Dephosphorisation is of great significance for the recycling of steel slags in iron and steel industry. In this paper, the dephosphorisation of steel slags by leaching with sulphuric acid was investigated. The influential factors such as leaching time, sulphuric acid concentration, temperature, particle size and liquid/solid ratio were optimised. Over 92% of the phosphorus can be dissolved in the sulphuric acid solution while the corresponding iron loss was 34% under the condition of 60 min, sulphuric acid concentration 2.5%, 30°C, particle size <75 μm and liquid/solid ratio 100. The kinetics of the dephosphorisation process of steel slags by leaching with sulphuric acid was analysed and it was demonstrated that the unreacted shrinking core model was suited for the present study. The diffusion through solid layer around the unreacted core was the rate-limiting step of the leaching process.
BarinI.1996. Thermochemical data of pure substances. Weinheim: VCH-Verlag; p. 1–2
2.
ChenTC, SapitanJF, BallesterosFC, LuMC.2016. Using activated clay for adsorption of sulfone compounds in diesel. J Clean Prod.124:378–382. doi: 10.1016/j.jclepro.2016.03.004
3.
DiaoJ, XieB, WangYH, GuoX.2012. Recovery of phosphorus from dephosphorization slag produced by duplex high phosphorus hot metal refining. ISIJ Int. 52(6):955–959. doi: 10.2355/isijinternational.52.955
4.
DiaoJ, ZhouW, KeZ, QiaoY, ZhangT, LiuX, XieB.2016. System assessment of recycling of steel slag in converter steelmaking. J Clean Prod125:159–167. doi: 10.1016/j.jclepro.2016.03.040
5.
FixW, HeymannH, HeinkeR.1969. Subsolidus relations in the system 2CaO·SiO2-3CaO·P2O5. J Am Ceram Soc. 52(6):346–347. doi: 10.1111/j.1151-2916.1969.tb11948.x
6.
FutatsukaT, ShitogidenK, MikiT, NagasakaT, HindM.2003. Dissolution behavior of elements in steelmaking slag into artificial seawater. Tetsu-to-Hagane. 89(4):382–387. doi: 10.2355/tetsutohagane1955.89.4_382
7.
FutatsukaT, ShitogidenK, MikiT, NagasakaT, HinoM.2004. Dissolution behavior of nutrition elements from steelmaking slag into seawater. ISIJ Int. 44(4):753–761. doi: 10.2355/isijinternational.44.753
8.
GaoX, OkuboM, MaruokaN, ShibataH, ItoT, KitamuraS-Y.2015. Production and utilisation of iron and steelmaking slag in Japan and the application of steelmaking slag for the recovery of paddy fields damaged by tsunami. Min Proc Extractive Metall.124(2):116–124. doi: 10.1179/1743285514Y.0000000068
9.
ItoK, YanagisawaM, SanoN.1982. Phosphorus distribution between solid 2CaO·SiO2 and molten CaO-SiO2-FeO-Fe2O3 slags. Tetsu-to-Hagane. 68(2):342–344. doi: 10.2355/tetsutohagane1955.68.2_342
10.
KuboH, Matsubae-YokoyamaK, NagasakaT.2010. Magnetic separation of phosphorus enriched phase from multiphase dephosphorization slag. ISIJ Int. 50(1):59–64. doi: 10.2355/isijinternational.50.59
11.
MikiT, ShitogidenK, SamadaY, NagasakaT, HinoM.2003. Consideration of dissolution behavior of elements in steelmaking slag based on their stability diagram in seawater. Tetsu-to-Hagane. 89(4):388–392. doi: 10.2355/tetsutohagane1955.89.4_388
12.
MohammedAT, StephenS, SeetharamanS.2014. Phosphorus: the noose of sustainability and renewability in steelmaking. JOM. 66(9):1565–1571. doi: 10.1007/s11837-014-1093-x
13.
NumataM, MaruokaN, KimSJ, KitamuraSY.2014. Fundamental experiment to extract phosphorous selectively from steelmaking slag by leaching. ISIJ Int. 54(8):1983–1990. doi: 10.2355/isijinternational.54.1983
14.
OnoH, InagakiA, MasuiT, NaritaH, MitsuoT, NosakaS, GohdaS.1980. Removal of phosphorus from LD converter slag by floating of dicalcium silicate during solidification. Tetsu-to-Hagane. 66(9):1317–1326. doi: 10.2355/tetsutohagane1955.66.9_1317
15.
PahlevaniF, KitamuraS, ShibataH, MaruokaN.2010. Distribution of P2O5 between solid solution of 2CaO·SiO2-3CaO·P2O5 and liquid phase. ISIJ Int. 50(6):822–829. doi: 10.2355/isijinternational.50.822
16.
ProctorDM, FehlingKA, ShayEC, WittenbornJL, GreenJJ, AventC, BighamRD, ConnollyM, LeeB, ShepkerTO, ZakMA.2000. Physical and chemical characteristics of blast furnace, basic oxygen furnace, and electric arc furnace steel industry slags. Environ Sci Technol. 34(8):1576–1582. doi: 10.1021/es9906002
17.
QiaoY, DiaoJ, LiuX, ZhangT, XieB.2015. Dephosphorization of steelmaking slag by leaching with acidic aqueous solution. JOM. 68(9):2511–2519. doi: 10.1007/s11837-015-1760-6
18.
ShenH, ForssbergE.2003. An overview of recovery of metals from slags. Waste Manage. 23:933–949. doi: 10.1016/S0956-053X(02)00164-2
19.
TeratokoT, MaruokaN, ShibataH, KitamuraS.2012. Dissolution behavior of dicalcium silicate and tricalcium phosphate solid solution and other phases of steelmaking slag in an aqueous solution. High Temp Mater Proc. 31:329–338. doi: 10.1515/htmp-2012-0032