Electrochemical analysis of silane incorporated sodium dodecylbenzene sulphonate: Zinc sulphate pre-treatment on mild steel and its effect on epoxy coating performance
Restricted accessResearch articleFirst published online May, 2022
Electrochemical analysis of silane incorporated sodium dodecylbenzene sulphonate: Zinc sulphate pre-treatment on mild steel and its effect on epoxy coating performance
Variation of surface chemical energy and its effects on adhesion strength and corrosion protection properties of epoxy coatings of mild steel substrates were studied. Results indicated that pre-treatment with a mixture of 3-glycidoxypropyltrimethoxysilane, sodium dodecylbenzene sulphonates and zinc sulphate inhibitors enhanced the corrosion protection properties of epoxy coating when compared to untreated substrates. The formation of a compact insoluble layer of zinc hydroxide/oxide together with SDBS complex on the mild steel surface was found to affect the adhesion properties and resistance towards cathodic/anodic delamination of epoxy coating. This was primarily caused by the formation of strong interfacial interaction and increased in surface passivation. The findings suggested, adhesion alone plays a little part in preventing underfilm corrosion. The underfilm corrosion activities are determined by surface passivity towards corrosion reactions.
FunkeW.Corrosion tests for organic coatings. A review of their usefulness and limitations. J Oil Colour Chem Assoc. 1979; 62 (2): 63–67.
2.
LeidheiserHFunkeW.Water disbondment and wet adhesion of organic coatings on metals: a review and interpretation. J Oil Colour Chem Assoc. 1987; 70 (5): 121–132.
3.
PalanivelVHuangYVan OoijWJ.Effects of addition of corrosion inhibitors to silane films on the performance of AA2024-T3 in a 0.5 M NaCl solution. Prog Org Coat. 2005; 53 (2): 153–168.
4.
KinsellaEMayneJ.Ionic conduction in polymer films I. Influence of electrolyte on resistance. Br Polym J. 1969; 1 (4): 173–176.
5.
NguyenT.Unified model for the degradation of organic coatings on steel in a neutral electrolyte. J Coat Tech. 1996; 68: 45–56.
6.
HarunMKMarshJLyonSB.The effect of surface modification on the cathodic disbondment rate of epoxy and alkyd coatings. Prog Org Coat. 2005; 54 (4): 317–321.
7.
LiuMMHuHXZhengYG. Effect of sol-gel sealing treatment loaded with different cerium salts on the corrosion resistance of Fe-based amorphous coating. Surf Coat Technol. 2019; 367: 311–326.
8.
IzadiMShahrabiTRamezanzadehB.Active corrosion protection performance of an epoxy coating applied on the mild steel modified with an eco-friendly sol-gel film impregnated with green corrosion inhibitor loaded nanocontainers. Appl Surf Sci. 2018; 440: 491–505.
9.
NikpourSNaderiRMahdavainM.Synergistic effect of Mentha longifolia and zinc cations in silane primer coating to improve protection properties of the subsequent epoxy coating. Prog Org Coat. 2019; 127: 55–69.
10.
MarshJScantleburyJLyonS.The effect of surface/primer treatments on the performance of alkyd coated steel. Corros Sci. 2001; 43 (5): 829–852.
11.
MahidashtiZShahrabiTRamezanzadehB.The role of post-treatment of an ecofriendly cerium nanostructure conversion coating by green corrosion inhibitor on the adhesion and corrosion protection properties of the epoxy coating. Prog Org Coat. 2018; 114: 19–32.
12.
RamezanzadehBRaeisiEMahdavianM.Studying various mixtures of 3-aminopropyltriethoxysilane (APS) and tetraethylorthosilicate (TEOS) silanes on the corrosion resistance of mild steel and adhesion properties of epoxy coating. Int J Adhes Adhes. 2015; 63: 166–176.
13.
YuanXYueZFChenX. The protective and adhesion properties of silicone-epoxy hybrid coatings on 2024 Al-alloy with a silane film as pretreatment. Corros Sci. 2016; 104: 84–97.
14.
ParhizkarNRamezanzadehBShahrabiT.Corrosion protection and adhesion properties of the epoxy coating applied on the steel substrate pre-treated by a sol-gel based silane coating filled with amino and isocyanate silane functionalized graphene oxide nanosheets. Appl Surf Sci. 2018; 439: 45–59.
15.
ChenCDongSHouR. Insight into the anti-corrosion performance of electrodeposited silane/nano-CeO2 film on carbon steel. Surf Coat Technol. 2017; 326: 183–191.
ChaudhariSPatilPP.Inhibition of steel corrosion by electrosynthesized poly(o-anisidine)-dodecylbenzenesulfonate coatings. Electrochim Acta. 2010; 55 (22): 6715–6723.
18.
LiuJWangDGaoL. Synergism between cerium nitrate and sodium dodecylbenzenesulfonate on corrosion of AA5052 aluminium alloy in 3 wt.% NaCl solution. Appl Surf Sci. 2016; 389: 369–377.
19.
IsmailIHarunMKYahyaMZA.Corrosion protection of mild steel by the synergetic effect of sodium dodecylbenzenesulfonates and zinc sulfate in sodium chloride solution. Int J Electrochem Sci. 2019; 14: 11491–11508.
20.
D4541. Standard test method for pull-off strength of coatings using portable adhesion testers. West Conshohocken (PA): ASTM International; 2017.
21.
G8-96. Standard test methods for cathodic disbonding of pipeline coatings. West Conshohocken (PA): ASTM International; 2019.
22.
D3358. Standard test methods for rating adhesion by tape test. West Conshohocken (PA): ASTM International; 2017.
23.
AlinejadSNaderiRMahdavianM.Effect of inhibition synergism of zinc chloride and 2-mercaptobenzoxzole on protective performance of an ecofriendly silane coating on mild steel. J Ind Eng Chem. 2017; 48: 88–98.
24.
NaderiRArmanSFouladvandS.Investigation on the inhibition synergism of new generations of phosphate-based anticorrosion pigments. Dyes Pigm. 2014; 105: 23–33.
25.
LandoulsiJGenetMJFleithS. Organic adlayer on inorganic materials: XPS analysis selectivity to cope with adventitious contamination. Appl Surf Sci. 2016; 383: 71–83.
26.
LeeJ-COhS-JChoM. Chemical structure of the interface in ultrathin HfO 2/Si films. Appl Phys Lett. 2004; 84 (8): 1305–1307.
27.
LiDNeumannA.A reformulation of the equation of state for interfacial tensions. J Colloid Interface Sci. 1990; 137 (1): 304–307.
Murillo-GutierrezNVAnsartFBoninoJP. Architectural optimization of an epoxy-based hybrid sol–gel coating for the corrosion protection of a cast Elektron21 magnesium alloy. Appl Surf Sci. 2014; 309: 62–73.
31.
IsmailIHarunMKYahyaMZA.Effects of dissolved oxygen on the integrity of industrial chlorinated rubber-based primer used in rubber/metal composites. Rubber Chem Technol. 2015; 88 (3): 502–514.
32.
QianBHouBZhengM.The inhibition effect of tannic acid on mild steel corrosion in seawater wet/dry cyclic conditions. Corros Sci. 2013; 72: 1–9.
33.
DeflorianFRossiSFedelM. Electrochemical investigation of high-performance silane sol–gel films containing clay nanoparticles. Prog Org Coat. 2010; 69 (2): 158–166.
34.
TaheriMNaderiRSaremiM. Development of an ecofriendly silane sol-gel coating with zinc acetylacetonate corrosion inhibitor for active protection of mild steel in sodium chloride solution. J Solgel Sci Technol. 2017; 81 (1): 154–166.
35.
MontemorMFFerreiraMGS.Cerium salt activated nanoparticles as fillers for silane films: evaluation of the corrosion inhibition performance on galvanised steel substrates. Electrochim Acta. 2007; 52 (24): 6976–6987.
ParhizkarNRamezanzadehBShahrabiT.The epoxy coating interfacial adhesion and corrosion protection properties enhancement through deposition of cerium oxide nanofilm modified by graphene oxide. J Ind Eng Chem. 2018; 64: 402–419.
38.
IsmailIHarunMK.Cathodic disbonding of industrial chlorinated rubber-based primer used in rubber/metal composites: an electrochemical impedance spectroscopy analysis. Rubber Chem Technol. 2016; 89 (4): 712–723.
39.
FunkeW.The role of adhesion in corrosion protection by organic coatings. J Oil Colour Chem Assoc. 1985; 68 (9): 229–232.
40.
ZhengSLiJ.Inorganic–organic sol gel hybrid coatings for corrosion protection of metals. J Solgel Sci Technol. 2010; 54 (2): 174–187.
41.
HarunMKLyonSBMarshJ.A surface analytical study of functionalised mild steel for adhesion promotion of organic coatings. Prog Org Coat. 2003; 46: 21–27.
42.
SanaeiZBahlakehGRamezanzadehB.Active corrosion protection of mild steel by an epoxy ester coating reinforced with hybrid organic/inorganic green inhibitive pigment. J Alloys Compd. 2017; 728: 1289–1304.
43.
SalehiENaderiRRamezanzadehB.Synthesis and characterization of an effective organic/inorganic hybrid green corrosion inhibitive complex based on zinc acetate/Urtica dioica. Appl Surf Sci. 2017; 396: 1499–1514.
44.
IsmailI.HarunM.K.YahyaM.Z.A.The inhibition mechanism of surfactant composite for mild steel corrosion in NaCl solution. ASM Sci J. 2021; 14.
45.
SabataAVan OoijWJKochR.The interphase in painted metals pretreated by functional silanes. J Adhes Sci Technol. 1993; 7 (11): 1153–1170.
46.
LyonSBBinghamRMillsDJ.Advances in corrosion protection by organic coatings: what we know and what we would like to know. Prog Org Coat. 2017; 102: 2–7.
47.
MalasABharatiAVerkinderenO. Effect of the GO reduction method on the dielectric properties, electrical conductivity and crystalline behavior of PEO/rGO nanocomposites. Polymers (Basel). 2017; 9 (11): 613.