This study compares the hot corrosion performance of yttria-stabilised zirconia (7YSZ), and 7YSZ + Gd2O3 composite samples in the presence of molten mixture of Na2SO4 + V2O5 at 1150°C. For 7YSZ, the reaction between NaVO3 and Y2O3 produces YVO4 and leads the transformation of tetragonal ZrO2 to monoclinic ZrO2. A high-density in sintered 7YSZ + Gd2O3 samples, led minor amounts of monoclinic ZrO2 and tetragonal GdVO4 as the hot corrosion products with only traceable amounts of YVO4, and a stable corroded layer was formed. Due to the synergic effect of doping of zirconia with Gd2O3, the 7YSZ + Gd2O3 sample has a much better hot corrosion crack resistance than 7YSZ.
LeviCG. Emerging materials and processes for thermal barrier systems. Curr Opin Solid State Mater Sci.2004; 8: 77–91. doi: 10.1016/j.cossms.2004.03.009
6.
XieLDorfmanMrCipitriaA. Properties and performance of high-purity thermal barrier coatings. J Thermal Spray Technol. 2007; 16: 804–808. doi: 10.1007/s11666-007-9079-7
ChenXZhaoYGuL. Hot corrosion behaviour of plasma sprayed YSZ/LaMgAl11O19 composite coatings in molten sulfate-vanadate salt. Corros Sci. 2011; 53: 2335–2343. doi: 10.1016/j.corsci.2011.03.019
9.
SreedharGRajaVS. Hot corrosion of YSZ/Al2O3 dispersed NiCrAlY plasma-sprayed coatings in Na2SO4–10 wt.% NaCl melt. Corros Sci. 2010; 52: 2592–2602. doi: 10.1016/j.corsci.2010.04.007
10.
RaghavanSWangHDinwiddieRB. Ta2O5/Nb2O5 and Y2O3 Co-doped zirconias for thermal barrier coatings. J Am Ceram Soc. 2004; 87: 431–437. doi: 10.1111/j.1551-2916.2004.00431.x
11.
MaloneyMJ. Thermal barrier coating systems and materials. U.S. Patent No. 6 284 323. 2001.
12.
SureshGSeenivasanGKrishnaiahMV. Investigation of the thermal conductivity of selected compouds of Gadolinium and Lathanium. J Nucl Mater. 1997; 249: 259–261. doi: 10.1016/S0022-3115(97)00235-3
13.
WangCWangYChengY. Preparation and thermophysical properties of nano-sized Ln2Zr2O7 (Ln5La, Nd, Sm, and Gd) ceramics with pyrochlore structure. J Mater Sci. 2012; 47: 4392–4399. doi: 10.1007/s10853-012-6293-6
14.
GuoLLiMZhangY. Improved toughness and thermal expansion of non-stoichiometry Gd2-xZr2+xO7+x/2 ceramics for thermal barrier coating application. J Mater Sci Technol. 2016; 32 (1): 28–33. doi: 10.1016/j.jmst.2015.11.022
15.
WangCMGuoLZhangY. Enhanced thermal expansion and fracture toughness of Sc2O3-doped Gd2Zr2O7 ceramics. Ceram Int. 2015; 41: 10730–10735. doi: 10.1016/j.ceramint.2015.05.008
16.
KuttyKVGRajagopalanSMathewsCK. Thermal expansion behaviour of some rare earth oxide pyrochlores. Mate Res Bull. 1994; 29: 759–766. doi: 10.1016/0025-5408(94)90201-1
17.
LiuZGOuyangJHZhouY. Preparation and thermophysical properties of (NdxGd1-x)2Zr2O7 ceramics. J Mater Sci. 2008; 43: 3596–3603. doi: 10.1007/s10853-008-2570-9
18.
LiuZhan-GuoOuyangJia-HuZhouYu. Influence of gadolinia on thermal expansion property of ZrO2–4.5 mol%Y2O3 ceramics. J Alloys Compd. 2009; 473 (1-2): L17–L19. doi: 10.1016/j.jallcom.2008.05.053
19.
QuZXWanCLPanW. Thermal expansion and defect chemistry of MgO-doped Sm2Zr2O7. Chem Mater. 2007; 19: 4913–4918. doi: 10.1021/cm071615z
20.
WangLWangYSunXG. Finite element simulation of residual stress of double-ceramic-layer La2Zr2O7/8YSZ thermal barrier coatings using birth and death element technique. Comput Mater Sci. 2012; 53 (1): 117–127. doi: 10.1016/j.commatsci.2011.09.028
21.
WangLWangYSunXG. Thermal shock behavior of 8YSZ and double-ceramic-layer La2Zr2O7/8YSZ thermal barrier coatings fabricated by atmospheric plasma spraying. Ceram Int. 2012; 38 (5): 3595–3606. doi: 10.1016/j.ceramint.2011.12.076
Flores FerreyraC. Efecto de la adicion de Gd2O3 en 7YSZ (t’) y su desempeño en corrosion seca [master's thesis]. Mexico; 2016 A140309.
24.
LiSLiuZ-GOuyangJ-H. Hot corrosion behaviour of Yb2Zr2O7 ceramic coated with V2O5 at temperatures of 600-800°C in air. Corros Sci. 2010; 52: 3568–3572. doi: 10.1016/j.corsci.2010.06.007
25.
AnstisGRChantikulPLawnBR. A critical evaluation of indentation techniques for measuring fracture toughness: I. Direct crack measurements. J Am Ceram Soc. 1981; 64: 533–538. doi: 10.1111/j.1151-2916.1981.tb10320.x
26.
DonzelLRobertsSG. Microstructure and mechanical properties of cubic zirconia (8YSZ)/SiC nanocomposites. J Eur Ceram Soc. 2000; 20: 2457–2462. doi: 10.1016/S0955-2219(00)00117-5
27.
GogotsiGADubSNLomonovaEE. Vickers and knoop indentation behaviour of cubic and partially stabilized zirconia crystals. J Eur Ceram Soc. 1995; 15: 405–413. doi: 10.1016/0955-2219(95)91431-M
28.
AfrasiabiASaremiMKobayashiA. A comparative study on hot corrosion resistance of three types of thermal barrier coatings: YSZ, YSZ+Al2O3 and YSZ/Al2O3. Mater Sci Eng A-Struct. 2008; 478: 264–269. doi: 10.1016/j.msea.2007.06.001
29.
HabibiMHWangLGuoSM. Evolution of hot corrosion resistance of YSZ, Gd2Zr2O7 and Gd2Zr2O7+YSZ composite thermal barrier coatings in Na2SO4 + V2O5 at 1050°C. J Eur Ceram Soc. 2012; 32: 1635–1642. doi: 10.1016/j.jeurceramsoc.2012.01.006
30.
ParkSYKimJHKimMC. Microscopic observation of degradation behavior in yttria and ceria stabilized zirconia thermal barrier coatings under hot corrosion. Surf Coat Technol.2005; 190: 357–365. doi: 10.1016/j.surfcoat.2004.04.065
31.
ChenZMabonJWenJ-G. Degradation of plasma-sprayed yttria stabilized zirconia coatings via ingress of vanadium oxide. J Eur Ceram Soc. 2009; 29: 1647–1656. doi: 10.1016/j.jeurceramsoc.2008.10.003
32.
JonesRLWilliamsCE. Hot corrosion studies of zirconia ceramics. Surf Coat Technol.1987; 32: 349–358. doi: 10.1016/0257-8972(87)90119-8
33.
JonesRL. Vanadate-sulfate melt thermochemistry relating to hot corrosion of thermal barrier coatings. Naval Res Lab. 1997: 1–23.
34.
ChenZSpeakmanSHoweJ. Investigation of reactions between vanadium oxide and plasma-sprayed yttria-stabilized zirconia coatings. J Eur Ceram Soc. 2009; 29: 1403–1411. doi: 10.1016/j.jeurceramsoc.2008.09.016
JonesRL. Some aspects of the hot corrosion of thermal barrier coatings. J Therm Spray Technol. 1997; 6: 77–84. doi: 10.1007/BF02646315
37.
CarreARogerFVarinotC. Study of acid/base properties of oxide, oxide glass, and glass-ceramic surfaces. J Colloid Interface Sci. 1992; 154: 174–183. doi: 10.1016/0021-9797(92)90090-9
38.
JonesRLWilliamsCEJonesSR. Reaction of vanadium compounds with ceramic oxides. J. Electrochem Soc. 1986; 133 (1): 227–230. doi: 10.1149/1.2108530
39.
XuZHeLMuR. Hot corrosion behavior of rare earth zirconates and yttria partially stabilized zirconia thermal barrier coatings. Surf Coat Technol.2010; 204: 3652–3661. doi: 10.1016/j.surfcoat.2010.04.044
40.
LiSLiuZ-GOuyangJ-H. Study on hot corrosion reactions between SmYbZr2O7 ceramic and vanadium pentoxide at temperatures of 600-1000°C in air. Mater Chem Phys. 2011; 130: 1134–1138. doi: 10.1016/j.matchemphys.2011.08.044
41.
LiSLiuZGOuyangJH. Hot corrosion of (Sm1−xYbx)2 Zr2O7 (x=0, 0.5, 1.0) ceramics against V2O5 molten salt in air at 800°C. Int J Appl Ceram Technol. 2012; 9(1):149-158.
42.
MarpleBRVoyerJThibodeauM. Hot Corrosion of lanthanum zirconate and partially stabilized zirconia thermal barrier coatings. J Eng Gas Turbine Power. 2006; 128: 144–152. doi: 10.1115/1.1924534