1993;62(1–3):669–673. doi: 10.1016/0257-8972(93)90316-G
8.
YanP, DengJ, WuZ, . Friction and wear behavior of the PVD (Zr,Ti)N coated cemented carbide against 40Cr hardened steel. Int J Refract Met H. 2012;35:213–220. doi: 10.1016/j.ijrmhm.2012.06.003
9.
AbadiasG, GuerinP.In situ stress evolution during magnetron sputtering of transition metal nitride thin films. Appl Phys Lett. 2008;93(11):111908. doi: 10.1063/1.2985814
10.
AbadiasG, KoutsokerasLE, SioziosA, . Stress, phase stability and oxidation resistance of ternary Ti–Me–N (Me=Zr, Ta) hard coatings. Thin Solid Films. 2013;538:56–70. doi: 10.1016/j.tsf.2012.10.119
11.
MarcinauskasL, ČernauskasM, MilieškaM, . The effect of hydrogen addition in argon-acetylene plasma on the structure of amorphous carbon films. J Non-Cryst Solids. 2017;466–467:1–7. doi: 10.1016/j.jnoncrysol.2017.03.021
12.
ZhouS, LiuL, MaL.Study on structure, mechanical and tribological properties of iron incorporated diamond-like carbon films. J Non-Cryst Solids. 2017;455:35–41. doi: 10.1016/j.jnoncrysol.2016.10.018
13.
BhushanB.Chemical, mechanical and tribological characterization of ultra-thin and hard amorphous carbon coatings as thin as 3.5 nm: recent developments. Diam Relat Mater. 1999;8(11):1985–2015. doi: 10.1016/S0925-9635(99)00158-2
14.
RobertsonJ.Diamond-like amorphous carbon. Mat Sci Eng R. 2002;37(4):129–281. doi: 10.1016/S0927-796X(02)00005-0
RybachukM, BellJM.The effect of sp2 fraction and bonding disorder on micro-mechanical and electronic properties of a-C: H films. Thin Solid Films. 2007;515(20):7855–7860. doi: 10.1016/j.tsf.2007.04.040
TianBM, YuanZH, HuiW.Formation and coalescence of linear chains in growth of nanostructured sp-sp2 amorphous carbon films. Chem Phys Lett. 2008;462(1):104–108.
BarshiliaHC, PrakashMS, RaoDVS, . Superhard nanocomposite coatings of TiN/a-C prepared by reactive DC magnetron sputtering. Surf Coat Tech. 2005;195(2):147–153. doi: 10.1016/j.surfcoat.2004.09.035
22.
ZhengXH, TuJP, GuB, . Preparation and tribological behavior of TiN/a-C composite films deposited by DC magnetron sputtering. Wear. 2008;265(1):261–265. doi: 10.1016/j.wear.2007.10.007
23.
SediraS, AchourS, AvciA, . Physical deposition of carbon doped titanium nitride film by DC magnetron sputtering for metallic implant coating use. Appl Surf Sci. 2014;295:81–85. doi: 10.1016/j.apsusc.2014.01.010
24.
NakamuraI, SasakiM, TakanoI, . Mechanical properties of carbon-doped TIN films by ion beam irradiation in ethylene gas atmosphere. Surf Coat Tech. 2005;196(1):104–107. doi: 10.1016/j.surfcoat.2004.08.113
ChenS, WangJ, WangH.Synthesis, characterization and pyrolysis of a high zirconium content zirconocene–polycarbosilane precursor without Zr–O bond. Mater Design. 2016;90:84–90. doi: 10.1016/j.matdes.2015.10.019
27.
YoshidaM, TanakaT, WatanabeS, . Improvement of oxygen barrier of PET film with diamond-like carbon film by plasma-source ion implantation. Surf Coat Tech. 2003;174–175:1033–1037. doi: 10.1016/S0257-8972(03)00714-X
28.
ChiuMC, HsiehWP, HoWY, . Thermal stability of Cr-doped diamond-like carbon films synthesized by cathodic arc evaporation. Thin Solid Films. 2005;476(2):258–263. doi: 10.1016/j.tsf.2004.09.029
29.
D'annaE, DeGML, LuchesA, . Study of C-N binding states in carbon nitride films deposited by reactive XeCl laser ablation. Thin Solid Films. 1999;347(1):72–77. doi: 10.1016/S0040-6090(98)01734-9
30.
Ech-ChamikhE, EssaftiA, ljdiyaouY, . XPS study of amorphous carbon nitride (a-C: N) thin films deposited by reactive RF sputtering. Sol Energ Mat Sol C. 2006;90(10):1420–1423. doi: 10.1016/j.solmat.2005.10.007
TsuchitaniS, KanekoR, HironoS.Annealing-induced modification of superhard conductive carbon film. Jpn J Appl Phys. 2006;45(9A):7036–7043. doi: 10.1143/JJAP.45.7036
33.
DíazJ, PaolicelliG, FerrerS, . Separation of the sp3 and sp2 components in the C1s photoemission spectra of amorphous carbon films. Phy Rev B. 1996;54(11):8064–8069. doi: 10.1103/PhysRevB.54.8064
34.
ReyS, AntoniF, PrevotB, . Thermal stability of amorphous carbon films deposited by pulsed laser ablation. Appl Phys A-Mat. 2000;71(4):433–439. doi: 10.1007/s003390000618