Scanning laser-MAG hybrid welding with weaving laser was developed for the bead-on-plate welding of high-strength steel. Weaving laser exerted little effect on the droplet transfer behaviour during the scanning laser-MAG hybrid welding process. In order to achieve the keyhole mode of laser welding, the weaving amplitude should be no more than 2 mm. The weld penetration decreased with the increasing weaving frequency. Compared to laser-MAG hybrid weld, the ratio of arc zone width to laser zone width decreased significantly. Scanning laser-MAG hybrid welding could suppress the porosity defects of weld efficiently. The optimal weaving frequency for the porosity defects suppression was 20 Hz. However, the porosity defects increased sharply with the weaving frequency of laser over 40 Hz. The impact-absorbed energy value of specimen fabricated by scanning laser-MAG hybrid welding was about 46 J, increased by about 31.4% compared to about 35 J of laser-MAG hybrid welding.
PetringD., FuhrmannC.: ‘Recent progress and innovative solutions for laser-arc hybrid welding’, Proc. of the 1st Pacific international conference on application of lasers and optics, Melbourne, Australia, 2004, 7–10.
5.
ThomyC., SeefeldT., VollertsenF. and VietzE.: ‘Application of fiber lasers to pipeline girth welding’, Weld. J., 2006, 7, 54–58.
6.
WestinE. M., StellingK. and GumenyukA.: ‘Single-pass laser-GMA hybrid welding of 13.5 mm thick duplex stainless steel’, Weld. World, 2011, 55, 39–49. doi: 10.1007/BF03263514
7.
CaoX., WanjaraP., HuangJ., MunroC. and NoltingA.: ‘Hybrid fiber laser-arc welding of thick section high strength low alloy steel’, Mater. Des., 2011, 32, 3399–3413. doi: 10.1016/j.matdes.2011.02.002
8.
MooreP. L., HowseD. S. and WallachE. R.: ‘Microstructures and properties of laser/arc hybrid welds and autogenous laser welds in pipeline steels’, Sci. Technol. Weld. Join., 2004, 9, 314–322. doi: 10.1179/136217104225021652
KatayamaS., UchiumiS., MizutaniM., WangJ. and FujiiK.: ‘Penetration and porosity prevention mechanism in YAG laser-MIG hybrid welding’, Weld. Int., 2007, 21, 25–31. doi: 10.1533/wint.2007.3680
11.
ChenY. B., FengJ. C., LiL. Q., ChangS. and MaG. L.: ‘Microstructure and mechanical properties of a thick-section high-strength steel welded joint by novel double-sided hybrid fibre laser-arc welding’, Mater. Sci. Eng. A, 2013, 582, 284–293. doi: 10.1016/j.msea.2013.05.077
12.
MaN., LiL. Q., HuangH., ChangS. and MurakawaH.: ‘Residual stresses in laser-arc hybrid welded butt-joint with different energy ratios’, J. Mater. Process. Technol., 2015, 220, 36–45. doi: 10.1016/j.jmatprotec.2014.09.024
13.
KouK. and LeY.: ‘Grain structure and solidification cracking in oscillated arc welds of 5052 aluminum alloy’, Metall. Trans. A, 1985, 16, 1345–1352. doi: 10.1007/BF02670338
14.
BiradarN. S. and RamanR.: ‘Grain refinement in Al–Mg–Si alloy TIG welds using transverse mechanical arc oscillation’, J. Mater. Eng. Perform., 2012, 21, 2495–2502. doi: 10.1007/s11665-012-0207-2
15.
MahajanS., BiradarN. S., RamanR. and MishraS.: ‘Effect of mechanical arc oscillation on the grain structure of mild steel weld metal’, Trans. Indian Inst. Met., 2012, 65, 171–177. doi: 10.1007/s12666-012-0118-9
16.
ChoiK. D., AhnY. N. and KimC.: ‘Weld strength improvement for Al alloy by using laser weaving method’, J. Laser Appl., 2010, 22, 116–119. doi: 10.2351/1.3499456
17.
KimC., KangM. and KangN.: ‘Solidification crack and morphology for laser weave welding of Al 5J32 alloy’, Sci. Technol. Weld. Join., 2013, 18, 57–61. doi: 10.1179/1362171812Y.0000000073
18.
ZhangX. D., ChenW. Z., BaoG. and ZhaoL.: ‘Suppression of porosity in beam weaving laser welding’, Sci. Technol. Weld. Join., 2004, 9, 374–376. doi: 10.1179/136217104225021625
19.
KangN. H., KimB. H., OhW. T., KimC. H., KimJ. H. and KimY. S.: ‘Effects of weaving laser on weld microstructure and crack for Al 6k21-T4 alloy’, J. Mater. Sci. Technol., 2011, 27, 93–96. doi: 10.1016/S1005-0302(11)60031-5
20.
YamazakiY., AbeY., KitagawaA. and NakataK.: ‘Fundamental study on the laser welding phenomena with high-frequency laser beam oscillation’, Proc. of LAMP2013 – the 6th international congress on laser advanced materials processing, Niigata, Japan, 2013, 1–7.
21.
HaoK. D., LiG., GaoM. and ZengX. Y.: ‘Weld formation mechanism of fiber laser oscillating welding of austenitic stainless steel’, J. Mater. Process. Technol., 2015, 225, 77–83. doi: 10.1016/j.jmatprotec.2015.05.021
22.
VanskaM. and SalminenA.: ‘Laser welding of stainless steel self-steering tube-to-tube joints with oscillation mirror’, J. Eng. Manuf., 2012, 226, 632–640. doi: 10.1177/0954405411425114
23.
RubbenK., MohrbacherH. and LeirmanE.: ‘Advantages of using an oscillating laser beam for the production of tailed blanks’, Proc. SPIE, 1997, 3097, 228–241. doi: 10.1117/12.281143
24.
SchedewyR., DittrichD., StandfußJ. and BrennerB.: ‘LBW of high stiffness light weight structures generated by scanned fiber laser beams’, Proc. of the 27th international congress on application of lasers and electro-optics (ICALEO), Temecula, USA, 2008, 332–339.
25.
ZhangX. D., ChenW. Z., BaoG. and ZhaoL.: ‘Improvement of weld quality using a weaving beam in laser welding’, J. Mater. Sci. Technol., 2003, 20, 633–636.
26.
MatsunawaA., SetoN., KimJ. D., MizutaniM. and KatayamaS.: ‘Dynamics of keyhole and molten pool in high power CO2 laser welding’, Proc. SPIE, 2000, 3888, 34–45. doi: 10.1117/12.377006
27.
PastorM., ZhaoH., MartukanitzR. P. and DebRoyT.: ‘Porosity, underfill and magnesium loss during continuous wave Nd:YAG laser welding of thin plates of aluminum alloys 5182 and 5754’, Weld. J., 1999, 78, 207s–216s.