In this study, solution grade styrene–butadiene rubber (SSBR) compound was prepared by partial replacement of silica with lignin. The compounds were designed and optimised using an L9 orthogonal array (using Taguchi method) targeting ‘magic triangle’. Cure rate index (CRI), reinforcement index (RI) and hysteresis loss (loss tangent at 60°C) were considered as the responses. Thermo-gravimetric analysis and Differential scanning calorimeter is used to assess thermal degradation and intramolecular reactivity of lignin. Morphological analysis of the composites has instituted the fact that above 20% replacement of synthetic silica by lignin results in re-agglomeration of filler particles due to inferior dispersion. Response analysis through ANOVA coupled with an experimental study on physico-mechanical and dynamic-mechanical properties has manifested that SSBR with 58% vinyl content with 40:10 silica: lignin compounded at 160°C with 10% silane coupling agent (SCA) with respect to silica at factorial levels furnished a ‘magic triangle’ optimised tyre tread compound.
Abdelaal MRMA.Green mobility as an approach for sustainable urban planning. Int J Innov Res Sci Eng Technol. 2015; 4 ( 8 ): 6949–6959.
2.
PereraF.Pollution from fossil-fuel combustion is the leading environmental threat to global pediatric health and equity: solutions exist. Int J Environ Res Public Health. 2018; 15 ( 1 ).
3.
KrzyzanowskiBK-D M, JS. ( 2005 ). Health effects of transport-related air pollution.
4.
PeterM.Dr. ( 2013 ). Reducing CO2 and fuel consumption from new cars: assessing the near-term technology potential in the EU.
5.
DasS, RedrouthuB. ( 2014 ). Tyre modelling for rolling resistance.
6.
ChowdhurySG, PalK, SatpathiH, Improving hysteresis of a typical carbon black-filled natural rubber tread compound by using a novel coupling agent. Prog Rubber, Plast Recycl Technol. 2019; ( 437 ).
7.
ZaeimoedinTZ, ClarkeJ.Improving the abrasion resistance of “green” tyre compounds. Proc World Congr Mech Chem Mater Eng. 2017: 1–6.
8.
KernWJ, FutamuraS.Effect of tread polymer structure on tyre performance. Polymer (Guildf). 1988; 29 ( 10 ): 1801–1806.
9.
ThaptongP, Sae-OuiP, SirisinhaC.Influences of styrene butadiene rubber and silica types on performance of passenger car radial tire tread. Rubber Chem Technol. 2017; 90 ( 4 ): 699–713.
10.
HamannE, LeHH, RaduschH-J.Styrene and vinyl content of styrene butadiene rubber – dispersion and phase specific distribution of carbon black in SSBR/NR blends. Kautsch Gummi Kunstst. 2011; 03: 33–38.
11.
KimE, LeeE, ParkI, End functionalization of styrene-butadiene rubber with poly(ethylene glycol)-poly(dimethylsiloxane) terminator. Polym J. 2002; 34 ( 9 ): 674–681.
12.
PogodaevAK, Karmanova OV, Firsova AV, Synthesis and properties of functionalized styrene-butadiene rubbers. J Chem Technol Metall. 2019; 54 ( 6 ): 1137–1140.
13.
BerkiP, GöblR, Karger-KocsisJ.Structure and properties of styrene-butadiene rubber (SBR) with pyrolytic and industrial carbon black. Polym Test. 2017; 61 ( May ): 404–415.
14.
ManoharanP, AnaghaMG, ChandradasN, Influence of different specific surface area of highly dispersible silica and interfacial characteristics of green elastomer composites. Rubber Chem Technol. 2018; 91 ( 3 ): 548–560.
15.
KutsovskyY, CorporationC, ZhangP, Using carbon-silica dual phase filler. Kautsch Gummi Kunstst. 2002; ( January ).
16.
EgwaikhideP, AkporhonorE, OkieimenF.Effect of coconut fibre filler on the cure characteristics physicomechanical and swelling properties of natural rubber vulcanisates. Int J Phys Sci. 2007; 2 ( 2 ): 39–46.
17.
NordinR. M.Properties of rice husk powder/natural rubber composite. Solid State Sci Technol. 2007; 15 ( 2 ): 15–16.
18.
ChigondoF, ShokoP, NyamundaBC, Maize stalk as reinforcement In natural rubber composites. Maize Stalk As Reinf Nat Rubber Compos. 2013; 2 ( 6 ): 263–271.
19.
OSABOHIENE, EGBOHSHO.Cure characteristics and physico-mechanical properties of natural rubber filled with seeds chell of cherry.pdf. J Appl Sci Environ Manag. 2007; 11 ( 2 ): 43–48.
20.
Aini NAM, OthmanN, HussinMH, Lignin as alternative reinforcing filler in the rubber industry: a review. Front Mater. 2020; 6 ( January ).
21.
BahlK, MiyoshiT, JanaSC.Hybrid fillers of lignin and carbon black for lowering of viscoelastic loss in rubber compounds. Polymer (Guildf. 2014; 55 ( 16 ): 3825–3835.
22.
BahlK, SwansonN, PughC, Polybutadiene-g-polypentafluorostyrene as a coupling agent for lignin-filled rubber compounds. Polymer (Guildf ). 2014; 55 ( 26 ): 6754–6763.
23.
TenE, VermerrisW.Recent developments in polymers derived from industrial lignin. J Appl Polym Sci. 2015; 132 ( 24 ): 1–13.
24.
BahlK, JanaSC.Surface modification of lignosulfonates for reinforcement of styrene-butadiene rubber compounds. J Appl Polym Sci. 2014; 131 ( 7 ): 1–9.
25.
GregorováA, KošíkováB, MoravčíkR.Stabilization effect of lignin in natural rubber. Polym Degrad Stab. 2006; 91 ( 2 ): 229–233.
26.
BulaK, Łukasz KlapiszewskiTJ.A Novel functional silica/lignin hybrid material as a potential bio-based polypropylene filler karol. Polym Polym Compos. 2015; 36 ( 2 ): 913–922.
27.
JiangC, HeH, YaoX, In situ dispersion and compatibilization of lignin/epoxidized natural rubber composites: reactivity, morphology and property. J Appl Polym Sci. 2015; 132 ( 23 ): 1–10.
28.
JiangC, HeH, YaoX, The aggregation structure regulation of lignin by chemical modification and its effect on the property of lignin/styrene–butadiene rubber composites. J Appl Polym Sci. 2018; 135 ( 5 ): 1–11.
29.
CetinZ, AytacA, DenizV, Investigation into the effects of process parameters on tire: cord adhesion by Taguchi experimental design method. KGK Kautschuk Gummi Kunststoffe. 2010; 63 ( 6 ): 255–258.
30.
FeiNC, MehatNM, KamaruddinS.Practical applications of Taguchi method for Optimization of Processing parameters for plastic injection moulding: a retrospective review. ISRN Ind Eng. 2013; 2013: 1–11.
31.
AthreyaS, VenkateshYD.Application of Taguchi method for optimization of process parameters in improving the surface roughness of lathe facing operation. Int Ref J Eng Sci. 2012; 1 ( 3 ): 13–19.
32.
LuY, LuYC, HuHQ, Structural characterization of lignin and its degradation products with spectroscopic methods. J Spectrosc. 2017; 2017.
33.
RodriguesJ, FaixO, PereiraH. Determination of lignin content of eucalyptus globulus wood using FTIR spectroscopy. Holzforschung. 1998; 52: 46–50.
34.
SantosK, NunesD, PardiniLC.Methods for lignin biomass as a potential precursor for carbon materials. Cellul Chem Technol. 2019; 53 ( 3-4 ): 227–242.
35.
LiD-L, GeS-B, PengW-X, Chemical structure characteristics of wood/lignin composites during mold pressing. Polym Polym Compos. 2015; 16 ( 2 ): 101–113.
36.
KhannaR, Ikram-Ul-HaqM, RajaraoR, Novel multidimensional carbons from structural transformations of waste lignin: a low temperature pyrolysis investigation. Fuel Process Technol. 2017; 166: 312–321.
HuaJ, LiuK, WangZ, Effect of vinyl and phenyl group content on the physical and dynamic mechanical properties of HVBR and SSBR. J Appl Polym Sci. 2018; 135 ( 12 ): 1–8.
39.
GhoshS, JagannathC, GhoshS.Impact of adhesive ingredients on adhesion between rubber and brass-plated steel wire in tire. Polym Eng Sci. 2020; ( May ): 1–11.
40.
JeongHH, JinHH, HaSH, The effect of silane addition timing on mixing processability and properties of silica reinforced rubber compound. AIP Conf Proc. 2016; ( March ): 1713.
41.
ZhuL, TianX, PanY, Optimization of serial modular continuous mixing process parameters for natural rubber composites reinforced by silica/carbon black. Polymers (Basel). 2020; 12 ( 2 ).
42.
MishraPK, EkielskiA.The self-assembly of lignin and its application in nanoparticle synthesis: a short review. Nanomaterials. 2019; 9 ( 2 ): 1–15.
43.
ThielemansW, WoolRP.Kraft lignin as fiber treatment for natural fiber-reinforced composites. Polym Compos. 2005; 26 ( 5 ): 695–705.
44.
ChoiSS, KimIS, LeeSG, Filler-polymer interactions of styrene and butadiene units in silica-filled styrene-butadiene rubber compounds. J Polym Sci Part B Polym Phys. 2004; 42 ( 4 ): 577–584.
45.
JinJ, NoordermeerJWM, DierkesWK, The effect of silanization temperature and time on the marching modulus of silica-filled tire tread compounds. Polymers (Basel. 2020; 12 ( 1 ).
46.
MiharaS. ( 2009 ). Reactive processing of silica-reinforced tire rubber: new insight into the time- and temperature-dependence of silica rubber interaction.
47.
WarasitthinonN, RobertsonCG.Interpretation of the tand peak height for particle-filled rubber and polymer nanocomposites with relevance to tire tread performance balance. Rubber Chem Technol. 2018; 91 ( 3 ): 577–594.