Neutron diffraction (ND) is commonly used to investigate the stress redistribution before and after post-weld heat treatment (PWHT) in welded structures. However, there is a lack of information on the evaluations of strains during PWHT. The present work employed in situ ND to measure the relaxation of residual strains during conventional PWHT in multi-pass high-strength low-alloy steel welds. It was found that strain relaxation occurs principally during the heating stage of the heat treatment. The findings have important economic bearings and can be used to characterise comparable material combinations and optimise the PWHT process for high-strength low-alloy weld joints. This unique information also provides a valuable benchmark for the finite element modelling of this complex process.
AloraierAS, IbrahimRN, GhojelJ. Eliminating post-weld heat treatment in repair welding by temper bead technique: role bead sequence in metallurgical changes. J Mater Process Tech.2004; 153–154:392–400. doi: 10.1016/j.jmatprotec.2004.04.383
2.
EbertH, BallisW, SperkoW. Recommended practices for local heating of welds in piping and tubing. Miami: American Welding Society; 1990. 1990:260.
3.
PaddeaS, FrancisJA, ParadowskaAM, Residual stress distributions in a P91 steel-pipe girth weld before and after post weld heat treatment. Mater Sci Eng: A. 2012; 534:663–672. doi: 10.1016/j.msea.2011.12.024
4.
SmithDJ, GarwoodSJ. Influence of postweld heat treatment on the variation of residual stresses in 50 mm thick welded ferritic steel plates. Int J Press Ves Pip. 1992; 51:241–256. doi: 10.1016/0308-0161(92)90083-R
5.
ChoJR, LeeBY, MoonYH, Investigation of residual stress and post weld heat treatment of multi-pass welds by finite element method and experiments. J Mater Process Tech. 2004; 155–156:1690–1695. doi: 10.1016/j.jmatprotec.2004.04.325
6.
ASME boiler & pressure vessel code. Sec VIII Div 2 (2007 Edition)– an international code. The American society of Mechanical Engineers. New York: ASME Publication; August 2007.
7.
Standard API. 579-1/ASME FFS-1 Fitness for Service. Houston, TX: American Petroleum Institute; August 2007.
8.
ZhangJ, DongP, SongS. Stress relaxation behavior in PWHT of welded components. ASME 2011 Pressure Vessels and Piping Conference: American Society of Mechanical Engineers; 2011. p. 673–679.
9.
DongP, HongJK. Residual stress relief in post-weld heat treatment. ASME 2008 Pressure Vessels and Piping Conference: American Society of Mechanical Engineers; 2008. p. 321–329.
10.
ChenB, SkourasA, WangYQ, In situ neutron diffraction measurement of residual stress relaxation in a welded steel pipe during heat treatment. Mater Sci Eng: A. 2014; 590:374–383. doi: 10.1016/j.msea.2013.10.060
11.
DodgeM, GittosM, DongH, In-situ neutron diffraction measurement of stress redistribution in a dissimilar joint during heat treatment. Mater Sci Eng: A. 2015; 627:161–170. doi: 10.1016/j.msea.2014.12.095
12.
LombardiA, SediakoD, MachinA, Transient analysis of residual strain during heat treatment of multi-material engine blocks using in-situ neutron diffraction. Mater Lett. 2015; 157:50–52. doi: 10.1016/j.matlet.2015.05.094
13.
ParadowskaA, FinlaysonTR, PriceJWH, Investigation of reference samples for residual strain measurements in a welded specimen by neutron and synchrotron X-ray diffraction. Phys B: Cond Matt.2006; 385–386, Part 2:904–907. doi: 10.1016/j.physb.2006.05.245
14.
AlipooramirabadH, ParadowskaA, GhomashchiR, Prediction of welding stresses in WIC test and its application in pipelines. Mater Sci Tech. 2016; 32:1462–1470. doi: 10.1080/02670836.2016.1200285
15.
AlipooramirabadH, ParadowskaA, GhomashchiR, Quantification of residual stresses in multi-pass welds using neutron diffraction. J Mate Process Tech. 2015; 226:40–49. doi: 10.1016/j.jmatprotec.2015.07.002
WithersP, BhadeshiaH. Residual stress. Part 1 – measurement techniques. Mater Sci Tech. 2001; 17:355–365. doi: 10.1179/026708301101509980
18.
LavigneO, GamboaE, LuzinV, The effect of the crystallographic texture on intergranular stress corrosion crack paths. Mater Sci Eng: A. 2014; 618:305–309. doi: 10.1016/j.msea.2014.09.038
19.
AlipooramirabadH, GhomashchiR, ParadowskaA, Residual stress- microstructure-mechanical property interrelationships in multipass HSLA steel welds. J Mater Process Tech. 2016; 231:456–467. doi: 10.1016/j.jmatprotec.2016.01.020
20.
TakazawaH, YanagidaN. Effect of creep constitutive equation on simulated stress mitigation behavior of alloy steel pipe during post-weld heat treatment. Int J Press Ves Pip. 2014; 117–118:42–48. doi: 10.1016/j.ijpvp.2013.10.008
21.
DongP, SongS, ZhangJ. Analysis of residual stress relief mechanisms in post-weld heat treatment. Int J Press Ves Pip. 2014; 122:6–14. doi: 10.1016/j.ijpvp.2014.06.002