Slots with uneven width were cut by femtosecond laser in small plates of IN738LC superalloy to imitate service cracks. The ‘cracks’ were repaired by diffusion brazing using BNi-1a or a mixed filler alloy at 1100°C. The joint region was composed of isothermal solidification zone (ISZ), diffusion affected zone (DAZ) and precipitate zone (PZ). The compositions were different between the upper and lower ISZ due to the variation of gap width. The sample, repaired with two kinds of filler metals, had similar DAZ microstructure. PZ of mixed filler alloy bonded sample had a similar microstructure with that of BNi-1a, but less borides. The maximum gap sizes of complete isothermal solidification were almost the same for different filler alloys, followed a square root relationship with time. However, PZ of BNi-1a bonded was larger, resulting from a more base metal dissolution. The relationship between the PZ, ISZ and crack width is discussed.
MattheijJHG. Role of brazing in repair of superalloy components – advantages and limitations. Mater Sci Technol. 1985; 1(8):608–612. doi: 10.1179/mst.1985.1.8.608
2.
NagyD, HuangX. Wide gap braze repair using vertically laminated repair scheme. J Eng Gas Turbines Power. 2009; 131(1):1–7. doi: 10.1115/1.2967496
3.
VitekJM. The effect of welding conditions on stray grain formation in single crystal welds-theoretical analysis. Acta Mater. 2005; 53:53–67. doi: 10.1016/j.actamat.2004.08.039
4.
DuPontJN, MarderAR, NotisMR. Solidification of Nb-bearing superalloys: part II. Pseudoternary solidification surfaces. Metall Mater Trans A. 1998; 29:2797–2806. doi: 10.1007/s11661-998-0320-x
5.
HendersonMB, ArrellD, LarssonR. Nickel based superalloy welding practices for industrial gas turbine applications. Sci Technol Weld Join. 2004; 9:13–21. doi: 10.1179/136217104225017099
6.
MacDonaldWD, EagarTW. Transient liquid phase bonding. Ann Rev Mater Sci. 1992; 22(1):23–26. doi: 10.1146/annurev.ms.22.080192.000323
7.
IdowuOA, RichardsNL, ChaturvediMC. Effect of bonding temperature on isothermal solidification rate during transient liquid phase bonding of inconel 738LC superalloy. Mater Sci Eng A. 2005; 397:98–112. doi: 10.1016/j.msea.2005.01.055
OjoOA, RichardsNL, CharturvediMC. Effect of gap size and process parameters on diffusion brazing of inconel 738’. Sci Technol Weld Join. 2004; 9:209–220. doi: 10.1179/136217104225012175
10.
IdowuOA, OjoOA, ChaturvediMC. Microstructural study of transient liquid phase bonded cast inconel 738LC superalloy. Metall Mater Trans A. 2006; 37:2787–2796. doi: 10.1007/BF02586111
11.
WikstromNP, OjoOA, ChaturvediMC. Influence of process parameters on microstructure of transient liquid phase bonded inconel 738LC superalloy with amdry DF-3 interlayer. Mater Sci Eng A. 2006; 417:299–306. doi: 10.1016/j.msea.2005.10.056
12.
JalilvandV, OmidvarH, RahimipourMR. Investigation on microstructural properties of transient liquid phase (TLP) bonded IN-738LC superalloy with AMS 4776 filler metal. Mater Sci Technol. 2013; 29:439–445. doi: 10.1179/1743284712Y.0000000138
13.
MosallaeeM, EkramiA, OhsasaK. Microstructural evolution in the transient-liquid-phase bonding area of IN-738LC/BNi-3/IN-738LC. Met Mater Trans A. 2008; 39:2389–2402. doi: 10.1007/s11661-008-9588-0
SahaRK, KhanTI. Effect of bonding temperature on transient liquid phase bonding behavior of a Ni-based oxide dispersion-strengthened superalloy. J Mater Eng Perform. 2006; 15(6):722–728. doi: 10.1361/105994906X150786
16.
WuPH, ChengCW, ChangCP, Fabrication of large-area hydrophobic surfaces with femtosecond-laser-structured molds. J Micromech Microeng. 2011; 21(11):1–7. doi: 10.1088/0960-1317/21/11/115032
17.
WeiJ, YeY, ZouGS, Control of the kerf size and microstructure in inconel 738 superalloy by femtosecond laser beam cutting. Appl Surf Sci. 2016; 370:364–372. doi: 10.1016/j.apsusc.2016.02.162
18.
PouranvariM, EkramiA, KokabiAH. Microstructure development during transient liquid phase bonding of GTD-111 nickel-based superalloy. J Alloys Compd. 2008; 461:641–647. doi: 10.1016/j.jallcom.2007.07.108
19.
BakhtiariR, EkramiA. The effect of gap size on the microstructure and mechanical properties of the transient liquid phase bonded FSX-414 superalloy. Mater Des. 2012; 40:130–137. doi: 10.1016/j.matdes.2012.03.036
20.
JahnkeB, DemnyJ. Microstructural investigations of a nickel-based repair coating processed by liquid phase diffusion sintering. Thin Solid Films. 1983; 110:225–235. doi: 10.1016/0040-6090(83)90240-7
21.
LippoldJ, KiserSD, DuPontJN. Welding metallurgy and weldability of nickel-base alloys. New York: Wiley Publishing; 2009.
22.
ShakerinS, OmidvarH, MirsalehiSE. The effect of substrate's heat treatment on microstructural and mechanical evolution of transient liquid phase bonded IN-738 LC. Mater Des. 2016; 9:611–619. doi: 10.3390/ma9080611
23.
BakhtiariR, EkramiA, KhanTI. Microstructure-mechanical properties relation of TLP-bonded FSX-414 superalloy: effect of homogenization design. J Mater Eng Perform. 2015; 24:1687–1696. doi: 10.1007/s11665-015-1413-5
Abbasi-KhazaeiB, JahanbakhshA, BakhtiariR. TLP bonding of dissimilar FSX-414/IN-738 system with MBF-80 interlayer: the effect of homogenizing treatment on microstructure and mechanical properties. Mater Sci Eng A. 2016; 651:93–101. doi: 10.1016/j.msea.2015.10.087
26.
ZhangD, NiuW, CaoX. Effect of standard heat treatment on the microstructure and mechanical properties of selective laser melting manufactured inconel 718 superalloy. Mater Sci Eng A. 2015; 644:32–40. doi: 10.1016/j.msea.2015.06.021
27.
CaoJ, WangYF, SongXG. Effects of post-weld heat treatment on microstructure and mechanical properties of TLP bonded Inconel718 superalloy. Mater Sci Eng A. 2014; 590:1–6. doi: 10.1016/j.msea.2013.10.013
28.
PouranvariM, EkramiA, KokabiAH. Transient liquid phase bonding of wrought IN718 nickel based superalloy using standard heat treatment cycles: microstructure and mechanical properties. Mater Des. 2013; 50:694–701. doi: 10.1016/j.matdes.2013.03.030
29.
BakhtiariR, EkramiA. Transient liquid phase bonding of FSX-414 superalloy at the standard heat treatment condition. Mater Charact. 2012; 66:38–45. doi: 10.1016/j.matchar.2012.02.002
30.
TungSK, LimLC, LaiMO. Evolution of nickel borides in Ni-Si-B brazed joints of nickel during post-braze heat treatment. Mater Sci Technol. 1997; 13:1051–1056. doi: 10.1179/mst.1997.13.12.1051
31.
PouranvariM, EkramiA, KokabiAH. Solidification and solid state phenomena during TLP bonding of IN718 superalloy using Ni-Si-B ternary filler alloy. J Alloys Compd. 2013; 563:143–149. doi: 10.1016/j.jallcom.2013.02.100
32.
PouranvariM, EkramiA, KokabiAH. Phase transformations during diffusion brazing of IN718/Ni-Cr-B/IN718. Mater Sci Technol. 2013; 29:980–984. doi: 10.1179/1743284713Y.0000000238
33.
OhsasaK, NaritaT, ShinmuraT. Numerical modeling of the transient liquid phase bonding process of Ni using Ni-B-Cr ternary filler metal. J Phase Equilib. 1999; 20:199–206. doi: 10.1361/105497199770335721
34.
ZhouY, GaleWF, NorthTH. Modelling of transient liquid phase bonding. Int Mater Rev. 1995; 40:181–196. doi: 10.1179/imr.1995.40.5.181
35.
RamirezJE, LiuS. Diffusion brazing in the nickel-boron system. Weld J New York. 1992; 71:365s–376s.
36.
Tuah-PokuI, DollarM, MassalskiTB. A study of the transient liquid phase bonding process applied to a Ag/Cu/Ag sandwich joint. Metall Trans A. 1988; 19:675–686. doi: 10.1007/BF02649282
37.
KuceraJ, BuchalA, RekA. Redistribution of boron in the vicinity of Ni-B brazed joint. Kokove Materialy. 1984; 22:250–262.
38.
PouranvariM, EkramiA, KokabiAH. Diffusion brazing of cast INCONEL 718 superalloy utilising standard heat treatment cycle. Mater Sci Technol. 2014; 30:109–115. doi: 10.1179/1743284713Y.0000000320