The corrosion behaviour of electrochemically induced surface annealed (EISA) 304L stainless steel was analysed using a range of electrochemical methods, such as polarisation, impedance and Mott–Schottky techniques. Secondary ion mass spectroscopy was used to examine the elemental distribution around the surface of an EISA-treated specimen. The results showed that the EISA treatment increases the resistance to pitting corrosion due to surface densification caused by the absorption of NO and/or N2, which had been reduced under cathodic polarisation during the EISA process. Owing to the limited annealing depth, however, the prolonged corrosion process (i.e. Fe dissolution) can lead to the dissolution of NO and/or N2 species, which had been absorbed on the outer surface, and only smaller portions remained with an uneven distribution at the surface. This can make the EISA-treated steel more vulnerable to corrosion.
HedbergYSOdnevallWI.Metal release from stainless steel in biological environments: a review. Biointerphases. 2016; 11: 018901-1-17. doi: 10.1116/1.4934628
2.
SumitomoH.Investigation of the development of cold-rolling and annealing textures in SUS304 austenitic stainless steel. J Iron Steel Inst Jpn. 1991; 77: 558–565. doi: 10.2355/tetsutohagane1955.77.4_558
3.
AngelT.Formation of martensite in austenitic stainless steel. J Iron Steel Inst. 1954; 177: 165–174.
4.
LudwigsonDCBergerJA.Plastic behaviour of metastable austenitic stainless steels. J Iron Steel Inst. 1969; 207: 63–69.
5.
OlsonGBCohenM.Kinetics of strain-induced martensitic transformation. Metall Trans A. 1975; 6: 791–795. doi: 10.1007/BF02672301
6.
OlsonGBCohenM.Stress-assisted isothermal martensitic transformation: application to TRIP steels. Metall Trans A. 1982; 13: 1907–1914. doi: 10.1007/BF02645934
7.
HuangGLMatlockDKKraussG.Martensite formation, strain rate sensitivity and deformation behaviour of type 304 stainless steel sheet. Metall Trans A. 1989; 20: 1239–1246. doi: 10.1007/BF02647406
8.
TomimuraKTakakiSTokunagaY.Reversion mechanism from deformation induced martensite to austenite in metastable austenitic stainless steels. ISIJ Int. 1991; 31: 1431–1437. doi: 10.2355/isijinternational.31.1431
9.
TakakiSTomimuraKUedaS.Effect of pre-cold-working on diffusional reversion of deformation induced martensite in metastable austenitic stainless steel. ISIJ Int. 1994; 34: 522–527. doi: 10.2355/isijinternational.34.522
GleidysMAsuncionBSusanaG. Influence of the cold working induced martensite on the electrochemical behavior of AISI 304 stainless steel surfaces. J Mater Res Tech. 2019; 8 (1): 1335–1346. doi: 10.1016/j.jmrt.2018.10.004
12.
GravierJVignalVBissey-BrestonS.Influence of residual stress, surface roughness and crystallographic texture induced by machining on the corrosion behaviour of copper in salt-fog atmosphere. Corr Sci. 2012; 61: 162–170. doi: 10.1016/j.corsci.2012.04.032
13.
XueLFeiXDanW. Effect of residual and external stress on corrosion behaviour of X80 pipeline steel in sulphate-reducing bacteria environment. Eng Fail Anal. 2018; 91: 275–290. doi: 10.1016/j.engfailanal.2018.04.016
14.
NazarovAVivierVThierryD. Effect of mechanical stress on the properties of steel surfaces: scanning kelvin probe and local electrochemical impedance study. J Electrochem Soc. 2017; 164: C66–C74. doi: 10.1149/2.1311702jes
15.
GrabkeHJ.Carburization, carbide formation, metal dusting, coking. J Mater Technol. 2002; 36: 297–305.
16.
BabakrAHabibyF.Lengthening, cracking and weld ability problems of Fe-Ni-Cr alloy tube. J Miner Mater Charact Eng. 2009; 8: 133–148.
17.
RashidMWAGakimMRosliZM. Formation of Cr23C6 during the sensitization of AISI 304 stainless steel and its effect to pitting corrosion. Int J Electrochem Sci. 2012; 7: 9465–9477.
18.
PunburiPTareelapN.Post weld heat treatment to reduce intergranular corrosion susceptibility of dissimilar welds between austenitic 304 and ferritic 430 stainless steels. Proceedings of the 1st Mae Fah Luang University International Conference; Bangkok, Thailand; 2012. p. 1-9.
19.
ShaoG.Thermodynamic modeling of the Cr-Nb-Si system. J Intermet. 2005; 13: 69–78. doi: 10.1016/j.intermet.2004.06.003
BursteinGTSasakiKHutchingsIM.Lattice changes generated by electrochemically induced surface annealing of austenitic stainless steel. Electrochem Solid State Lett. 2003; 6: D13–D15. doi: 10.1149/1.1612013
22.
LiZQiJLiuW.The effect of electrochemically induced annealing on the pitting resistance of metastable austenite stainless steel. Metall Mater Trans A. 2006; 37: 435–439. doi: 10.1007/s11661-006-0014-1
23.
ChunchunXKeHYongxinW. Deformation-induced martensite phase transition and its effect on pitting susceptibility for 1Cr18Ni9Ti stainless steel. J Chin Soc Corr Protect. 1996; 16: 47–52.
24.
GangHChunchunXXingshengZ. Effect of cold working on pitting susceptibility of 304 stainless steel. J Chin Soc Corr Protect. 2002; 22: 198–201.
25.
GuangjieSYulinWYurongW. Correlation between pit corrosive sensitivity of metastable austenite stainless steel and its content of ferromagnetic phases. Iron Steel. 1996; 31: 48–52.
26.
RuifenXChunchunXHuiyongX. Relation between deformation induced martensite and pitting susceptibility of 1Cr18Ni9Ti. Corr Sci Protect Technol. 1998; 10: 197–201.
27.
ChunchunXRuifenXWeizhenO. EIS study of the effect of deformation induced α′ martensite on pitting sensibility of 1Cr18Ni9Ti stainless steel in acidic NaCl solution. Corr Sci Protect Technol. 1997; 9: 95–102.
28.
RuifenXChunchunXWeizhenO. Effect of the martensite phase transition of austenitic stainless steel on the corrosion resistance. J Beijing Univ Chem Technol. 1998; 25: 57–63.
29.
ChunchunXXinshengZGangH. Deformation induced martensite of cold worked stainless steel and its corrosion behaviors. Mater Protect. 2002; 35: 15–17.
30.
ChunchunXWeizhenORuifenX.An investigation of the relationship between SCC susceptibility and ferromagnetic content of 1Cr18Ni9Ti stainless steel in chloride solution. J Chin Soc Corr Protect. 1997; 17: 73–76.
31.
ChunchunXWeizhenOBaowenJ. The effect of martensite induced by deformation on stress corrosion cracking of 1Cr18Ni9Ti stainless steel. Corr Sci Protect Technol. 1996; 8: 267–270.
32.
MaximilianSAlexandarRZOlagaK. A perspective on low-temperature water electrolysis-challenges in alkaline and acidic technology. Int J Electorchem Sci. 2018; 13: 1173–1226.
33.
DurstJSiebelASimonC. New insights into the electrochemical hydrogen oxidation and evolution reaction mechanism. Energy Environ Sci. 2014; 7: 2255–2260. doi: 10.1039/C4EE00440J
34.
NeyerlinKCGuWJorneJ. Study of the exchange current density for the hydrogen oxidation and evolution reactions. J Electrochem Soc. 2007; 154: B631–B635. doi: 10.1149/1.2733987
35.
ShengWGasteigerHAShao-HornY.Hydrogen oxidation and evolution reaction kinetics on platinum: acid vs. alkaline electrolytes. J Electrochem Soc. 2010; 157: B1529–B1536. doi: 10.1149/1.3483106
36.
ShengWZhuangZGaoM. Correlating hydrogen oxidation and evolution activity on platinum at different pH with measured hydrogen binding energy. Nat Commun. 2015; 6: 1–6. doi: 10.1038/ncomms6848
37.
ZhengJShengWZhuangZ. Universal dependence of hydrogen oxidation and evolution reaction activity of platinum-group metals on pH and hydrogen binding energy. Sci Adv. 2016; 2: 1–8.
38.
BrianCSSayedMHToddCH.NO2− activation and reduction to NO by a nonheme Fe(NO2)2 complex. J Am Chem Soc. 2014; 136: 10230–10233. doi: 10.1021/ja505236x
BhaduriBVermaN.Preparation of asymmetrically distributed bimetal ceria CeO2 and copper (Cu) nanoparticles in nitrogen-doped activated carbon micro/nanofibers for the removal of nitric oxide (NO) by reduction. J Colloid Interface Sci. 2014; 436: 218–226. doi: 10.1016/j.jcis.2014.08.030
41.
XuWTZhouJCLiH. Microwave-assisted catalytic reduction of NO into N2 by activated carbon supported Mn2O3 at low temperature under O2 excess. Fuel Process Technol. 2014; 127: 1–6. doi: 10.1016/j.fuproc.2014.06.005
42.
ZhangJZhangJYXuYF. Efficient selective catalytic reduction of NO by novel carbon-doped metal catalysts made from electroplating sludge. Environ Sci Technol. 2014; 48 (19): 11497–11503. doi: 10.1021/es502391y
43.
AarnaISuubergEM.The role of carbon monoxide in the NO-carbon reaction. Energy Fuels. 1999; 13 (6): 1145–1153. doi: 10.1021/ef9900278
44.
LuCYWeyMY.Simultaneous removal of VOC and NO by activated carbon impregnated with transition metal catalysts in combustion flue gas. Fuel Process Technol. 2007; 88 (6): 557–567. doi: 10.1016/j.fuproc.2007.01.004
45.
GoncalvesFFigueiredoJL.Development of carbon supported metal catalysts for the simultaneous reduction of NO and N2O. Appl Catal B. 2004; 50 (4): 271–278. doi: 10.1016/j.apcatb.2004.01.014
46.
LuBTZengYPangX. Effects of hydrogen and tensile stress on passivity of carbon steel. Corr Eng Sci Technol. 2015; 50: 186–190. doi: 10.1179/1743278215Y.0000000020
47.
SimoesAMPFerreiraMGSRondotB. Study of passive films formed on AISI 304 stainless steel by impedance measurements and photoelectrochemistry. J Electrochem Soc. 1990; 137: 82–87. doi: 10.1149/1.2086444
48.
JingWGuoQQHourYQ. Catalytic role of vanadium (V) sulfate on activated carbon for SO2 oxidation and NH3-SCR of NO at low temperatures. Catal Commun. 2014; 56: 23–26. doi: 10.1016/j.catcom.2014.06.017
49.
WangJPYanZLiuLL. In situ DRIFTS investigation on the SCR of NO with NH3 over V2O5 catalyst supported by activated semi-coke. Appl Surf Sci. 2014; 313: 660–669. doi: 10.1016/j.apsusc.2014.06.043
50.
HuangZGHouYQZhuZP. Study on the NO reduction by NH3 on a SO42−/AC catalyst at low temperature. Catal Commun. 2014; 50: 83–86. doi: 10.1016/j.catcom.2014.03.008
51.
LiuQYLiuZY.Carbon supported vanadia for multi-pollutants removal from flue gas. Fuel. 2013; 108: 149–158. doi: 10.1016/j.fuel.2011.05.015
52.
XieWSunZXiongY. Effects of surface chemical properties of activated coke on selective catalytic reduction of NO with NH3 over commercial coal-based activated coke. Int J Min Sci Technol. 2014; 24: 471–475. doi: 10.1016/j.ijmst.2014.05.009
53.
WangYLLiXXZhanL. Effect of SO2 on activated carbon honeycomb supported CeO2-MnOx catalyst for NO removal at low temperature. Ind Eng Chem Res. 2015; 54 (8): 2274–2278. doi: 10.1021/ie504074h
54.
MehtaYTrivediSChandraK. Miner effect of silicon on the corrosion behavior of powder-processed phosphoric irons. Mater Charact Eng. 2010; 9: 855–865.