The circular-patch welding test was used to study the liquation and liquation cracking of AZ-series Mg alloys. A heat treatment was carried out on the as-received AZ91 alloy to dissolve the γ(Mg17Al12) particles before welding. The circular-patch welding test was then conducted on the heat-treated, as-received AZ91 alloy using AZ61 and AZ91 filler wires. The results showed that the susceptibility of AZ91 alloy to liquation and liquation cracking was significantly reduced by the dissolution of massive γ(Mg17Al12) particles via a heat treatment before welding as the liquation mechanism was changed. Both constitutional liquation and incipient melting occurred in the partially melted zone of the as-received AZ91 welds, while only incipient melting occurred in the heat-treated AZ91 welds.
KainerKU.Challenges for implementation of magnesium into more applications. In: SinghA, SolankiK, ManuelMV, editors. Magnesium technology. New York, United States: Springer-Verlag; 2016. p. 5–6.
2.
Sameer KumarD, Tara SasankaC, RavindraK, Magnesium and its alloys in automotive applications: a review. Am J Mater Sci Technol. 2015; 4:12–30.
3.
ChenS, WangX, YuanT, Research on prediction method of liquation cracking susceptibility to magnesium alloy welds. Acta Metall Sinica. 2018; 54:1735–1744.
4.
HassaniB, KarimzadehF, EnayatiMH, Effect of friction stir processing on microstructure and mechanical properties of AZ91C magnesium cast alloy weld zone. J. Mater Eng Perform. 2016; 25:2776–2785. doi: 10.1007/s11665-016-2129-x
5.
CaoX, JahaziM, ImmarigeonJP, A review of laser welding techniques for magnesium alloys. J Mat Proc Technol. 2006; 171:188–204. doi: 10.1016/j.jmatprotec.2005.06.068
6.
LiuL.Welding and joining of magnesium alloys. Cambridge: Woodhead Publishing; 2012.
7.
YuZ, YanHG, YinXY, Liquation cracking in laser beam welded joint of ZK60 magnesium alloy. Trans Nonferrous Met Soc China. 2012; 22:2891–2897. doi: 10.1016/S1003-6326(11)61547-1
8.
YuanT, ChaiX, LuoZ, Predicting susceptibility of magnesium alloys to weld-edge cracking. Acta Mater. 2015; 90:242–251. doi: 10.1016/j.actamat.2015.02.031
9.
SunDQ, LangB, SunDX, Microstructures and mechanical properties of resistance spot welded magnesium alloy joints. Mater Sci Eng A. 2007; 460:494–498. doi: 10.1016/j.msea.2007.01.073
10.
HorieS, ShinozakiK, YamamotoM, Effect of microstructure on liquation cracking during AZ91 friction stir spot welding. Sci Technol Weld Join. 2010; 15:671–675. doi: 10.1179/136217110X12720264008439
11.
HuangCJ, ChengCM, ChouCP, Hot cracking in AZ31 and AZ61 magnesium alloy. J Mater Sci Technol. 2011; 27:633–640. doi: 10.1016/S1005-0302(11)60118-7
12.
PepeJJ, SavageWF.Effects of constitutional liquation in 18-Ni maraging steel weldment. Weld J. 1967; 46:411s–422s.
13.
PepeJJ, SavageWF.The heat affected zone of the 18-Ni maraging steels. Weld J. 1970; 49:545s.
14.
LippoldJC, Welding metallurgy and weld ability. Hoboken (NJ): Wiley; 2015. p. 53–58, 376.
15.
MassalskiTB, MurrayJL, BennettLH, Binary alloy phase diagrams. Metals Park (OH): American Society for Metals; 1986. p. 1565.
16.
AdamiekJ, KierzekA.Influence of heat treatment on susceptibility to hot cracking of magnesium alloy EN-MCMgRE3Zn2Zr. Archives Metall Mater. 2010; 55:69–78.
17.
QianM, LippoldJC.The effect of annealing twin-generated special grain boundaries on HAZ liquation cracking of nickel-base superalloys. Acta Mater. 2003; 51:3351–3361. doi: 10.1016/S1359-6454(03)00090-9
18.
PakniatM, Malek GhainiF, TorkamanyMJ.Effect of heat treatment on liquation cracking in continuous fiber and pulsed Nd:YAG laser welding of HASTELLOY X alloy. Metall Mater Trans A. 2017; 48:5387–5395. doi: 10.1007/s11661-017-4300-x
19.
StevensonA.Metals handbook. Materials Park (OH): ASM International; 4(1989), p. 899.
20.
LuoA.Processing, microstructure and mechanical behavior of cast magnesium metal matrix composites. Metall Mater Trans A. 1995; 26:2445–2455. doi: 10.1007/BF02671259
Electron AZ31B Sheet. Plate & Coil, Data Sheet 482, Magnesium Electron, Manchester, England.
23.
MohammadiJ, GhoreishiM, BehnamianY.An investigation into the dissolution characteristics of γ precipitates in Mg-3Al-Zn alloy. Mater Res. 2014; 17:996–1002. doi: 10.1590/1516-1439.261814
24.
ZhuT, ChenZW, GaoW.Incipient melting in partially melted zone during arc welding of AZ91D magnesium alloy. Mater Sci Eng A. 2006; 416:246–252. doi: 10.1016/j.msea.2005.10.032
25.
HuangC, KouS.Partially melted zone in aluminum welds – planar and cellular solidification. Weld J. 2001; 80:46–53.
26.
KouS.Fluid flow and solidification in welding: three decades of fundamental research at the University of Wisconsin. Weld J. 2012; 91:287–302.