In this study, the mechanical and biocorrosion behavior of as-cast Zn-xCu-0.1Sr (x = 1, 2, and 3wt%) alloys for potential application was studied. The microstructure, mechanical properties, and in vitro degradation of Zn-xCu-0.1Sr alloys were investigated. The results show that as Cu content increased from 1.0 to 3.0wt%, the number of CuZn5 phases increased and the average grain size of CuZn5 phases increased from 6.96 μm to 10.92 μm. The 2wt% addition of Cu resulted in the best mechanical properties with 129.4 MPa in ultimate tensile strength and 108.4 MPa in yield strength. Furthermore, the higher corrosion rate was experienced in the alloys with higher Cu content after immersion. Zn-xCu-0.1Sr alloys all presented appropriate in vitro degradation rates in a basically uniform degradation mode. The strength, ductility and biocorrosion property exhibited by the Zn-2Cu-0.1Sr alloy compositions make it a promising candidate for cardiovascular stent applications.
RatnerBDHoffmanASSchoenFJ. Biomaterials science: an introduction to materials in medicine[M]. 3rd ed. Buddy D R: Academic Press; 2013. p. 315-320.
2.
TobisJMAbudayyehI.New devices and technology in interventional cardiology[J]. J Cardiol. 2015; 65 (1): 5–16.
3.
WitteFFischerJNellesenJ. In vivo corrosion and corrosion protection of magnesium alloy LAE442[J]. Acta Biomater. 2010; 6 (5): 1792–1799.
4.
GuX-NZhengY-F.A review on magnesium alloys as biodegradable materials[J]. Front Mater Sci Chin. 2010; 4 (2): 111–115.
5.
LiZGuXLouS. The development of binary Mg–Ca alloys for use as biodegradable materials within bone[J]. Biomaterials. 2008; 29 (10): 1329–1344.
6.
WitteFHortNVogtC. Degradable biomaterials based on magnesium corrosion[J]. Curr Opinion Solid State Mater Sci. 2008; 12 (5): 63–72.
7.
ZhenZXiTZhengY. In vitro study on Mg–Sn–Mn alloy as biodegradable metals[J]. J Mater Sci Technol. 2014; 30 (7): 675–685.
8.
SchinhammerMHänziACLöfflerJF. Design strategy for biodegradable Fe-based alloys for medical applications[J]. Acta Biomater. 2010; 6 (5): 1705–1713.
9.
HermawanHPurnamaADubeD. Fe–Mn alloys for metallic biodegradable stents: degradation and cell viability studies[J]. Acta Biomater. 2010; 6 (5): 1852–1860.
10.
LiuBZhengY.Effects of alloying elements (Mn, Co, Al, W, Sn, B, C and S) on biodegradability and in vitro biocompatibility of pure iron[J]. Acta Biomater. 2011; 7 (3): 1407–1420.
11.
TapieroHTewKD.Trace elements in human physiology and pathology: zinc and metallothioneins[J]. Biomed Pharmacother. 2003; 57 (9): 399–411.
12.
ZhouCLiHFYinYX. Long-term in vivo study of biodegradable Zn-Cu stent: a 2-year implantation evaluation in porcine coronary artery[J]. Acta Biomater. 2019; 97: 657–670.
13.
YangHWangCLiuC. Evolution of the degradation mechanism of pure zinc stent in the one-year study of rabbit abdominal aorta model[J]. Biomaterials. 2017; 145: 92–105.
14.
YangHJiaBZhangZ. Alloying design of biodegradable zinc as promising bone implants for load-bearing applications[J]. Nat Commun. 2020; 11 (1): 401.
15.
XiaoCWangLRenY. Indirectly extruded biodegradable Zn-0.05wt-%Mg alloy with improved strength and ductility: in vitro and in vivo studies[J]. JMaterSciTechnol. 2018; 34 (9): 1618–1627.
DambattaMIzmanSKurniawanD. Influence of thermal treatment on microstructure, mechanical and degradation properties of Zn–3Mg alloy as potential biodegradable implant material[J]. Mater Des. 2015; 85: 431–437.
18.
LiHFXieXHZhengYF. Development of biodegradable Zn-1X binary alloys with nutrient alloying elements Mg, Ca and Sr[J]. Sci Rep. 2015; 5: 10719.
19.
LiHYangHZhengY. Design and characterizations of novel biodegradable ternary Zn-based alloys with IIA nutrient alloying elements Mg, Ca and Sr[J]. Mater Des. 2015; 83: 95–102.
20.
BakerHOkamotoH.ASM handbook, alloy phase diagrams, Vol. 3. Materials Park (OH 44073-0002): ASM International; 1992. p. 501.
21.
TangZNiuJHuaH. Potential biodegradable Zn-Cu binary alloys developed for cardiovascular implant application[J]. J Mech Behav Biomed Mater. 2017; 72: 182.
22.
WangCYangHTLiX. In Vitro evaluation of the feasibility of commercial Zn alloys as biodegradable metals[J]. J Mater Sci Technol. 2016; 32 (9): 909–918.
23.
LiuXSunJQiuK. Effects of alloying elements (Ca and Sr) on microstructure, mechanical property and invitro, corrosion behavior of biodegradable Zn-1.5Mg alloy[J]. J Alloys Compd. 2016; 162: 242–245.
24.
MassalskiTBMurrayJLBennettLH. Binary alloy phase diagrams[M]. Metals Park (OH): American Society for Metals; 1986.
25.
AlanemeKKEdwin-EzehaJC.Mechanical characteristics and biocorrosion behaviour of AS-CAST Zn-3Cu-Al alloys for cardiovascular bioabsorbable devices[J]. Mater Today: Proc. 2022; 62: S49–S56.
26.
YueRHuangHKeG. Microstructure, mechanical properties and in vitro degradation behavior of novel Zn-Cu-Fe alloys[J]. Mater Charact. 2017; 134: 114–122.
27.
HuangSChenLJiangB. Early electrochemical characteristics and corrosion behaviors of pure zinc in simulated body fluid[J]. J Electroanal Chem. 2021; 886: 115–145.
28.
GuessoumKVeys-RenauxDRoccaE. Corrosion behaviour of zinc–cerium alloys: role of intermetallic phases [J]. Corros Sci. 2011; 53: 1639–1645.
29.
SongYWHanEHShanDY. The effect of Zn concentration on the corrosion behavior of Mg−xZn alloys [J]. Corros Sci. 2012; 65: 322–330.
30.
WangYQKongGChenCS.Corrosion behavior of Zn−Al alloys in saturated Ca(OH)2 solution [J]. Corros Sci. 2016; 112: 679–686.