The early stage atmospheric corrosion of T91 and Q235B steels exposed to Tianjin's urban atmosphere over 20 days was studied using two electrochemical probes via an electrochemical noise (EN) technique. To identify the corrosion process and the corrosion form of the two steels, EN data were analysed by statistics and wavelet transform. The results revealed that the wavelet energy of decomposed EN mainly located at high-frequency level for Q235B steel, whereas it mainly located at the low-frequency level for T91 steel. Analyses of surface images confirmed that Q235B steel underwent uniform corrosion whereas T91 steel suffered from localised corrosion. The obtained noise resistance correlated well with weight loss data.
XiaD-HMaCSongS. Atmospheric corrosion assessed from corrosion images using fuzzy kolmogorov–sinai entropy. Corros Sci. 2017. doi:10.1016/j.corsci.2017.02.015.
7.
PengAYMLyonSBThompsonGE. Comparison of cross-sectional image analysis with weight change measurements for assessing non-uniform attack during corrosion testing of aluminium. Br Corros J. 1993; 28 (2): 103–106. doi: 10.1179/bcj.1993.28.2.103
8.
YadavAPNishikataATsuruT.Electrochemical impedance study on galvanized steel corrosion under cyclic wet–dry conditions––influence of time of wetness. Corros Sci. 2004; 46 (1): 169–181. doi: 10.1016/S0010-938X(03)00130-6
9.
TheeCHaoLDongJ. Atmospheric corrosion monitoring of a weathering steel under an electrolyte film in cyclic wet–dry condition. Corros Sci. 2014; 78 (1): 130–137. doi: 10.1016/j.corsci.2013.09.008
10.
NishikataAZhuQTadaE.Long-term monitoring of atmospheric corrosion at weathering steel bridges by an electrochemical impedance method. Corros Sci. 2014; 87: 80–88. doi: 10.1016/j.corsci.2014.06.007
11.
Torres-MendozaVRodriguez-GomezFJGarcia-OchoaEM. The assessment of natural atmosphere corrosivity by the use of electrochemical noise analysis. Anti-Corros Meth Mater. 2006; 53 (6): 348–356. doi: 10.1108/00035590610711688
12.
García-OchoaEGonzález-SánchezJCorvoF. Application of electrochemical noise to evaluate outdoor atmospheric corrosion of copper after relatively short exposure periods. J Appl Electrochem. 2008; 38 (10): 1363–1368. doi: 10.1007/s10800-008-9572-9
13.
HanLSongSZhangZ.Applying electrochemical noise technique to detect the atmospheric corrosion of aluminum alloy. J Chin Soc Corros Protect. 2009; 29 (6): 471–474.
14.
GuoMDongCZhangX. Atmospheric corrosion monitoring of 2B06 aluminum alloy by electrochemical noise. Fail Anal Prev. 2010; 5 (3): 149–154.
15.
HeiMXiaD-HSongS-Z. Sensing atmospheric corrosion of carbon steel and low-alloy steel using the electrochemical noise technique: effects of weather conditions. Prot Met Phys Chem Surf. 2017.
16.
JamaliSSZhaoYGaoZ. In situ evaluation of corrosion damage using non-destructive electrochemical measurements—a case study. J Ind Eng Chem. 2016; 43: 36–43. doi: 10.1016/j.jiec.2016.07.045
17.
XiaDHSongSZBehnamianY.Detection of corrosion degradation using electrochemical noise (EN): review of signal processing methods for identifying corrosion forms. Corros Eng Sci Technol. 2016; 51 (7): 527–544.
18.
HomborgAMTingaTvan WestingEPM. A critical appraisal of the interpretation of electrochemical noise for corrosion studies. Corrosion. 2014; 70 (10): 971–987. doi: 10.5006/1277
19.
WeiY-JXiaD-HSongS-Z.Detection of SCC of 304 NG stainless steel in an acidic NaCl solution using electrochemical noise based on chaos and wavelet analysis. Russ J Electrochem. 2016; 52 (6): 560–575. doi: 10.1134/S1023193516060124
20.
ShahidiMHosseiniSMAJafariAH.Comparison between ED and SDPS plots as the results of wavelet transform for analyzing electrochemical noise data. Electrochim Acta. 2011; 56 (27): 9986–9997. doi: 10.1016/j.electacta.2011.08.091
21.
BahramiMJShahidiMHosseiniSMA.Comparison of electrochemical current noise signals arising from symmetrical and asymmetrical electrodes made of Al alloys at different pH values using statistical and wavelet analysis. Part I: neutral and acidic solutions. Electrochim Acta. 2014; 148: 127–144. doi: 10.1016/j.electacta.2014.10.031
22.
HomborgAMTingaTZhangX. Transient analysis through Hilbert spectra of electrochemical noise signals for the identification of localized corrosion of stainless steel. Electrochim Acta. 2013; 104 (0): 84–93. doi: 10.1016/j.electacta.2013.04.085
BertocciUHuetFNogueiraRP. Drift removal procedures in the analysis of electrochemical noise. Corrosion. 2002; 58 (4): 337–347. doi: 10.5006/1.3287684
25.
XiaD-HBehnamianY.Electrochemical noise: a review of experimental setup, instrumentation and DC removal. Russ J Electrochem. 2015; 51 (7): 593–601. doi: 10.1134/S1023193515070071
26.
HomborgAMTingaTZhangX. Time–frequency methods for trend removal in electrochemical noise data. Electrochim Acta. 2012; 70: 199–209. doi: 10.1016/j.electacta.2012.03.062
27.
XiaDHSongSZWangJH. Determination of corrosion types from electrochemical noise by phase space reconstruction theory. Electrochem. Commun. 2012; 15 (1): 88–92. doi: 10.1016/j.elecom.2011.11.032