A preceramic polymer for ZrC was successfully synthesised by chemical reaction between zirconium oxychloride (ZrOCl2·8H2O) and 2-Hydroxybenzyl alcohol via a one-pot route. The molecular structure, thermal properties and pyrolysis behaviour of the precursor were investigated. The results indicated that the precursor might be Zr–O–Zr chain polymer with 2-Hydroxybenzyl alcohol as ligand. The precursor was air-stable and exhibited excellent solubility in common organic solvents. The conversions from precursor to ZrC powders were investigated by TG-DTA, X-ray diffraction, Scanning electron microscope, TEM and Raman spectrum. The precursor underwent a thermal decomposition in four steps, and ZrC powders were formed at 1300°C via carbothermal reduction reaction of ZrO2 and carbon in argon with ceramic yield of 63.0%. The ZrC particles were fine and exhibited irregular polyhedron morphology with average size in the range of 100–300 nm.
LiZ. Q., LiH. J., ZhangS. Y. and LiK. Z.: ‘Microstructure and ablation behaviors of integer felt reinforced C/C–SiC–ZrC composites prepared by a two-step method’, Ceram. Int., 2012, 38, 3419–3425. doi: 10.1016/j.ceramint.2011.12.054
2.
LiZ. Q., LiH. J., ZhangS. Y., LW. and WJ.: ‘Microstructures and ablation properties of C/C−SiC−ZrC composites prepared using C/C skeletons with various densities’, Ceram. Int., 2013, 39, 8173–8181. doi: 10.1016/j.ceramint.2013.03.093
3.
JayaseelanD. D., de SáR. G., BrownP. and LeeW. E.: ‘Reactive infiltration processing (RIP) of ultra high temperature ceramics (UHTC) into porous C/C composite tubes’, J. Europ. Ceram. Soc., 2011, 31, 361–368. doi: 10.1016/j.jeurceramsoc.2010.10.013
4.
LiF., HuangX. and ZhangG. J.: ‘Scalable foaming assisted synthesis of ZrC nanopowder by carbothermal reduction’, Ceram. Int., 2015, 41, 3335–3338. doi: 10.1016/j.ceramint.2014.10.170
5.
RyuH. Y., NersisyanH. H. and LeeJ. H.: ‘Preparation of zirconium-based ceramic and composite fine-grained powders’, Int. J. Refract. Met. Hard. Mater., 2012, 30, 133–138. doi: 10.1016/j.ijrmhm.2011.07.015
6.
ChengG. W.: ‘An inorganic-organic hybrid precursor strategy for the synthesis of zirconium diboride powders’, Int. J. Refract. Met. Hard. Mater., 2013, 36, 149–153. doi: 10.1016/j.ijrmhm.2012.08.008
7.
WuH. T., ZhangW. G. and ZhangJ. H.: ‘Pyrolysis synthesis and microstructure of zirconium carbide from new preceramic polymers’, Ceram. Int., 2014, 40, 5967–5972. doi: 10.1016/j.ceramint.2013.11.044
8.
ZhaoJ., ZhouJ., ManZ.-Y., WangX.-G., XueJ.-X. and ZhangG.-J.: ‘Dopant effects on high temperature mechanical properties of zirconium carbide ceramics’, Adv. Appl. Ceram., 2015, 114, (6), 338–343. doi: 10.1179/1743676115Y.0000000001
9.
HarrisonR. W. and LeeW. E.: ‘Processing and properties of ZrC, ZrN and ZrCN ceramics: a review’, Adv. Appl. Ceram., 2015, doi:10.1179/1743676115Y.0000000061.
10.
TaoX. Y., WeiX. Y., ChenQ., LuW. Z. and ZhaoT.: ‘Synthesis, characterization and thermal behavior of new preceramic polymers for ZrC’, Adv. Appl. Ceram., 2013, 112, 302–305. doi: 10.1179/1743676113Y.0000000076
11.
ZhaoD., HuH. F. and ZhangC. R.: ‘A simple way to prepare precursors for zirconium carbide’, J. Mater. Sci., 2010, 45, 6401–6405. doi: 10.1007/s10853-010-4722-y
12.
DongZ. J., ZhangX. and HuangQ.: ‘Synthesis and pyrolysis behavior of a soluble polymer precursor for ultra-fine zirconium carbide powders’, Ceram. Int., 2015, 41, 7359–7365. doi: 10.1016/j.ceramint.2015.02.039
13.
YanC. L., LiuR. J., CaoY. B. and ZhangC. R.: ‘Synthesis of zirconium carbide powders using chitosan as carbon source’, Ceram. Int., 2013, 39, 3409–3412. doi: 10.1016/j.ceramint.2012.09.032
14.
LiuC. Q., LiK. Z. and LiH. J.: ‘Synthesis, characterization and ceramization of a carbon-rich zirconium-containing precursor for ZrC ceramic’, Ceram. Int., 2014, 40, 7285–7292. doi: 10.1016/j.ceramint.2013.12.069
15.
DolléM., GossetD., BogicevicC., KarolakF., SimeoneD. and BaldinozziG.: ‘Synthesis of nanosized zirconium carbide by a sol–gel route’, J. Eur. Ceram. Soc., 2007, 27, (4), 2061–2067. doi: 10.1016/j.jeurceramsoc.2006.06.005
16.
LiuH. Y., LiuG. S., PeiS. G., ChenY. and LiuJ. Q.: ‘Preparation of zirconia fibers cotton by centrifugal spinning of polyacetylacetonatozirconium spinning solution’, Bull. Chin. Ceram. Soc., 2011, 6, 1410–1414.
17.
CaoS. W., XieZ. F., WangJ. and WangH.: ‘Synthesis and characterization of polyzirconocarbosilane precursor’, Acta. polym. Sin., 2008, 6, 621–625. doi: 10.3724/SP.J.1105.2008.00621
18.
LiuC.-X., ChenJ.-X., SuZ.-A., YangX., CaoL.-X. and HuangQ.-Z.: ‘Pyrolysis mechanism of ZrC precursor and fabrication of C/C-ZrC composites by precursor infiltration and pyrolysis’, Trans. Nonferrous Met. Soc. China, 2014, 24, 1779–1784. doi: 10.1016/S1003-6326(14)63253-2
19.
XieJ. J., FuZ. Y., WangY. C., LeeS. W. and NiiharaK.: ‘Synthesis of nanosized zirconium carbide powders by a combinational method of sol-gel and pulse current heating’, J. Europ. Ceram. Soc., 2014, 34, (13), e1–13.e7.
20.
ZhouG. H., WangS. W., GuoJ. K. and ZhangZ.: ‘The preparation and mechanical properties of the unidirectional carbon fiber reinforced zirconia composite’, J. Eur. Ceram. Soc., 2008, 28, (4), 787–792. doi: 10.1016/j.jeurceramsoc.2007.07.005
21.
WonY. S., VaranasiV. G., KrylioukO., AndersonT. J., WhiteL. M. and PerezR. J.: ‘Equilibrium analysis of zirconium carbide growth’, J. Cryst. Growth, 2007, 307, 302–308. doi: 10.1016/j.jcrysgro.2007.05.039
22.
YanY. J., HuangZ. R., LiuX. J. and JiangD. L.: ‘carbothermal synthesis of ultra-fine zirconium carbide powders using inorganic precursors via sol-gel method’, J. Sol-Gel Sci. Technol., 2007, 44, 81–85. doi: 10.1007/s10971-007-1595-x
23.
SacksM. D., WangC. A., YangZ. H. and JainA. H.: ‘Carbothermal reduction synthesis of nanocrystalline zirconium carbide and hafnium carbide powders using solution-derived precursors’, J. Mater. Sci., 2004, 39, 6057–6062. doi: 10.1023/B:JMSC.0000041702.76858.a7
24.
TaoX. Y., LiH., HuJ. D., QiuW. F. and ZhaoT.: ‘One pot synthesis of a soluble polymer for zirconium carbide’, Chin. Chem. Lett., 2010, 21, (5), 620–623. doi: 10.1016/j.cclet.2010.01.002
25.
StormsE. K.: ‘The refractory carbides. Refractory materials’, Vol. 2; 1967, New York, Academic.
26.
SarkarS. K., MillerA. D. and MuellerJ. I.: ‘Solubility of oxygen in ZrC’, J. Am. Ceram. Soc., 1972, 55, 628–630. doi: 10.1111/j.1151-2916.1972.tb13457.x
27.
AtchisonJ. S., ZeigerM., TolosaA., FunkeL. M., JäckelN. and PresserV.: ‘Electrospinning of ultrafine metal oxide/carbon and metal carbide/carbon nanocomposite fibers’, RSC. Adv., 2015, 5, 35683–35692. doi: 10.1039/C5RA05409E
28.
FitzerE. and RozplochF.: ‘Laser Raman spectroscopy for determination of the C–C bonding length in carbon’, Carbon, 1988, 26, 594–595. doi: 10.1016/0008-6223(88)90162-5
29.
YoshidaM., TanabeT., OhnoN., YoshimiM. and TakamuraS.: ‘High temperature irradiation damage of carbon materials studies by laser Raman spectroscopy’, J. Nucl. Mater., 2009, 386–388, 841–843. doi: 10.1016/j.jnucmat.2008.12.256
30.
TuinstraF. and KoenigJ. L.: ‘Raman spectrum of graphite’, J. Chem. Phys., 1970, 53, 1126–1130. doi: 10.1063/1.1674108
31.
FerrariA. C. and RobertsonJ.: ‘Interpretation of Raman spectra of disordered and amorphous carbon’, Phys. Rev. B, 2000, 61, 14095–14107. doi: 10.1103/PhysRevB.61.14095
32.
FerrariA. C. and RobertsonJ.: ‘Raman spectroscopy of amorphous, nanostructured, diamond-like carbon and nanodiamond’, Philos. Trans. R. Soc. A, 2004, 362, 2477–2512. doi: 10.1098/rsta.2004.1452
33.
BergerL. M., GrunerW., LangholfE. and StolleS.: ‘On the mechanism of carbothermal reduction processes of TiO2 and ZrO2’, Int. J. Refract. Metals Hard Mater., 1999, 17, 235–243. doi: 10.1016/S0263-4368(98)00077-8
34.
DavidJ., TrolliardG., GendreM. and MaitreA.: ‘TEM study of the reaction mechanisms involved in the carbothermal reduction of zirconia’, J. Eur. Ceram. Soc., 2013, 33, 165–179. doi: 10.1016/j.jeurceramsoc.2012.07.024