Mitigation of thermal distortion in wire arc additively manufactured Ti6Al4V part using active interpass cooling

Abstract

In this study, active interpass cooling using compressed CO₂ was innovatively employed in the wire arc additively manufactured Ti6Al4V process with the aim of mitigating part distortion. A comparative analysis between simulation and experimental results was performed to explore the effects of active interpass cooling on the thermal behaviours, geometric features and distortion levels of deposit. The results show that active interpass cooling with CO₂ gas is an effective means of reducing Wire arc additive manufacturing (WAAM)-part distortion by increasing heat dissipation and reducing heat accumulation within the deposition. It can contribute to a maximum reduction of 81% in longitudinal distortion and 69% in transverse distortion for the wall structures produced in this study. Compared to the cooling gas flow rate, cooling time alternation is more effective in mitigating WAAM-part distortion due to more effective heat dissipation per unit time. The findings reveal that using active interpass cooling in WAAM can offer significant cost and build-time savings, as well as providing conditions for the improvement of WAAM-part quality.

Keywords

Wire arc additive manufacturing Ti6Al4V active interpass cooling distortion

Get full access to this article

View all access options for this article.

References

Williams

, Martina

, Addison

, Wire + arc additive manufacturing. Mater Sci Technol. 2016; 32:641–647. doi: 10.1179/1743284715Y.0000000073

Ding

, Pan

, Cuiuri

, Wire-feed additive manufacturing of metal components: technologies, developments and future interests. Int J Adv Manuf Technol. 2015; 81:465–481. doi: 10.1007/s00170-015-7077-3

, Pan

, Ding

, A review of the wire arc additive manufacturing of metals: properties, defects and quality improvement. J Manuf Process. 2018; 35:127–139. doi: 10.1016/j.jmapro.2018.08.001

Brandl

, Baufeld

, Leyens

, Additive manufactured Ti-6Al-4 V using welding wire: comparison of laser and arc beam deposition and evaluation with respect to aerospace material specifications. Phys Procedia. 2010; 5:595–606. doi: 10.1016/j.phpro.2010.08.087

Collins

, Brice

, Samimi

, Microstructural control of additively manufactured metallic materials. Annu Rev Mater Res. 2016; 46:63–91. doi: 10.1146/annurev-matsci-070115-031816

, Ding

, Pan

, Effects of heat accumulation on the arc characteristics and metal transfer behavior in wire arc additive manufacturing of Ti6Al4 V. J Mater Process Technol. 2017; 250:304–312. doi: 10.1016/j.jmatprotec.2017.07.037

Mukherjee

, Manvatkar

, De

, Mitigation of thermal distortion during additive manufacturing. Scripta Mater. 2017; 127:79–83. doi: 10.1016/j.scriptamat.2016.09.001

Denlinger

ER.

Chapter 11 – mitigation of distortion in large additive manufacturing parts✶, thermo-mechanical modeling of additive manufacturing. Butterworth-Heinemann; 2018. p. 183–195.

Michaleris

Minimization of welding distortion and buckling: modelling and implementation. Sawston: Elsevier; 2011; p. 274.

10.

Masubuchi

Analysis of welded structures: residual stresses, distortion, and their consequences. Elsevier. 2013; 33:372.

11.

Cao

, Gharghouri

, Nash

Finite-element analysis and experimental validation of thermal residual stress and distortion in electron beam additive manufactured Ti-6Al-4 V build plates. J Mater Process Technol. 2016; 237:409–419. doi: 10.1016/j.jmatprotec.2016.06.032

12.

Montevecchi

, Venturini

, Grossi

, Finite element mesh coarsening for effective distortion prediction in wire arc additive manufacturing. Addit Manuf. 2017; 18:145–155. doi: 10.1016/j.addma.2017.10.010

13.

Ding

, Colegrove

, Mehnen

, Thermo-mechanical analysis of wire and arc additive layer manufacturing process on large multi-layer parts. Comput Mater Sci. 2011; 50:3016–3025. doi: 10.1016/j.commatsci.2011.05.020

14.

Zhang

, Ying

, Liu

, Deformation control during the laser welding of a Ti6Al4 V thin plate using a synchronous gas cooling method. Mater Des. 2016; 90:931–941. doi: 10.1016/j.matdes.2015.11.035

15.

Colegrove

, Donoghue

, Martina

, Application of bulk deformation methods for microstructural and material property improvement and residual stress and distortion control in additively manufactured components. Scripta Mater. 2017; 135:111–118. doi: 10.1016/j.scriptamat.2016.10.031

16.

Schenk

, Richardson

, Kraska

, A study on the influence of clamping on welding distortion. Comput Mater Sci. 2009; 45:999–1005. doi: 10.1016/j.commatsci.2009.01.004

17.

Guan

, Zhang

, Guo

Dynamically controlled low stress no distortion welding method and its facility. (Chinese patent. No. 93101690.8). 1993.

18.

, Pan

, Ding

, The effects of forced interpass cooling on the material properties of wire arc additively manufactured Ti6Al4 V alloy. J Mater Process Technol. 2018; 258:97–105. doi: 10.1016/j.jmatprotec.2018.03.024

19.

Mukherjee

, Zuback

, De

, Printability of alloys for additive manufacturing. Sci Rep. 2016; 6:19717. doi: 10.1038/srep19717

20.

Elmer

, Palmer

, Babu

, In situ observations of lattice expansion and transformation rates of α and β phases in Ti–6Al–4 V. Mater Sci Eng A. 2005; 391:104–113. doi: 10.1016/j.msea.2004.08.084

21.

Denlinger

, Heigel

, Michaleris

, Effect of inter-layer dwell time on distortion and residual stress in additive manufacturing of titanium and nickel alloys. J Mater Process Technol. 2015; 215:123–131. doi: 10.1016/j.jmatprotec.2014.07.030