Literature data on the influence of concrete cracks on corrosion propagation of reinforcing steel are contradictory. This might be due to very different exposure and test conditions but also to a lack of time-resolved data in cyclic wetting–drying exposure. Here, the influence of the environmental conditions on the corrosion rates in cracked concrete is studied experimentally. The results show that the corrosion rate in cracked concrete depends on the duration of wetting and drying phases and the relative humidity (RH) during the drying phase. The lower the ambient RH in the drying phase, the faster the cracks dry, which depresses the corrosion rate in the periods between the wetting events. A model is proposed to estimate corrosion rates in cracked concrete cyclic wetting/drying exposure.
British Cement Association. Development of an holistic approach to ensure the durability of new concrete construction. Crowthorne: British Cement Association; 1997.
2.
ACI Committee 224. Causes, evaluation, and repair of cracks in concrete structures. Farmington Hills (MI): American Concrete Institute; 2007, p. 1–22.
3.
The Concrete Society. Non-structural cracks in concrete: report of a Concrete Society Working Party. London: The Concrete Society; 1982.
4.
BrühwilerEMennC.Stahlbetonbrücken, 3., aktual. und erw. Aufl. ed.Wien: Springer; 2003.
5.
OtienoMBeushausenHAlexanderM.Towards incorporating the influence of cover cracking on steel corrosion in RC design codes: the concept of performance-based crack width limits. Mater Struct. 2012; 45: 1805–1816. doi: 10.1617/s11527-012-9871-9
6.
PeaseBGeikerMStangH. The design of an instrumented rebar for assessment of corrosion in cracked reinforced concrete. Mater Struct. 2011; 44: 1259–1271. doi: 10.1617/s11527-010-9698-1
7.
DangVHFrançoisRL'HostisV. Propagation of corrosion in pre-cracked carbonated reinforced mortar. Mater Struct. 2015; 48: 2575–2595. doi: 10.1617/s11527-014-0338-z
8.
GowripalanNSirivivatnanonVLimCC.Chloride diffusivity of concrete cracked in flexure. Cem Concr Res. 2000; 30: 725–730. doi: 10.1016/S0008-8846(00)00216-7
9.
WinPPWatanabeMMachidaA.Penetration profile of chloride ion in cracked reinforced concrete. Cem Concr Res. 2004; 34: 1073–1079. doi: 10.1016/j.cemconres.2003.11.020
10.
The Concrete Society. Relevance of cracking in concrete to reinforcement corrosion. Technical Report. Hampshire (UK): The Concrete Society; 2015, pp. 43.
11.
GehlenCKapteinaG.Influence of cracks upon corrosion. Kongens Lyngby DK: Durable and Reliable Tunnel Structures; 2004.
12.
BlagojevicAFennis-HuijbenSAAMWalravenJC.Impact of cracks on chloride-induced corrosion and durability of reinforced concrete structures – a literature review, V International PhD Student Workshop on Durability of Reinforced Concrete, VTT Technical Research Center, 2012.
13.
PachecoJPolderR.Corrosion initiation and propagation in cracked concrete – a literature review. In: Andrade C, Gulikers J, editors. Advances in modeling concrete service life: Proceedings of 4th International RILEM PhD Workshop, RILEM Bookseries 3, Madrid, Spain, 2010, p. 85-93.
14.
AhmadiBRemezanianpourAASobhaniJ.Rebar corrosion in cracked RC prisms located in harsh marine environment. Mag Concr Res. 2014; 66: 1007–1019. doi: 10.1680/macr.14.00055
15.
FrançoisRArliguieG.Effect of microcracking and cracking on the development of corrosion in reinforced concrete members. Mag Concr Res. 1999; 51: 143–150. doi: 10.1680/macr.1999.51.2.143
16.
OtienoMBAlexanderMGBeushausenH-D.Corrosion in cracked and uncracked concrete – influence of crack width, concrete quality and crack reopening. Mag Concr Res. 2010; 62: 393–404. doi: 10.1680/macr.2010.62.6.393
17.
ScottAAlexanderMG.The influence of binder type, cracking and cover on corrosion rates of steel in chloride-contaminated concrete. Mag Concr Res. 2007; 59: 495–505. doi: 10.1680/macr.2007.59.7.495
18.
Boschmann KäthlerCAngstUMWagnerM. Effect of cracks on chloride-induced corrosion of reinforcing steel in concrete, Statens Vegvesen, Oslo, Norway, 2017 “open access”.
19.
Boschmann KäthlerCAngstUMLarsenCK. Effect of cracks on chloride-induced corrosion of reinforcing steel in concrete, EuroCorrPrague, 2017.
20.
IsgorBAngstUGeikerM. Recommended practice for reporting experimental data produced from studies on corrosion of steel in cementitious systems. RILEM Tech Lett. 2019; 4: 22–32. doi: 10.21809/rilemtechlett.2019.90
21.
Bundesamt für Statistik, Strassenlängen: Stand 31. Dezember 2018, in: Bundesamt für Statistik (Ed.), Bundesamt für Statistik, Neuchâtel, 2018.
22.
BollerMBrynerA.Häufig gestellte Fragen zur Strassensalzung. Eawag, editor. Dübendorf: Eawag; 2016.
23.
MohammedTUOtsukiNHisadaM. Effect of crack width and bar types on corrosion of steel in concrete. J Mater Civil Eng. 2001; 13: 194–201. doi: 10.1061/(ASCE)0899-1561(2001)13:3(194)
24.
OtienoMBAlexanderMGBeushausenHD.Corrosion propagation in cracked and uncracked concrete. In: AlexanderMGBeushausenH-DDehnFMoyoP, editors. International conference on concrete repair, rehabilitation and retrofitting (ICCRRR). Cape Town: CRC Press; 2009. p. 339–344.
25.
GlassGKPageCLShortNR.Factors affecting the corrosion rate of steel in carbonated mortars. Corros Sci. 1991; 32: 1283–1294. doi: 10.1016/0010-938X(91)90048-T
26.
AlonsoCAndradeCGonzálezJA.Relation between resistivity and corrosion rate of reinforcements in carbonated mortar made with several cement types. Cem Concr Res. 1988; 18: 687–698. doi: 10.1016/0008-8846(88)90091-9
27.
OsbornL.Current results – weather and science facts. Smithers (BC): Current Results Publishing Ltd; 2019.
28.
PeaseBJ.Influence of concrete cracking on ingress and reinforcement corrosion. Lyngby: DTU Department of Civil Engineering, Technical University of Denmark; 2010, pp. 298.
29.
van NygaardP.Non-destructive electrochemical monitoring of reinforcement corrosion. Lyngby: Technical University of Denmark, Technical University of Denmark, Kgs; 2008.
30.
AngstUMBoschmannCWagnerM. Experimental protocol to determine the chloride threshold value for corrosion in samples taken from reinforced concrete structures. J Vis Exp. 2017; 126: 1–11.
31.
AngstUWagnerMElsenerB. Schlussbericht ASTRA AGB 2012/010: Methode zur Bestimmung des kritischen Chloridgehalts an bestehenden Stahlbetonbauwerken, ASTRA; 2016.
32.
LambertPPageCLVassiePRW.Investigations of reinforcement corrosion. 2. Electrochemical monitoring of steel in chloride-contaminated concrete. Mater Struct1991; 24: 351–358. doi: 10.1007/BF02472068