The Nd:YAG transparent ceramics with addition of Lu3+ ions were fabricated by co-precipitation method and vacuum sintering. Pure YAG phases were obtained when Lu3+ ion content was kept under 4.5 at.-%. Lattice constant of polycrystalline ceramic with 0.8 at.-% Lu3+ calculated from XRD patterns was similar to that of YAG single crystal, and its fluorescent intensity arising from 4F3/2 → 4I9/2 transition of Nd3+ ions reached the maximum although the ceramic was opaque. The results indicated that Lu3+ ions under 1.5 at.-% relieved strains from lattice distortion and enhanced the fluorescent intensity.
LupeiV., LupeiA. and UrsuI.: ‘The heating effects and concentration quenching of Nd:YAG’, Proc. SPIE, 1996, 4, 108–116. doi: 10.1117/12.238088
2.
KuwanoY., SudaK., IshizawaN. and YamadaT.: ‘Crystal growth and properties of (Lu, Y)3Al5O12’, J. Cryst. Growth, 2004, 260, 159–165. doi: 10.1016/j.jcrysgro.2003.08.060
3.
KestigianM. and HollowayW. W.Jr: ‘Incorporation of increased concentrations of rare earth activator ions in optical quality single crystals of yttrium aluminum garnet’, J. Cryst. Growth, 1968, 3–4, 455–457. doi: 10.1016/0022-0248(68)90199-1
4.
LiG. S., WuJ. H., GuoX. B., LvJ. and YangH.: ‘Study on the growth and characteristics of “volume compensation” doped LuαNdβYAlO3 crystals’, J. Chin. Ceram. Soc., 1990, 18, (2), 142–148(in Chinese).
5.
IkesueA., KinoshitaT., KamataK. and YoshidaK.: ‘Fabrication and optical-properties of high-performance polycrystalline Nd-YAG ceramics for Solid-State lasers’, J. Am. Ceram. Soc., 1995, 78, 1033–1040. doi: 10.1111/j.1151-2916.1995.tb08433.x
6.
CaponettiE., EnzoS., LasioB. and SaladinoM. L.: ‘Co-precipitation synthesis of neodymium-doped yttrium aluminium oxides nanopowders: quantitative phase investigation as a function of joint isothermal treatment conditions and neodymium content’, Opt. Mater., 2007, 29, 1240–1243. doi: 10.1016/j.optmat.2005.11.037
7.
WangD. Y. and GuoY. Y.: ‘A comparative study of the energy migration and energy transfer in highly doped Nd:YAG single crystal’, Phys. B: Condens. Matter., 2009, 404, 55–57. doi: 10.1016/j.physb.2008.10.018
8.
KatsurayamaM., AnzaiY., SugiyamaA., KoikeM. and KatoY.: ‘Growth of neodymium doped Y3Al5O12 single crystals by double crucible method’, J. Cryst. Growth, 2001, 229, 193–198. doi: 10.1016/S0022-0248(01)01119-8
9.
P. Jiao: ‘Preparation of Y2O2S: Lu3+ blue photoluminescent’, New Chem. Mater., 2014, 42, 65–67(in Chinese).
10.
BonnetL., BoulesteixR., MaîtreA., SalléC. and CoudercV.: ‘Manufacturing issues and optical properties of rare-earth (Y, Lu, Sc, Nd) aluminate garnets composite transparent ceramics’, Opt. Mater., 2015, 50, 2–10. doi: 10.1016/j.optmat.2015.04.050
11.
WagnerN., HerdenB., DierkesT., PlewaJ. and JüstelT.: ‘Towards the preparation of transparent LuAG:Nd3+ ceramics’, J. Eur. Ceram. Soc., 2012, 32, 3085–3089. doi: 10.1016/j.jeurceramsoc.2012.03.015
12.
ZhangW., LuT. C., WeiN., MaB. Y., LiF., LuZ. W. and QiJ. Q.: ‘Effect of annealing on the optical properties of Nd:YAG transparent ceramics’, Opt. Mater., 2012, 34, 685–690. doi: 10.1016/j.optmat.2011.10.001
13.
YangP. Z., DengP. Z. and YinZ. W.: ‘Concentration quenching in Yb:YAG’, J. Lumin., 2002, 97, 51–54. doi: 10.1016/S0022-2313(01)00426-4
14.
StrozykJ. W.: ‘Lutetium effects on Uv absorption spectra of Nd:YAG’, IEEE J. Quantum Elect., 1971, Qe7, 467–469. doi: 10.1109/JQE.1971.1076836
15.
LiuW., XieZ. and ChengL.: ‘Sintering kinetics window: an approach to the densification process during the preparation of transparent alumina’, Adv. Appl. Ceram., 2015, 114, 33–38. doi: 10.1179/1743676114Y.0000000186
16.
NankoM. and DangK. Q.: ‘Two-step pulsed electric current sintering of transparent Al2O3 ceramics’, Adv. Appl. Ceram., 2014, 113, 80–84. doi: 10.1179/1743676113Y.0000000109