Cathodic protection prolongs the service life of fluid transport and offshore engineering components by suppressing corrosion. This study assesses the effect of two cathodic protection methods, such as impressed current cathodic protection (ICCP) and sacrificial anode cathodic protection (SACP), on three ferrous-based materials under laboratory-controlled corrosive wear conditions. The SACP was as effective as ICCP on the protection of the low alloy steel and white chromium cast iron under both solid and solid-free corrosive wear conditions. Under solid–liquid impingement, significant reductions in the material loss were also observed in both the direct impingement zone and the outer area (oblique angle of attack). This demonstrates the substantial impact of cathodic protection systems that are exposed to erosion–corrosion dominated environments.
WalkerCIBodkinGC.Empirical wear relationships for centrifugal slurry pumps. Part 1: side-liners. Wear. 2000; 242 (1-2): 140–146. doi: 10.1016/S0043-1648(00)00413-0
2.
WalkerCI.Slurry pump side-liner wear: comparison of some laboratory and field results. Wear. 2001; 250-251 (1-12): 81–87. doi: 10.1016/S0043-1648(01)00613-5
3.
LópezDAlonso FalleirosNPaulo TschiptschinA.Effect of nitrogen on the corrosion-erosion synergism in an austenitic stainless steel. Tribol Int. 2011; 44 (5): 610–616. doi: 10.1016/j.triboint.2010.12.013
4.
Aminul IslamMFarhatZNAhmedEM. Erosion enhanced corrosion and corrosion enhanced erosion of API X-70 pipeline steel. Wear. 2013; 302 (1-2): 1592–1601. doi: 10.1016/j.wear.2013.01.041
5.
MalkaRNešićSGulinoDA.Erosion-corrosion and synergistic effects in disturbed liquid-particle flow. Wear. 2007; 262 (7-8): 791–799. doi: 10.1016/j.wear.2006.08.029
6.
SouzaVADNevilleA.Corrosion and synergy in a WC-Co-Cr HVOF thermal spray coating – understanding their role in erosion-corrosion degradation. Wear. 2005; 259 (1-6): 171–180. doi: 10.1016/j.wear.2004.12.003
7.
HodgkiessTNevilleAShresthaS.Electrochemical and mechanical interactions during erosion-corrosion of a high-velocity oxy-fuel coating and a stainless steel. Wear. 1999; 233-235: 623–634. doi: 10.1016/S0043-1648(99)00246-X
8.
PopoolaLTGremaASLatinwoGK. Corrosion problems during oil and gas production and its mitigation. Int J Ind Chem. 2013; 4 (1): 1–15. doi: 10.1186/2228-5547-4-35
9.
RajeevPSurendranathanAOMurthyCSN.Corrosion mitigation of the oil well steels using organic inhibitors – a review. J Mater Environ Sci. 2012; 3 (5): 856–869.
10.
NevilleAWangC.Erosion-corrosion of engineering steels – can it be managed by use of chemicals?Wear. 2009; 267 (11): 2018–2026. doi: 10.1016/j.wear.2009.06.041
11.
MorganJH.Cathodic protection. 2nd ed. Houston, United States: NACE International; 1987.
12.
RevieRWUhligHH.Corrosion and corrosion control: an introduction to corrosion science and engineering.4th ed. New Jersey, USA: Hoboken; 2008.
13.
BattCDodsonJRobinsonMJ.Hydrogen embrittlement of cathodically protected high strength steel in sea water and seabed sediment. Br Corros J. 2002; 37 (3): 194–198. doi: 10.1179/000705902225006606
14.
HeidersbachR.Metallurgy and corrosion control in oil and gas production. New Jersey, USA: Hoboken; 2010.
15.
NevilleAHodgkiessT.Characterisation of high-grade alloy behaviour in severe erosion-corrosion conditions. Wear. 1999; 233-235: 596–607. doi: 10.1016/S0043-1648(99)00220-3
16.
JonesMLlewellynRJ.Erosion-corrosion assessment of materials for use in the resources industry. Wear. 2009; 267 (11): 2003–2009. doi: 10.1016/j.wear.2009.06.025
17.
RajahramSSHarveyTJWoodRJK.Erosion–corrosion resistance of engineering materials in various test conditions. Wear. 2009; 267 (1-4): 244–254. doi: 10.1016/j.wear.2009.01.052
18.
NevilleAHuX.Mechanical and electrochemical interactions during liquid–solid impingement on high-alloy stainless steels. Wear. 2001; 251: 1284–1294. doi: 10.1016/S0043-1648(01)00757-8
19.
GiourntasLHodgkiessTGallowayAM.Comparative study of erosion–corrosion performance on a range of stainless steels. Wear. 2015; 332-333: 1051–1058. doi: 10.1016/j.wear.2014.12.052
20.
BarikRCWhartonJAWoodRJK. Erosion and erosion-corrosion performance of cast and thermally sprayed nickel-aluminium bronze. Wear. 2005; 259 (1-6): 230–242. doi: 10.1016/j.wear.2005.02.033
21.
BrownlieFHodgkiessTPearsonA. Effect of nitriding on the corrosive wear performance of a single and double layer Stellite 6 weld cladding. Wear. 2017: 1279–1285. doi: 10.1016/j.wear.2017.01.006
22.
BellezzeTRoventiGFratesiR.Localised corrosion and cathodic protection of 17 4PH propeller shafts. Corros Eng Sci Technol. 2013; 48 (5): 340–345. doi: 10.1179/1743278213Y.0000000082
23.
GiourntasLHodgkiessTGallowayAM.Enhanced approach of assessing the corrosive wear of engineering materials under impingement. Wear. 2015; 338-339: 155–163. doi: 10.1016/j.wear.2015.06.004
BrownlieFAneneCHodgkiessT. Comparison of hot wire TIG Stellite 6 weld cladding and lost wax cast Stellite 6 under corrosive wear conditions. Wear. 2018: 71–81. doi: 10.1016/j.wear.2018.03.004
26.
AndrewsNGiourntasLGallowayAM. Effect of impact angle on the slurry erosion-corrosion of Stellite 6 and SS316. Wear. 2014; 320 (1): 143–151. doi: 10.1016/j.wear.2014.08.006
27.
BermúdezMDCarriónFJMartínez-NicolásG. Erosion-corrosion of stainless steels, titanium, tantalum and zirconium. Wear. 2005; 258 (1-4): 693–700. doi: 10.1016/j.wear.2004.09.023
28.
MalayogluUNevilleA.Comparing the performance of HIPed and cast Stellite 6 alloy in liquid–solid slurries. Wear. 2003; 255 (1-6): 181–194. doi: 10.1016/S0043-1648(03)00287-4
29.
LapidesLLevyA.The halo effect in jet impingement solid particle erosion testing of ductile metals. Wear. 1980; 58 (2): 301–311. doi: 10.1016/0043-1648(80)90159-3
30.
de SouzaVANevilleA.Corrosion and erosion damage mechanisms during erosion - corrosion of WC-Co-Cr cermet coatings. Wear. 2003; 255 (1-6): 146–156. doi: 10.1016/S0043-1648(03)00210-2
31.
WoodFW.Erosion by solid-particle impacts : a testing update. J Test Eval. 1986; 14 (1): 23–27. doi: 10.1520/JTE10316J