The objective of the present work is to investigate mode I and mode II delamination behaviour of chopped strand mat (CSM) E-glass reinforced vinyl ester (VE) composite. Double cantilever beam and end notched flexure tests were carried out to evaluate the mode I and mode II delamination, respectively. The fracture toughnesses were calculated using the experimental calibration method. Results showed that the average mode I and mode II fracture toughnesses were 185 and 2386 N m−1, respectively. Furthermore, the mode II–mode I ratio for this material was 12.9. This value was the highest when compared with other composite materials from the literature. Finally, through scanning electron micrographs, the dominant failure mechanisms were found to be matrix cracking, fibre debonding and fibre breakage. In addition, shear cusps were observed in mode II specimen, which signified the shearing between the layers.
TuronA, CamanhoPP, CostaJ, A damage model for the simulation of delamination in advanced composites under variable-mode loading. Mech Mater. 2006;38:1072–1089. doi: 10.1016/j.mechmat.2005.10.003
2.
ZhaoY, LiuW, SeahLK, Delamination growth behavior of a woven E-glass/bismaleimide composite in seawater environment. Compos Part B Eng. 2016;106:332–343. doi: 10.1016/j.compositesb.2016.09.045
3.
PaganoNJ, SchoeppnerGA.Delamination of polymer matrix composites: problems and assessment. In: KellyA, ZwebenC, editor. Comprehensive composite materials. Oxford: Pergamon; 2000. p. 433–528.
4.
HeckadkaSS, NayakSY, NarangK, Chopped strand/plain weave E-glass as reinforcement in vacuum bagged epoxy composites. J Mater. 2015;2015:1–7. Article ID 957043. doi: 10.1155/2015/957043
5.
PanneerselvamC, Gopala KrishnanM, Gaudham BabuS.Analysis of particle influence on energy release rate of CSM E-glass/epoxy composite laminates. Int J Mater Sci Eng. 2016;4:24–34.
6.
JacobGC, StarbuckJM, FellersJF, Fracture toughness in random-chopped fiber-reinforced composites and their strain rate dependence. J Appl Polym Sci. 2006;100:695–701. doi: 10.1002/app.23414
LindgrenM, WallinM, KakkonenM, The influence of high-temperature sulfuric acid solution ageing on the properties of laminated vinyl-ester joints. Int J Adhes Adhes. 2016;68:298–304. doi: 10.1016/j.ijadhadh.2016.04.011
9.
AfsharA, LiaoH-T, ChiangF-p, Time-dependent changes in mechanical properties of carbon fiber vinyl ester composites exposed to marine environments. Compos Struct. 2016;144:80–85. doi: 10.1016/j.compstruct.2016.02.053
10.
Wee Tee Tong Chemicals. Vinyl ester resin SR-825, technical datasheet.
11.
JoharM, IsrarHA, LowKO, Numerical simulation methodology for mode II delamination of quasi-isotropic quasi-homogeneous composite laminates. J Compos Mater. 2017;51:3955–3968. doi: 10.1177/0021998317695414
12.
IrwinGR, KiesJA.Critical energy rate analysis of fracture strength. Weld J Res Suppl. 1954;33:193–198.
13.
DavidsonBD, KumarM, SoffaMA.Influence of mode ratio and hygrothermal condition on the delamination toughness of a thermoplastic particulate interlayered carbon/epoxy composite. Compos Part A Appl S. 2009;40:67–79. doi: 10.1016/j.compositesa.2008.10.006
14.
FuS-Y, LaukeB.Fracture resistance of unfilled and calcite-particle-filled ABS composites reinforced by short glass fibers (SGF) under impact load. Compos Part A Appl S. 1998;29:631–641. doi: 10.1016/S1359-835X(97)00111-5
15.
WongKJ, LowKO, IsrarHA.Impact resistance of short bamboo fibre reinforced polyester concretes. P I Mech Eng L-J Mat. 2017;231(8):683–692.
16.
WongKJ, GongXJ, AivazzadehS, Delamination behaviour of carbon/epoxy composites. In: WongKJ, AhmadZ, editor. Structural composites: mechanical properties and behaviour. Malaysia: UTM Press; 2017. p. 33–48.
GoutianosS, PeijsT, NystromB, Development of flax fibre based textile reinforcements for composite applications. Appl Compos Mater. 2006;13:199–215. doi: 10.1007/s10443-006-9010-2
ChenH, WangJ, NiA, Effect of an intumescent flame retardant on the fracture toughness (mode I), thermal, and flame-retardant properties of continuous glass fibre-reinforced polypropylene composites. Plast, Rubber Compos. 2018;47:113–121. doi: 10.1080/14658011.2018.1442765
21.
SajithS, ArumugamV, DhakalHN.Effects of curing pressure on mode II fracture toughness of uni-directional GFRP laminates. Polym Test. 2015;48:59–68. doi: 10.1016/j.polymertesting.2015.09.011
22.
NaghipourP, BartschM, ChernovaL, Effect of fiber angle orientation and stacking sequence on mixed mode fracture toughness of carbon fiber reinforced plastics: numerical and experimental investigations. Mater Sci Eng A. 2010;527:509–517. doi: 10.1016/j.msea.2009.07.069
23.
BensadounF, VerpoestI, Van VuureAW.Interlaminar fracture toughness of flax-epoxy composites. J Reinf Plast Compos. 2016;36:121–136. doi: 10.1177/0731684416672925
24.
PanY, WuG, ChengX, Mode I and mode II interlaminar fracture toughness of CFRP/magnesium alloys hybrid laminates. Compos Interface. 2016;23:453–465. doi: 10.1080/09276440.2016.1144911
25.
SampathPS, MurugesanV, SarojadeviM, Mode I and mode II delamination resistance and mechanical properties of woven glass/epoxy–PU IPN composites. Polym Compos. 2008;29:1227–1234. doi: 10.1002/pc.20371
26.
GongXJ, WongKJ, TaminMN.Moisture absorption effects on interlaminar fracture toughness of woven glass/epoxy composite laminates. In: TaminMN, editor. Damage and fracture of composite materials and structures, advanced structured materials. Berlin, Heidelberg: Springer; 2012. p. 107–129.
27.
SacchettiF, GrouveWJB, WarnetLL, Interlaminar fracture toughness of 5HS carbon/PEEK laminates. A comparison between DCB, ELS and mandrel peel tests. Polym Test. 2018;66:13–23. doi: 10.1016/j.polymertesting.2017.12.005
28.
ReisPNB, FerreiraJAM, CostaJDM, Interlaminar fracture in woven carbon/epoxy laminates. Frattura ed Integrita Strutturale. 2014;30:431–437. doi: 10.3221/IGF-ESIS.30.52
29.
ZhengN, HuangY, LiuH-Y, Improvement of interlaminar fracture toughness in carbon fiber/epoxy composites with carbon nanotubes/polysulfone interleaves. Compos Sci Technol. 2017;140:8–15. doi: 10.1016/j.compscitech.2016.12.017
30.
NaghipourP, SchneiderJ, BartschM, Fracture simulation of CFRP laminates in mixed mode bending. Eng Fract Mech. 2009;76:2821–2833. doi: 10.1016/j.engfracmech.2009.05.009
31.
BonhommeJ, ArgüellesA, ViñaJ, Fractography and failure mechanisms in static mode I and mode II delamination testing of unidirectional carbon reinforced composites. Polym Test. 2009;28:612–617. doi: 10.1016/j.polymertesting.2009.05.003
32.
MathewsMJ, SwansonSR.Characterization of the interlaminar fracture toughness of a laminated carbon/epoxy composite. Compos Sci Technol. 2007;67:1489–1498. doi: 10.1016/j.compscitech.2006.07.035
33.
LeBlancLR, LaPlanteG.Experimental investigation and finite element modeling of mixed-mode delamination in a moisture-exposed carbon/epoxy composite. Compos Part A-Appl S. 2016;81:202–213. doi: 10.1016/j.compositesa.2015.11.017
34.
JoharM, WongKJ, TaminMN.Mixed-mode delamination failures of quasi-isotropic quasi-homogeneous carbon/epoxy laminated composite. In: AliA, editor. Failure analysis and prevention. Rijeka: InTech; 2017. p. 33–45.
35.
JohannessonT, SjöblomP, SeldénR.The detailed structure of delamination fracture surfaces in graphite/epoxy laminates. J Mater Sci. 1984;19:1171–1177. doi: 10.1007/BF01120026