Cyclic oxidation tests of sintered MCrAlY:Pt composites were carried out at temperatures of 1223 and 1273 K. Composite tablets were previously produced by spark plasma sintering. To assess an effect of platinum dispersed, microstructural characterisation was performed on the tablets before and after the cyclic oxidation treatment. Scanning electron microscopy analysis of the oxide layer showed that the presence of typical α-Al2O3 and NiAl2O4 spinel had structure columnar and equiaxial in both samples. Fine sintered microstructure and addition of Pt into the MCrAlY matrix enhanced the resistance of the material to cyclic oxidation.
CzechNSchmitzFStamW.Improvement of MCrAlY coatings by addition of rhenium. Surf Coat Technol. 1994; 68-69: 17–21. doi: 10.1016/0257-8972(94)90131-7
2.
NickelHClemensDQuadakkersWJDevelopment of NiCrAlY alloys for corrosion – resistant coatings of Gas turbine components. J Press Vessel Technol. 1999; 121: 384–387. doi: 10.1115/1.2883719
3.
MonceauDBoudot-MiquetABouhanekKOxidation et protection des materiaux pour sous-couches (NiAlPd, NiAlPt, NiCoCrAlTa, CoNiCrAlY) de barriers thermiques. J Phys IV France. 2000; 10: 167–171. doi: 10.1051/jp4:2000423
4.
TaylorTABettridgeDF.Development of alloyed and disperse –strengthened MCrAlY coatings. Surf Coat Technol. 1996; 86-87: 9–14. doi: 10.1016/S0257-8972(96)02961-1
5.
CockingLJJohnstonRPRichardsPG.Protecting Gas turbine components: the relative durability of a conventional and a platinum –modified aluminide coating. Plat Met Rev. 1985; 29 (1): 17–26.
6.
PatnaikP.C.ThamburajR.SudarshanT.S.Formation and behaviour of platinum aluminide coatings on nickel-base alloys. In: SudarshanTSBhatDG, editors. Surface modification technologies III. Warrendale (PA): TMS; 1990. p. 759.
7.
StreiffRBooneDH.Corrosion resistant modified aluminide coatings. In: SissonRDJR, editor. Coatings and bimetallics for aggressive environments. Metals Park (OH): ASM International; 1985. p. 159.
8.
KimGMMieirGHPettitFS.Platinum-modified diffusion aluminide coatings on nickel-base, Report University of Pittsburgh; 1993. 28.
9.
FeltonEJPettitFS.Development growth and adhesion of Al2O3 on platinum–aluminum alloys. Oxid Met. 1976; 10 (3): 189–223. doi: 10.1007/BF00612159
10.
KammLJMilliganWW.Phase stability in (Ni,Pt)3Al alloys. Scripta Metall Mater. 1994; 31 (11): 1461–1464. doi: 10.1016/0956-716X(94)90056-6
11.
FountainJGGolightlyFAStottFHThe influence of platinum on the maintenance of α-Al2O3 as a protective scale. Oxid Met. 1976; 10: 341–345. doi: 10.1007/BF00612031
12.
AllamIMAkuezueHCWhittleDP.Influence of small Pt additions on Al2O3 scale adherence. Oxid Met. 1980; 14 (6): 517–530. doi: 10.1007/BF00603477
13.
HoppinG.S.DanesiW.P. In: SimsCTStolofNS, and HagelWC editors. High Temperature Materials for Aerospace and Industrial Power. New York (NY): John Wiley & Sons; 1987. p. 949–962. A Wiley-Interscience Publication.
14.
MurakumoTKobayashTKoizumiYCreep behaviour of Ni-base single-crystal superalloys with various γ volume fraction. Acta Mater. 2004; 52: 3737–3744. doi: 10.1016/j.actamat.2004.04.028
15.
DrostEGölitzerHPoniatowskiMPlatinwerstoffe für hochtemperatur-einsatz=platinum engineering materials for high temperature applications. Metallurgy. 1996; 50: 492–498.
16.
HillPJCornishLAEllisPThe effects of Ti and Cr additions on the phase equilibria and properties of (Pt)/Pt3Al alloys. J Alloys Compds. 2001; 322: 166–175. doi: 10.1016/S0925-8388(01)01018-0
17.
HillPJAdamsNBiggsTPlatinum alloys based on Pt–Pt3Al for ultra-high temperature use. Mater Sci Eng. 2002; 329-331: 295–304. doi: 10.1016/S0921-5093(01)01577-5
HuellerMWenderothMVorbergSOptimization of composition and heat treatment of Age-hardened Pt-Al-Cr-Ni alloys. Metall Mater Trans. 2005; 36A: 681–689.
20.
WenderothMGlatzelUVölklROn the development and investigations of Quaternary Pt-based superalloys with Ni-additions. Metall Mater Trans. 2005; 36: 567–575. doi: 10.1007/s11661-005-0171-7
21.
VorbergSWenderothMFischerBTEM investigations of the γ/γ’ phase boundary in Pt-base superalloys. JOM. 2005; 57: 49–51. doi: 10.1007/s11837-005-0233-8
22.
PintBAWrightIGLeeWYSubstrate and bond coat compositions: factors affecting alumina scale adhesion. Mater Sci Eng. 1998; A245: 201–211. doi: 10.1016/S0921-5093(97)00851-4
23.
YangYFJiangCYYaoHRCyclic oxidation and rumpling behaviour of single phase β-(Ni,Pt)Al coatings with different thickness of initial Pt plating. Corr Sci. 2016; 111: 162–174. doi: 10.1016/j.corsci.2016.05.011
24.
ZhouZPengaHZhengaL. Microstructure and cyclic oxidation behaviour of low-Pt/Dy co-composite β-NiAl coatings on single crystal (SC) superalloy. Surf Coat Technol. 2016; 304 (25): 108–116. doi: 10.1016/j.surfcoat.2016.01.062
25.
LiuRDJiangSMYuHJPreparation and hot corrosion behaviour of Pt modified AlSiY coating on a Ni-based superalloy. Corr Sci. 2016; 104: 162–172. doi: 10.1016/j.corsci.2015.12.007
26.
TerockMKonradCHPoppRTailored platinum-nickel nanostructures on zirconia developed by metal casting, internal oxidation and dealloying. Corr Sci. 2016; 112: 246–254. doi: 10.1016/j.corsci.2016.06.010
27.
VialasNMonceauD.Effect of Pt and Al content on the long-term, high temperature oxidation behavior and interdiffusion of a Pt-modified aluminide coating deposited on Ni-base superalloys. Surf Coat Technol. 2006; 201 (7): 3846–3851. doi: 10.1016/j.surfcoat.2006.07.246
28.
ChenK.Sulphur diffusion in β-NiAl and effect of Pt additive: an ab initio study. J Phys D: Appl Phys. 2016; 49: 055306. doi: 10.1088/0022-3727/49/5/055306
29.
BiondoCStrohlJPSamuelsonJWNickel-base alloy for gas turbine applications. Power Systems Manufacturing LIc-US Patent, 20100080729 A1 2016 Patents.
30.
MurphyMS.Pt-Al-Hf/Zr coating and method, US Patent 9284846 B2 2016 Patents.
31.
GleesonBWangWHayashiSEffects of platinum on the interdiffusion and oxidation behavior of Ni-Al-based alloys. Mater Sci Forum. 2004; 461-464: 213–222. doi: 10.4028/www.scientific.net/MSF.461-464.213
32.
PintBA.Experimental observations in support of the dynamic segregation theory to explain the reactive element effectOxid Met. 1996; 45: 1–37. doi: 10.1007/BF01046818
33.
EvansHLobbRC.Conditions for the initiation of oxide-scale cracking and spallation. Corr Sci. 1984; 24: 209–222. doi: 10.1016/0010-938X(84)90051-9
34.
HaynesJAPintBAPorterWDComparison of thermal expansion and oxidation behavior of various high-temperature coating materials and superalloysMater High Temp. 2004; 21: 87–94. doi: 10.1179/mht.2004.012
35.
PintBAHaynesJAMoreKL In: ReedRC, editors. The performance of Pt-modified alumina-forming coatings and model alloys. Warrendale (PA): TMS; 2008. Submitted to Superalloys 2008.
36.
NichollsJR.Advances in coating design for high performance Gas turbines. MRS Bull. 2003; 28: 659–670. doi: 10.1557/mrs2003.194
37.
Cuenca-ÁlvarezR. Díaz de la TorreSJuarez LopezF.Mechanical dispersion of platinum particles and its effect on the microstructure of MCrAlY alloy prepared by SPS. Powder Technol. 2016; 291: 193–200. doi: 10.1016/j.powtec.2015.12.017
38.
OmoriM.Sintering, consolidation, reaction and crystal growth by the spark plasma system (SPS). Mater Sci Eng A. 2000; 287: 183–188. doi: 10.1016/S0921-5093(00)00773-5
39.
MunirZAAnselmi-TamburiniUOhyanagiU.The effect of electric field and pressure on the synthesis and consolidation of materials: A review of the spark plasma sintering method. J Mater Sci. 2006; 41: 763–777. doi: 10.1007/s10853-006-6555-2
40.
CouretAMolénatGGalyJMicrostructures and mechanical properties of TiAl alloys consolidated by spark plasma sintering. Intermetallics. 2008; 16: 1134–1141. doi: 10.1016/j.intermet.2008.06.015
41.
BangchaoYJiawenJYicanZ.Spark-plasma sintering the 8-mol% yttria-stabilized zirconia electrolyte. J Mater Sci. 2004; 39 (22): 6863–6865. doi: 10.1023/B:JMSC.0000045622.65071.3d
42.
DahlPKausIZhaoZDensification and properties of zirconia prepared by three different sintering techniques. Ceram Int. 2007; 33: 1603–1610. doi: 10.1016/j.ceramint.2006.07.005
43.
JuarezJMGJaramilloD-VCuencaCASintering comparison of NiCoCrAl-Ta powder processed by hot pressing andspark plasma. Powder Technol. 2012; 221: 264. doi: 10.1016/j.powtec.2012.01.011
44.
SerranoP-EMartinezG-HMartinezG-KDensification and microstructure of spark plasma sintered 7YSZ-Gd2O3 ceramic nano-composites. J Asian Ceram Soc. 2017; 5: 266–275. doi: 10.1016/j.jascer.2017.05.004
45.
ManièreCNigitoEDurandLSpark plasma sintering and complex shapes: The deformed interfaces approach. Powder Technol. 2017; 320: 340–345. doi: 10.1016/j.powtec.2017.07.048
46.
VoisinTMonchouxJPDurandLAn innovative Way to produce γ-TiAl blades: spark plasma sintering Adv. Eng Mater. 2015; 17 (10): 1408–1413.
47.
ArnaudCManièreCChevallierGDog-bone copper specimens prepared by one-step spark plasma sintering. J Mater Sci. 2015; 50: 7364–7373. doi: 10.1007/s10853-015-9293-5
48.
KhorKAYuLGChanSHDensification of plasma sprayed YSZ electrolytes by spark plasma sintering (SPS). Eur Ceram Soc. 2003; 23: 1855–1863. doi: 10.1016/S0955-2219(02)00421-1
49.
HeFZhangHLiuL.Study of rare-earth oxide sintering additive systems for spark plasma sintering AlN ceramics. Mater Sci Eng. 2010; A527: 5268–5272. doi: 10.1016/j.msea.2010.04.098
50.
CárdenasLCRuízJLViguerasDJSpark plasma sintering of alfa-Si3N4 ceramics with Al2O3 and Y2O3 as additives and its morphology transformation. J Alloys Compd. 2010; 501: 345–351. doi: 10.1016/j.jallcom.2010.04.102
51.
YeFHouZZhangHSpark plasma sintering of CBN/ß-SiAlON composites. Mater Sci Eng. 2010; A527: 4723–4726. doi: 10.1016/j.msea.2010.04.034
52.
MonceauDOquabDEstournesCPt-modified Ni aluminides MCrAlY-base multilayer coatings and TBC systems fabricated by spark plasma sintering for the protection of Ni-base superalloys. Surf Coat Technol. 2009; 204: 771–778. doi: 10.1016/j.surfcoat.2009.09.054
53.
BoidotMSelezneffSMonceauDProto-TGO formation in TBC systems fabricated by spark plasma sintering. Surf Coat Technol. 2010; 205: 1245–1249. doi: 10.1016/j.surfcoat.2010.09.042
54.
WangYFuZ.Study of temperature field in spark plasma sintering. Mater Sci Eng B. 2002; 90 (1-2): 34–37. doi: 10.1016/S0921-5107(01)00922-9
55.
WuYJLiJChenXMDensification and microstructures of PbTiO3 ceramics prepared by spark plasma sintering. Mater Sci Eng. 2010; A257: 5157–5160. doi: 10.1016/j.msea.2010.04.096
56.
PintB. A.HaynesJ. A.MoreK. L.WrightI. G. In: GreenKA, editors. The Use of Model Alloys to Understand and Improve the Performance of Pt-modified Aluminide Coatings. Warrendale (PA): TMS; 2004: 597–606.
57.
ZhangYLeeWYHaynesJASynthesis and cyclic oxidation behavior of a (Ni,Pt)Al coating on a desulfurized Ni-base superalloy. Met Trans A. 1999; 30A (10): 2679–2687. doi: 10.1007/s11661-999-0308-1
58.
LeyensCPintBAWrightIG.Effects of composition on the oxidation and Hot corrosion resistance of NiAl composite with precious metals. Surf Coat Technol. 2000; 133-134: 15–22. doi: 10.1016/S0257-8972(00)00878-1
59.
AudigiéPRouaix-VandeAPMaliéAObservation and modeling of α-NiPtAl and Kirkendall void formations during interdiffusion of a Pt coating with a γ-(Ni-13Al) alloy at high temperature. Surf Coat Technol. 2014; 260: 9–16. doi: 10.1016/j.surfcoat.2014.08.083
60.
WierzbaB.The kirkendall and frenkel effects during 2D diffusion process. Physica A. 2014; 413: 71–76. doi: 10.1016/j.physa.2014.06.084
61.
YangaYFJiangCYBaoZBEffect of aluminisation characteristics on the microstructure of single phase β-(Ni,Pt)Al coating and the isothermal oxidation behaviour. Corr Sci. 2016; 106: 43–54. doi: 10.1016/j.corsci.2016.01.024
62.
LiDWangLPengHCyclic oxidation behavior of β-NiAlDy alloys containing varying aluminum content at 1200°C. Progr Nat Sci Mater Int. 2012; 22 (4): 311–317. doi: 10.1016/j.pnsc.2012.06.003
63.
CadoretYBacosMPJossoPEffect of Pt additions on the sulfur segregation, void formation and oxide scale growth of cast nickel aluminides. Mater Sci Forum. 2004; 461-464: 247–254. doi: 10.4028/www.scientific.net/MSF.461-464.247
64.
PrzybylskiKYurekGJ.The influence of implanted yttrium on the mechanisms of growth of chromia scales. Mater Sci Forum. 1989; 43: 1–74. doi: 10.4028/www.scientific.net/MSF.43.1
65.
GuoHWangDZhangTCyclic oxidation of β-NiAl with various reactive element dopants at 1200 °C. Corr Sci. 2013; 66: 125–135. doi: 10.1016/j.corsci.2012.09.010
66.
EvansHE.Cracking and spalling of protective oxide layers. Mater Sci Eng A. 1989; 120-121: 139–146. doi: 10.1016/0921-5093(89)90731-4
67.
EvansHE.Stress effects in high-temperature oxidation of metals. Int Mater Rev. 1995; 40: 1–40. doi: 10.1179/imr.1995.40.1.1
68.
EvansHEDonaldsonATGilmourTC.Mechanisms of breakaway oxidation and application to a chromia-forming steel. Oxid Met (Basel). 1999; 52: 379–402. doi: 10.1023/A:1018855914737
69.
PillingNBBedworthRE.The oxidation of metals at high temperatures. J Inst Met. 1923; 29: 529–582.
70.
SchützeM.Deformation and cracking behaviour of protective oxide scales on heat resistant steels under tensile strain. Oxid Met (Basel). 1985; 24: 199–232. doi: 10.1007/BF00664232
71.
SchützeM.The healing behaviour of protective oxide scales on heat-resistant steels after cracking under tensile strain. Oxid Met (Basel). 1986; 25: 409–421. doi: 10.1007/BF01072918
72.
KarunaratneMSAKyawSJonesAModelling the coefficient of thermal expansion in Ni-based superalloys and bond coatings. J Mater Sci. 2016; 51: 4213–4226. doi: 10.1007/s10853-015-9554-3
73.
OsgerbySBerriche-BouhanekKEvansHE.Tensile cracking of a chromia layer on a stainless steel during thermal cycling with hold periods. Mater Sci Eng A. 2005; 412: 182–190. doi: 10.1016/j.msea.2005.08.193