The stress corrosion cracking (SCC) mechanism is investigated in high Si duplex stainless steel in a simulated PWR environment based on TEM analysis of FIB-extracted SCC crack tips. The microstructural investigation in the near vicinity of SCC crack tips illustrates a strain-rate dependence in SCC mechanisms. Detailed analysis of the crack tip morphology, that includes crack tip oxidation and surrounding deformation field, indicates the existence of an interplay between corrosion- and deformation-driven failure as a function of the strain rate. Slow strain-rate crack tips exhibit a narrow cleavage failure which can be linked to the film-induced failure mechanism, while rounded shaped crack tips for faster strain rates could be related to the strain-induced failure. As a result, two nominal strain-rate-dependent failure regimes dominated either by corrosion or deformation-driven cracking mechanisms can be distinguished.
AndresenPL.Emerging issues and fundamental processes in environmental cracking in hot water (reprinted from Proceedings of the CORROSION/2007 research topical symposium “Advances in environmentally assisted cracking”, 2007). Corrosion. 2008; 64 (5): 439–464.
2.
Lozano-PerezSDohrJMeisnarM. SCC in PWRs: learning from a bottom-Up approach. Metall Mater Trans E. 2014; 1 (2): 194–210.
3.
AriokaKYamadaTMiyamotoT. Intergranular stress corrosion cracking growth behavior of Ni-Cr-Fe alloys in pressurized water reactor primary water. Corrosion. 2014; 70 (7): 695–707.
4.
TerachiTYamadaTMiyamotoT. SCC growth behaviors of austenitic stainless steels in simulated PWR primary water. J Nucl Mater. 2012; 426 (1-3): 59–70.
5.
LiuXHwangWParkJ. Toward the multiscale nature of stress corrosion cracking. Nucl Eng Technol. 2018; 50 (1): 1–17.
ScottPM.Stress corrosion cracking in Pressurized Water Reactors - Interpretation, modeling and remedies. Corrosion. 2000; 56: 771–782.
8.
WasGSAndresenPL.Stress corrosion cracking behavior of alloys in aggressive nuclear reactor core environments. Corrosion. 2007; 63 (1): 19–45.
9.
ChopraOKRaoAS.A review of irradiation effects on LWR core internal materials – IASCC susceptibility and crack growth rates of austenitic stainless steels. J Nucl Mater. 2011; 409 (3): 235–256.
10.
BruemmerSMSimonenEPScottPM. Radiation-induced material changes and susceptibility to intergranular failure of light-water-reactor core internals. J Nucl Mater. 1999; 274 (3): 299–314.
BoschRWVankeerberghenMGérardR. Crack initiation testing of thimble tube material under PWR conditions to determine a stress threshold for IASCC. J Nucl Mater. 2015; 461: 112–121.
13.
BoschRWRitterSHerbstM. Stress corrosion crack initiation testing with tapered specimens in high-temperature water – results of a collaborative research project. Corros Eng Sci Technol. 2020; 0 (0): 1–16.
14.
BaiJRitterSSeifertHP. Using tapered specimens to study the effect of hydrogen and surface finish on SCC initiation in alloy 182 under boiling water reactor conditions. Corros Eng Sci Technol. 2017; 52 (8): 558–566.
15.
BaiJRitterSSeifertHP. The use of tapered specimens to evaluate the SCC initiation susceptibility in alloy 182 in BWR and PWR environments. In: JacksonJHParaventiDWrightM, eds. The minerals, metals & materials series. Proceedings of the 18th international conference on environmental degradation of materials in nuclear power systems – water reactors2018. p. 1929–1948. https://doi.org/10.1007/978-3-030-04639-2_131
16.
SinghRNLala MikinRDeyGK. Influence of temperature on threshold stress for reorientation of hydrides and residual stress variation across thickness of Zr-2.5Nb alloy pressure tube. J Nucl Mater. 2006; 359 (3): 208–219.
17.
YuJXueLJZhaoZJ. Determination of stress corrosion crack initiation stress and crack velocities using slowly strained tapered specimens. Fatigue Fract Eng Mater Struct. 1989; 12 (6): 481–493.
18.
KilianRBergerSBoschR. D16.4.2 Draft NUGENIA Proposal for optimized surface conditions to mitigate in-service degradation (NUGENIA Position Paper), pp. 1-31, 2016.
19.
PendersAKonstantinovićMJBoschR. Crack initiation in tapered high si stainless steel specimens – stress threshold analyses.Corros Eng Sci Technol. 2020; 55 (8): 721–728.
20.
KilianRDevrientB. Experimental data on crack initiation, fp6 project perfect deliverable c35c. Tech. Rep., VTT, SCK CEN, EdF, Uni Manchester, NAMRC, Wood, Framatome, CVR, 2008.
21.
de CurieresI.Corrosion in PWR stainless steel components: a TSO perspective based on operating experience and expertises. Proceedings of Fontevraud. 2014; 8: 14–18. September 2014, SFEN.
22.
Lozano-PerezS.A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atomprobe analysis. Micron. 2008; 39 (3): 320–328.
23.
IshitaniTUmemuraKOhnishiT. Improvements in performance of focused ion beam cross-sectioning: aspects of ion-sample interaction. J Electron Microsc (Tokyo). 2004; 53 (5): 443–449.
24.
LoeberTHLaegelBWolffS. Reducing curtaining effects in FIB/SEM applications by a goniometer stage and an image processing method. J Vac Sci Technol B Nanotechnol Microelectron: Mater, Process, Meas Phenom. 2017; 35 (6): 06GK01.
25.
SieradzkiKNewmanRCNewmanRC.Brittle behavior of ductile metals during stress-corrosion cracking.Philoso Mag A Phys Condens Matter Struct Defects Mech Prop. 1985; 51 (1): 95–132.
26.
NewmanRCSieradzkiK.Film-induced cleavage during stress-corrosion cracking of ductile metals and alloys. In: LatanisionRMJonesRH, editors. Chemistry and physics of fracture. NATO ASI Series (Series E: Applied sciences). Dordrecht: Springer; 1987. p. 130.
27.
RickerREFinkJLEscalanteE.Evidence of film-induced cleavage by electrodeposited Rh. Corros Deform Interact. 1993: 733–740.
28.
Lozano-PerezSKruskaKIyengarI. The role of cold work and applied stress on surface oxidation of 304 stainless steel. Corros Sci. 2012; 56: 78–85.
29.
KruskaKLozano-PerezSSaxeyDW. 3D atom-probe characterization of stress and cold-work in stress corrosion cracking of 304 stainless steel. 15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors 2011; 2011, vol. 2, pp. 891–898.
30.
KruskaKLozano-perezSSaxeyDW. Nanoscale characterisation of grain boundary oxidation in cold-worked stainless steels. Corros Sci. 2012; 63: 225–233.
31.
LenazDSkogbyHPrincivalleF. Structural changes and valence states in the MgCr2O4FeCr2O4 solid solution series. Phys Chem Miner. 2004; 31 (9): 633–642.
32.
MichalskeTAFreimanSW.A molecular mechanism for stress corrosion in vitreous silica. J Am Ceram Soc. 1983; 66: 284–288.
33.
SubramanyamKN.Neutron and X-ray diffraction studies of certain doped nickel ferrites. J Phys C Solid State Phys. 1971; 4: 2266–2268.
34.
RamachandranDEgoavilRCrabbeA. TEM and AES investigations of the natural surface nano-oxide layer of an AISI 316L stainless steel microfibre. J Microsc. 2016; 264: 207–214.
35.
FordFPAndresenPL.Corrosion in nuclear systems: environmentally assisted cracking in light water reactors. In: MarcusP, editor. Corrosion mechanisms in theory and practice. New York: CRC Press; 2002. p. 605–642. ISBN:9780429221668.
36.
ScottPMLe CalvarM.Proceedings of the Sixth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems. Water reactors; 1993, pp. 657–665.
RickerREFinkJEscalanteE.Evidence of film-induced cleavage by electrodeposited Rh. Corros Deformations Interact. 1993;(January 1993): 733–740.
39.
NewmanRCCordermanRRSieradzkiK.Evidence for dealloying of austenitic stainless steels in simulated stress corrosion crack environments. Br Corros J. 1989; 24: 143–148.
40.
BuehlerMJGaoH.Dynamical fracture instabilities due to local hyperelasticity at crack tips. Nature. 2006; 439 (January): 307–310.
41.
BuehlerMJAbrahamFFGaoH.Hyperelasticity governs dynamic fracture at a critical length scale. Nature. 2003; 426 (6963): 141–146. doi: 10.1038/nature02096. PMID: 14614496.
42.
KaramanISehitogluHChumlyakovY. The deformation of low-stacking-fault-energy austenitic steels. JOM. July 2002; 54: 31–37.
43.
IdrissiHRenardKSchryversD. On the relationship between the twin internal structure and the work-hardening rate of TWIP steels. Scr Mater. 2010; 63 (10): 961–964.
44.
ButzA.ZaparaM.ErhartA.CroizetD.StenN.HagstromJ.HelmD.SchneiderM.KampczykM.HaufeA.BiasuttiM.GmbhD.AbS. K.MannesmannS.GmbhF., and GmbhF. A., Plenary sessions deformation behavior of twip-steels: from experiments to constitutive modelling and simulations. June, p. 38-48, 2014.