The effect of galvannealed (GA) coating on the corona bond strengths of resistance spot welding joints was investigated. A cross tensile test was performed with removal of the nugget, using GA steel sheets and steel sheets whose coating had been removed via pickling. The maximum load with coating was lower than that without coating. When the nugget diameter was small (3√t, t: sheet thickness), GA coating reduced the corona bond strength (MPa). In contrast, when the nugget diameter was large (5√t), GA coating did not change the corona bond strength but reduced the corona bond area.
BayN.Cold pressure welding-the mechanisms governing bonding. Trans ASME J Eng Ind. 1979; 101(2):121–127.
3.
PouranvariM, AsgariHR, MosavizadchSM, Effect of weld nugget size on overload failure mode of resistance spot welds. Sci Technol Weld Joining. 2007; 12(3):217–225.
4.
SadasyeT, IgiS, TaniguchiK, Fracture behaviour and numerical study of resistance spot welded joints in high strength steel sheet. Weld Int. 2016; 30(8):502–613.
5.
MaY, TakikawaA, NakanishiJ, Measurement of local material properties and failure analysis of resistance spot welds of advanced high-strength steel sheets. Mater Des. 2021; 201:109505.
6.
MatsuiS, WakabayashiC, KodamaS.Effect of gap between steel sheet and electrode on resistance spot welding. Mater Sci Forum. 2018; 941:158–163.
7.
ChenT, LingZ, WangM, Effect of a slightly concave electrode on resistance spot welding of Q&P1180 steel. J Mater ProcessTechnol. 2020; 285:116797.
8.
MatsudaK, KodamaS.Evaluation of corona bond strength of resistance spot welding. Sci Technol Weld Joining. 2020; 25(1):66–72.
9.
GedeonSA, EagarTW.Resistance spot welding of galvanized steel: Part I. Material variations and process modifications. Metall Trans B. 1986; 17:879–885.
10.
GedeonSA, EagarTW.Resistance spot welding of galvanized steel: Part II. Mechanisms of spot weld nugget formation. Metall Trans B. 1986; 17:887–901.
11.
GoodarziM, MarashiSPH, PouranvariM.Dependence of overload performance on weld attributes for resistance spot welded galvanized low carbon steel. J Mater ProcessTechnol. 2009; 209(9):4379–4384.
12.
BöhneC, MeschutG, BieglerM, Prevention of liquid metal embrittlement cracks in resistance spot welds by adaption of electrode geometry. Sci Technol Weld Joining. 2020; 25(4):303–310.
13.
MahabunphachaiS, KoçM, NiJ.Pressure welding of thin sheet metals: experimental investigations and analytical modeling. J Manuf Sci Eng. 2009; 131(4):041003.