The Welding Institute of Canada (WIC) test is a simple and standardised weldability test for hydrogen assisted cold cracking that was developed in the 80s. It has been extensively utilised by the industry to qualify safe welding envelopes but the difficult access to the weldment by instrumentation hinders its use for scientific research. Moreover the lack of repeatability arising from the traditional manual deposit and the short weld length causes industrial trials to have a low success rate. The present work proposes a modified geometry, referred to as the modified WIC (MWIC) test that shows: (1) an improved success rate of weld deposition, (2) an enhancement to instrument the weldment and (3) welding conditions in better accordance with the field pipeline girth welding conditions. The design is validated under a mechanised, shielded metal arc welding process with the cellulosic electrodes used for in-field pipeline construction.
YuriokaN. Predictive methods for prevention and control of hydrogen assisted cold cracking. First international conference on ‘weld metal hydrogen cracking in pipeline grith welds’; 1999; Wollongong, Australia.
2.
YuriokaN, SuzukiH. Hydrogen assisted cracking in C-Mn and low alloy steel weldments. Int Mater Rev.1990; 35(4):217–249. doi: 10.1179/imr.1990.35.1.217
3.
KannengiesserT, BoellinghausT. Cold cracking tests – an overview of present technologies and applications. Weld World. 2013; 57(1):3–37. doi: 10.1007/s40194-012-0001-7
4.
AlamN, DunneD, BarbaroFJ. Weld metal crack testing for high strength cellulosic electrodes. First international conference on ‘weld metal hydrogen cracking in pipeline girth welds’; 1999; WTIA, Wollongong, Australia. p. 9.1–9.23.
5.
BarbaroFJ. Types of hydrogen cracking in pipeline girth welds. First international conference on ‘weld metal hydrogen cracking in pipeline girth welds’; 1999; WTIA, Wollongong, Australia. p. 11.1–11.15.
6.
CostinW, LavigneO, LintonVM, . Micromechanical examination of the relationship between weld metal microstructure and hydrogen assisted cold cracking. 6th International Pipeline Technology Conference; 2013Oct 6–9; Ostend, Belgium.
7.
CostinWL, LavigneO, KotousovA, . Investigation of hydrogen assisted cracking in acicular ferrite using site-specific micro-fracture tests. Mater Sci Eng A.2016; 651:859–868. doi: 10.1016/j.msea.2015.11.044
8.
ASNZS 2885.2-2008 Pipelines – Gas and liquid petroleum Part 2 – Welding; 2007; Australia.
9.
BS EN 1011-2:2001 Welding. Recommendations for welding of metallic materials. Arc welding of ferritic steels.
10.
EliazN, EliezerD, OlsonDL. Hydrogen-assisted processing of materials. Mater Sci Eng A. 2000; 289(1–2):41–53. doi: 10.1016/S0921-5093(00)00906-0
DavidsonJA, KonkolPJ, SovakJF. Assessing fracture toughness and cracking susceptibility of steel weldments—a review. Weld Res Coun Bull.1989; 45(345):1–43.
14.
LynchS. Hydrogen embrittlement phenomena and mechanisms. Corros Rev.2012; 30:105–123.
15.
SmialowskiM. Hydrogen in steel. Oxford: Pergamon Press Ltd; 1962.
16.
FletcherL. Field weldability of large-diameter thick-walled linepipe. Aust Weld J.1988; First Quarter(17):17–21.
17.
FletcherL, YuriokaN. A holistic model of hydrogen cracking in pipeline girth welds. First international conference on ‘weld metal hydrogen cracking in pipeline girth welds’; 1999; Wollongong, Australia.
18.
KotousovA, BorkowskiK, FletcherL, . A model of hydrogen assisted cold cracking in weld metal. 9th international pipeline conference; 2012; Calgary, Alberta, Canada, ASME.
19.
RoshanW, BumpsteadM, FletcherL, . Welding of small diameter pipelines in Australia. APIA/EPRG/PRCI 19th Joint Technical Meeting; 2013; Sydney, Australia.
20.
KumarPG, Yu-ichiK. Diffusible hydrogen in steel weldments. Trans JWRI. 2013; 42:39–62.
21.
AlipooramirabadH, GhomashchiR, ParadowskaA, . Residual stress-microstructure-mechanical property interrelationships in multipass HSLA steel welds. J Mater Process Technol.2016; 231:456–467. doi: 10.1016/j.jmatprotec.2016.01.020
22.
RadajD. Heat effects of welding: temperature field, residual stress, distortion. Berlin: Springer-Verlag; 2012.
23.
SatohK, TerasakiT, OhkumaY. Relationship between critical stress of HAZ cracking and residual diffusible hydrogen content. J Japan Weld Soc.1979; 48(4):248–252. doi: 10.2207/qjjws1943.48.248
24.
GravilleBA. A survey review of weld metal hydrogen cracking. Weld World. 1986; 24(9/10):190–198.
25.
GravilleBA. Interpretive report on weldability tests for hydrogen cracking of higher strength steels and their potential for standardization. New York: NY, Welding Research Council, New York; 1995.
26.
ConiglioN, BarbaroFJ, LintonVM, . Hydrogen assisted cold cracking susceptibility of weld metal deposited by cellulosic shielded metal arc welding consumables. International pipeline conference, IPC2010; 2010; Calgary, Canada.
27.
NorthTH, RothwellB, GloverA, . Weldability of high strength line pipe steels. Weld J.1982; 61(8):243–257.
LazorRB, GravilleB. Effect of microalloying on weld cracking in low carbon steels. Canadian Welder Fabricator. 1983; 74(21):21–23.
30.
SarrafanS, GhainiFM, RahimiE. Weld metal hydrogen cracking in transmission pipelines construction. Proceedings of the 8th international pipeline conference IPC2010; 2010; Calgary, Canada.
31.
ColaMJ. Investigation of WIC test variables. Houston, TX: Edison Welding Institute; 1991.
32.
LazorRB. Examination of pipeline welding procedural variables. Houston, TX: Pipeline Research Council International; 1984.
33.
NobleDN, PargeterRJ. Field weldability of high strength pipeline steels. Houston, TX: Edison Welding Institute; 1988.
34.
GloverA, RothwellB. Specifications and practices for hydrogen crack avoidance in pipeline girth welds. First international conference on ‘weld metal hydrogen cracking in pipeline girth welds’; 1999; WTIA: Wollongong, Australia. p. 13.1–13.18.
35.
KurjiR. Thermo mechanical factors influencing weld metal hydrogen assisted cold cracking. School of Mechanical Engineering. PhD Project, The University of Adelaide: Adelaide, Australia; 2016.
36.
DarmadiD, NorrishJ, TieuAK. Analytic and finite element solutions for temperature profiles in welding using varied heat source models. World Acad Sci Eng Technol. 2011; 81:154–162.
37.
IacobescuG. A theoretical model for welding process with Gaussian heat source – Part 1. Univ ‘Politehnica’ Bucharest Sci Bull, Series D: Mech Eng.2006; 68(4):45–50.
38.
TeixeiraPRDF, AraújoDBD, CundaLABD. Study of the Gaussian distribution heat source model applied to numerical thermal simulations of TIG welding processes; 2014.
39.
AlipooramirabadH, ParadowskaAM, GhomashchiR, . Prediction of welding stresses in WIC test and its application in pipelines. Mater Sci Technol. 2016; 32(14):1462–1470. doi: 10.1080/02670836.2016.1200285
40.
KurjiR, ConiglioN, GamboaE, GhomashchiR. Weld metal HACC susceptibility under controlled welding conditions and restraint levels. Adelaide, Australia: Energy Pipeline CRC; 2011.
41.
ChihoskiRA. The character of stress fields around a weld arc moving on aluminum sheet. Weld J.1972; 51(1):9–18.
42.
VasudevanR, StoutRD, PenseAW. Hydrogen-assisted cracking in HSLA pipeline steels. Weld Res Suppl.1981; 60(9):155–168.