The corrosion behavior of 2205 duplex stainless steel (2205 DSS) was investigated by atomization tests, which was performed in an S-bearing thin electrolyte layer used as the artificial industrial-marine environment. Electrochemical methods and X-ray photoelectron spectroscopy (XPS), were conducted to reveal the protection properties and the composition evolution of the passive film. The results indicated that the corrosion time would weak the protectiveness of passive film, which was attributed to the accumulation of defects and metal sulfides in the passive film. The decrease of composition percentage of Cr2O3 made more negative effects on the protection properties of passive film than the increase of Cr(OH)3 and CrO3, whose formation was related to the adequate supply of oxygen and water molecules. The metal sulfides such as NiS and MoS2 formed during atomization tests reduced the content of alloy oxides in the passive film, and provided locations for the growth of defects.
WuWLiuZHuS. Effect of pH and hydrogen on the stress corrosion cracking behavior of duplex stainless steel in marine atmosphere environment. Ocean Eng. 2017; 146: 311–323. doi: 10.1016/j.oceaneng.2017.10.002
2.
HouYZhaoJChengC. The metastable pitting corrosion of 2205 duplex stainless steel under bending deformation. J Alloys Compd. 2020; 830: 154422. doi: 10.1016/j.jallcom.2020.154422
3.
KongDNiXDongC. Bio-functional and anti-corrosive 3D printing 316L stainless steel fabricated by selective laser melting. Mater Des. 2018; 152: 88–101. doi: 10.1016/j.matdes.2018.04.058
4.
ConradiMSchönPMKocijanA. Surface analysis of localized corrosion of austenitic 316L and duplex 2205 stainless steels in simulated body solutions. Mater Chem Phys. 2011; 130: 708–713. doi: 10.1016/j.matchemphys.2011.07.049
5.
JinlongLZhuqingWTongxiangL. Enhancing the corrosion resistance of the 2205 duplex stainless steel bipolar plates in PEMFCs environment by surface enriched molybdenum. Results Phys. 2017; 7: 3459–3464. doi: 10.1016/j.rinp.2017.09.001
6.
KongDDongCNiX. Mechanical properties and corrosion behavior of selective laser melted 316L stainless steel after different heat treatment processes. J Mater Sci Technol. 2019; 35: 1499–1507. doi: 10.1016/j.jmst.2019.03.003
7.
KongDDongCNiX. Insight into the mechanism of alloying elements (Sn, Be) effect on copper corrosion during long-term degradation in harsh marine environment. Appl Surf Sci. 2018; 455: 543–553. doi: 10.1016/j.apsusc.2018.06.029
8.
WuWLiuZLiX. Influence of different heat-affected zone microstructures on the stress corrosion behavior and mechanism of high-strength low-alloy steel in a sulfurated marine atmosphere. Mater Sci Eng A. 2019; 759: 124–141. doi: 10.1016/j.msea.2019.05.024
9.
TangJHuYHanZ. Experimental and theoretical, study on the synergistic inhibition effect of pyridine derivatives and sulfur-containing compounds on the corrosion of carbon steel in CO2-Saturated 3.5 wt.% NaCl solution. Molecules. 2018; 23: 3270. doi: 10.3390/molecules23123270
10.
LvJGuoWLiangT.The effect of pre-deformation on corrosion resistance of the passive film formed on 2205 duplex stainless steel. J Alloy Compd. 2016; 686: 176–183. doi: 10.1016/j.jallcom.2016.06.003
11.
WengL.Corrosion behavior of weathering steel with high-content titanium exposed to simulated marine environment. Int J Electrochem Sci. 2018; 13: 5888–5903. doi: 10.20964/2018.06.61
12.
YangYYanBLiJ. The effect of large heat input on the microstructure and corrosion behaviour of simulated heat affected zone in 2205 duplex stainless steel. Corros Sci. 2011; 53: 3756–3763. doi: 10.1016/j.corsci.2011.07.022
13.
ÖrnekCEngelbergDL.SKPFM measured Volta potential correlated with strain localisation in microstructure to understand corrosion susceptibility of cold-rolled grade 2205 duplex stainless steel. Corros Sci. 2015; 99: 164–171. doi: 10.1016/j.corsci.2015.06.035
14.
JinlongLJinHTongxiangL.The effect of electrochemical nitridation on the corrosion resistance of the passive films formed on the 2205 duplex stainless steel. Mater Lett. 2019; 256: 126640. doi: 10.1016/j.matlet.2019.126640
15.
HerbslebGPoepperlingRK.Corrosion properties of austenitic-ferritic duplex steel AF 22 in chloride and sulfide containing environments. Corrosion. 1980; 36: 611–618. doi: 10.5006/0010-9312-36.11.611
16.
ChengXWangYLiX. Interaction between austein-ferrite phases on passive performance of 2205 duplex stainless steel. J Mater Sci Technol. 2018; 34: 2140–2148. doi: 10.1016/j.jmst.2018.02.020
17.
JinSLiuCMLinX. Effect of inorganic anions on the corrosion behavior of UNS S32750 duplex stainless steel in chloride solution. Mater Corros. 2015; 66 (10): 1077–1083. doi: 10.1002/maco.201408185
18.
TangJYangXWangY. Corrosion behavior of 2205 duplex stainless steels in HCl solution containing Sulfide. Metal. 2019; 9: 294. doi: 10.3390/met9030294
19.
HuangBSYinWFSangDH. Applied surface science synergy effect of naphthenic acid corrosion and sulfur corrosion in crude oil distillation unit. Appl Surf Sci. 2012; 259: 664–670. doi: 10.1016/j.apsusc.2012.07.094
20.
García-RenteríaMALópez-MorelosVHGarcía-HernándezR. Improvement of localised corrosion resistance of AISI 2205 duplex stainless steel joints made by gas metal arc welding under electromagnetic interaction of low intensity. Appl Surf Sci. 2014; 321: 252–260. doi: 10.1016/j.apsusc.2014.10.024
21.
TianHChengXWangY. Effect of Mo on interaction between α/γ phases of duplex stainless steel. Electrochim Acta. 2018; 267: 255–268. doi: 10.1016/j.electacta.2018.02.082
22.
KongDNiXDongC. Heat treatment effect on the microstructure and corrosion behavior of 316L stainless steel fabricated by selective laser melting for proton exchange membrane fuel cells. Electrochim Acta. 2018; 276: 293–303. doi: 10.1016/j.electacta.2018.04.188
23.
WangLXingYLiuZ. Erosion–corrosion behavior of 2205 duplex stainless steel in wet gas environments. J Nat Gas Sci Eng. 2016; 35: 928–934. doi: 10.1016/j.jngse.2016.09.029
24.
KongDNiXDongC. Anisotropic response in mechanical and corrosion properties of hastelloy X fabricated by selective laser melting. Constr Build Mater. 2019; 221 (10): 720–729. doi: 10.1016/j.conbuildmat.2019.06.132
25.
KongDDongCNiX. Superior resistance to hydrogen damage for selective laser melted 316L stainless steel in a proton exchange membrane fuel cell environment. Corros Sci. 2020; 108425. doi: 10.1016/j.corsci.2019.108425
26.
ChengJQingJGuoY. High-strength weathering steels obtained using bainite matrix and nanoscale co-precipitation. Mater Lett. 2019; 236: 307–311. doi: 10.1016/j.matlet.2018.10.076
27.
ZhangTWuJJinL. Enhancing the mechanical and anticorrosion properties of 316L stainless steel via a cathodic plasma electrolytic nitriding treatment with added PEG. J Mater Sci Technol. 2019; 35: 2630–2637. doi: 10.1016/j.jmst.2019.07.031
28.
Del Abra-ArzolaJLGarcía-RenteríaMACruz-HernándezVL. Study of the effect of sigma phase precipitation on the sliding wear and corrosion behaviour of duplex stainless steel AISI 2205. Wear. 2018; 400-401: 43–51. doi: 10.1016/j.wear.2017.12.019
29.
BrugGJvan den EedenALGSluyters-RehbachM. The analysis of electrode impedances complicated by the presence of a constant phase element. J Electroanal Chem Interfacial Electrochem. 1984; 176: 275–295. doi: 10.1016/S0022-0728(84)80324-1
30.
ZhaoYLiuWFanY. Effect of Cr content on the passivation behavior of Cr alloy steel in a CO2 aqueous environment containing silty sand. Corros Sci. 2020; 168: 108591. doi: 10.1016/j.corsci.2020.108591
31.
HakikiNE.Comparative study of structural and semiconducting properties of passive films and thermally grown oxides on AISI 304 stainless steel. Corros Sci. 2011; 53: 2688–2699. doi: 10.1016/j.corsci.2011.05.012
32.
HirschornBOrazemMETribolletB. Determination of effective capacitance and film thickness from constant-phase-element parameters. Electrochim Acta. 2010; 55: 6218–6227. doi: 10.1016/j.electacta.2009.10.065
33.
MartinURessJBoschJ. Stress corrosion cracking mechanism of AISI 316LN stainless steel rebars in chloride contaminated concrete pore solution using the slow strain rate technique. Electrochim Acta. 2020; 335: 135565. doi: 10.1016/j.electacta.2019.135565
34.
KongDDongCNiX. Corrosion of metallic materials fabricated by selective laser melting. NPJ Mater Degrad. 2019; 3 (1): 1–14. doi: 10.1038/s41529-019-0086-1
35.
LuoHLiZMingersAM. Corrosion behavior of an equiatomic CoCrFeMnNi high-entropy alloy compared with 304 stainless steel in sulfuric acid solution. Corros Sci. 2018; 134: 131–139. doi: 10.1016/j.corsci.2018.02.031
36.
YangXDuCWanH. Influence of sulfides on the passivation behavior of titanium alloy TA2 in simulated seawater environments. Appl Surf Sci. 2018; 458: 198–209. doi: 10.1016/j.apsusc.2018.07.068
37.
LiPZhaoYLiuY. Effect of Cu addition to 2205 duplex stainless steel on the resistance against pitting corrosion by the Pseudomonas aeruginosa Biofilm. J Mater Sci Technol. 2017; 33: 723–727. doi: 10.1016/j.jmst.2016.11.020
38.
JinlongLTongxiangLChenW. Comparison of corrosion properties of passive films formed on coarse grained and ultrafine grained AISI 2205 duplex stainless steels. J Electroanal Chem. 2015; 757: 263–269. doi: 10.1016/j.jelechem.2015.09.036
39.
KongDNiXDongC. Anisotropy in the microstructure and mechanical property for the bulk and porous 316L stainless steel fabricated via selective laser melting. Mater Lett. 2019; 235: 1–5. doi: 10.1016/j.matlet.2018.09.152