Laboratory investigation on the condensation and corrosion rates of top of line corrosion in carbon steel: A case study from pipeline transporting wet gas in elevated temperature

Abstract

A glass cell was designed to simulate the condition for top of line corrosion encountered in wet gas transportation pipelines. Aqueous solution of 3 wt-% NaCl saturated with CO₂ at atmospheric pressure was employed. Effect of temperature gradient in the formation of condensation and its rate was investigated. API 5L Grade X65 carbon steel material was used as the working electrode for the experiment. The condensation rate was measured for the temperature gradient of 20°C, 30°C and 50°C under atmospheric condition for 24 h duration of the experiment. The corrosion rate of the specimens was measured using weight loss and Linear Polarisation Resistance (LPR) techniques. The LPR probe was immersed in the collected condensed water from the experiment to calculate the corrosion rate. The measured corrosion rate from the weight loss technique was in agreement with the corrosion rate measured from LPR. The corrosion rate measurement was repeated with the addition of 1000 ppm of pH modifying agent. This study indicates that the corrosion rate of pipeline and piping when subject to temperature gradient of 50°C and above is very high and alarming.

Keywords

Top of line corrosion volatile corrosion inhibitor pH modifier carbon steel pipeline

Get full access to this article

View all access options for this article.

References

Nyborg

Dugstad

Top of line corrosion and water condensation rate in wet gas pipeline. NACE Int. 2007; paper no. 7555.

Olsen

Dugstad

Corrosion under dewing conditions. NACE Int. 2001; paper no. 472.

Gunaltun

Larrey

Correlation of cases of top of line corrosion with calculated water condensation rates. NACE Int. 2000; paper no. 71.

Crolet

Thevenot

Dugstad

Role of free acetic acid on the CO₂ corrosion of steels. NACE International Corrosion Conference 1999; paper no. 24.

Garsany

Pletcher

Hedges

The role of acetate in CO₂ corrosion of carbon steel: has the chemistry been forgotten. NACE International Corrosion Conference 2002; paper no. 2273.

Sun

Chokshi

Nesic

A study of protective iron carbonate scale formation in CO₂ corrosion. American Institute of Chemical Engineers; 2004.

Narasaiah

VK.

Development of continuous application based corrosion inhibitors to mitigate the problems caused by top of the line corrosion in upstream oil and gas industry. Orlando, Florida(IN): NACE; 2013.

Anuar

Ismail

Raja

. Condensation rate effect of top of line corrosion on CO2. J Eng Appl Sci. 2016; 11 (20): 12058–12063.

Vitse

Gunaltun

Alam

Semi-empirical model for prediction of the top of the line corrosion risk. NACE Int. 2002; paper no. 245.

10.

Vitse

Nesic

Mechanistic model for the prediction of top of the line corrosion risk. NACE Int. 2003; paper no. 3633.

11.

Singer

Study and modeling of the localized nature of top of the line corrosion. NACE International Corrosion Conference; 2013; paper no. 7664.

12.

Punpruk

Thammachart

Gunaltun

YM.

Field testing of volatile corrosion inhibitors and batch treatment efficiency by cooled probe. NACE International Corrosion Conference; 2010.

13.

Oehler

Bailey

Gubner

RC.

Comparison of top-of-the-line corrosion test methods for generic volatile inhibitor compounds. NACE Top of Line Conference; 2012.

14.

Gunaltun

YM.

Laboratory testing of volatile corrosion inhibitor. San Antonio, Texas(TX): NACE; 2010.