The present study compares corrosion behaviour of three austenitic stainless steels 316L, 317L and 904L (base materials and welds) in wet-process phosphoric acid (WPA) and reagent grade phosphoric acid with impurities, e.g., Cl-, F- and SO42-. The corrosion study was done by performing electrochemical polarisations at 50°C followed by Tafel extrapolation. Welds always had higher corrosion rates than their respective base materials. The corrosion rates of stainless steels in plant WPA were much less compared to that in reagent grade phosphoric acid with almost similar levels of Cl−, F− and . This is due to the presence of a variety of dissolved metallic ions in WPA that reduces its corrosiveness. Among the three metallic cations (Fe3+, Mg2+ and Al3+) examined in this study, the inhibiting action increased in the order Fe3+ < Mg2+ < Al3+. SS 904L was the most corrosion-resistant alloy in WPA followed by SS 317L and 316L.
Escriva-CerdanCBlasco-TamaritEGarcia-GarciaDM. Temperature effect on the austenitic stainless steel UNS N08031 used in the wet method phosphoric acid production. Chem Eng Trans. 2013; 32: 1717–1722.
5.
Corrosion Handbook. Corrosive agents and their interaction with materials vol. 3: hypochlorites, phosphoric acid. 2nd ed. In: KreysaGSchutzeM, editors. Wiley-VCH Verlag GmbH & Co. KGaA, Frankfurt.
6.
HondaMKobayashiY.Stainless steels for wet process phosphoric acid. Mater Perf. 1994; 33: 66–69.
7.
SydbergerTNordinS.Corrosivity of wet process phosphoric acid. Corrosion. 1978; 34 (1): 16–22.
ChandraKMahantiAKainV. Failure cases related to material issues in wet-process phosphoric acid plant. Eng Fail Anal. 2017; 79: 642–655.
10.
SchorrMValdezBZlatevR. Agitator corrosion in wet phosphoric acid production. Mater Perf. 2007;46: 50–53.
11.
SchorrMValdezBZlatevR. Erosion-corrosion in phosphoric acid production. Mater Perf. 2010; 56: 56–59.
12.
AimingFJinmingLZiyunT.Failure analysis of the impeller of a slurry pump subjected to corrosive wear. Wear. 1995; 181-183: 876–882.
13.
EbrahimHASalamehMAHamedH.The effect of motion on the behaviour of corrosion of stainless steels in industrial phosphoric acid. Sci Rep. 2012; 1: 453. doi: 10.4172/scientificreports.453
14.
AlonAYahalomJSchorrM.Influence of halides in phosphoric acid on the corrosion behavior of stainless steels. Corrosion. 1975; 31: 315–319.
15.
Ibanez-FerrandizMBlasco-TamaritEGarcia-GarciaDM. Effect of temperature on the corrosion resistance of stainless steels in polluted phosphoric acid. ECS Trans. 2009; 25(37): 49–61.
16.
Blasco-TamaritEGarcia-GarciaDMIbanez FerrandizM. Corrosion resistance and galvanic coupling of UNS N08031 base metal, heat-affected zone and weld metal in phosphoric acid at different temperatures. Corrosion. 2011; 67: 035001-1–035001-10.
17.
ASTM International. A262-15, Standard practices for detecting susceptibility to intergranular attack in austenitic stainless steels. West Conshohocken (PA): ASTM International; 2015.
18.
BarracoPChiaroGBarberaA.Influence of impurities on stainless steels corrosion in wet process phosphoric acid. Fertilizer Res. 1990; 26: 281–289.
19.
ASTM International. G1-03(2017)e1, Standard practice for preparing, cleaning, and evaluating corrosion test specimens. West Conshohocken (PA): ASTM International; 2017.
20.
StansburyEEBuchananRA.Fundamentals of electrochemical corrosion. Materials Park (OH): ASM International; 2000. p. 248–251.
21.
GhoshS.RamgopalT.Effect of chloride and phosphoric acid on the corrosion of alloy C-276, UNS N08028, and UNS N08367. Corros.2005; 61:609–619.
22.
TzanevaBRLoukaychevaMHFachikovLB. Effect of chloride ions on corrosion behaviour of austenitic nickel and nickel free stainless steels in phosphoric acid solutions. Corros Eng Sci Techn. 2015; 50: 568–578.
23.
SeastromCC.Passivity of chromium and stainless steel in hydrofluoric acid. Corros. 1964; 20: 179t–183t.
24.
ZouGShiWXiangS. Corrosion behaviour of 904L austenitic stainless steel in hydrofluoric acid. RSC Adv. 2018; 8: 2811–2817.
25.
KappesMA.Localized corrosion and stress corrosion cracking of stainless steels in halides other than chlorides solutions: a review. Corros Rev. 2020; 38: 1–24.
26.
BernhardssonS.Corrosion performance of a high-nickel alloy. Mater Des. 1989; 10: 186–196.
27.
IdrissiH.Corrosion behaviour of two stainless steels and a chromium cast iron in phosphoric acid contaminated with S2− ions. J Mater Sci. 1996; 31: 4599–4602.
28.
Sanchez-TovarRMontanesMTGarcia-AntonJ. Influence of temperature and hydrodynamic conditions on the corrosion behaviour of AISI 316L stainless steel in pure and polluted H3PO4: application of the response surface methodology. Mater Chem Phys. 2012; 133: 289–298.
29.
BenSalahMSabotRTrikiE. Passivity of Sanicro28 (UNS N-08028) stainless steel in polluted phosphoric acid at different temperatures studied by electrochemical impedance spectroscopy and Mott–Schottky analysis. Corros Sci. 2014; 86: 61–70.
30.
BoudaliaMGuenbourABellaouchouA. Corrosion behaviour of a highly alloyed austenitic alloy UB6 in contaminated phosphoric acid. Int J Corros.2013: 1–9. Article ID 363826.
31.
LiHJiangZFengH. Effect of temperature on the corrosion behaviour of super austenitic stainless steel S32654 in polluted phosphoric acid. Int J Electrochem Sci. 2015; 10: 4832–4848.
. This is due to the presence of a variety of dissolved metallic ions in WPA that reduces its corrosiveness. Among the three metallic cations (Fe3+, Mg2+ and Al3+) examined in this study, the inhibiting action increased in the order Fe3+ < Mg2+ < Al3+. SS 904L was the most corrosion-resistant alloy in WPA followed by SS 317L and 316L.